NASA NTRS1991

Low-Wear Ball-Bearing Separator

Proposed ball-bearing separator for use in cryogenic pump stronger and more resistant to wear. Consists of molded plastic-and-metal composite ring imbued with solid lubricant and containing embedded metal ring. Obtains combination of strength and lubricity. Before molding and machining, ring includes tooling portion for handling and indexing. Molded composite blend of PTFE and fluorinated ethylene/propylene (FEP) filled with brass and bronze powder and molybdenum disulfide powder.

Hawkinson, Elden L.↗
NASA NTRS2001

Cryogenic Treatment of Al-Li Alloys for Improved Weldability, Repairability, and Reduction of Residual Stresses

Service performance has shown that cryogenic treatment of some metals provides improved strength, fatigue life, and wear resistance to the processed material. Effects such as these were initially discovered by NASA engineers while evaluating spacecraft that had returned from the cold vacuum of space. Factors such as high cost, poor repairability, and poor machinability are currently prohibitive for wide range use of some aerospace aluminum alloys. Application of a cryogenic treatment process to these alloys is expected provide improvements in weldability and weld properties coupled with a reduction in repairs resulting in a significant reduction in the cost to manufacture and life cycle cost of aerospace hardware. The primary purpose of this effort was to evaluate the effects of deep cryogenic treatment of some aluminum alloy plate products, welds, and weld repairs, and optimize a process for the treatment of these materials. The optimized process is being evaluated for improvements in properties of plate and welds, improvements in weldability and repairability of treated materials, and as an alternative technique for the reduction of residual stresses in repaired welds. This paper will present the results of testing and evaluation conducted in this effort. These results will include assessments of changes in strength, toughness, stress corrosion susceptability, weldability, repairability, and reduction in residual stresses of repaired welds.

Malone, Tina W.↗
NASA NTRS1990

Diamond Coatings

Advances in materials technology have demonstrated that it is possible to get the advantages of diamond in a number of applications without the cost penalty, by coating and chemically bonding an inexpensive substrate with a thin film of diamond-like carbon (DLC). Diamond films offer tremendous technical and economic potential in such advances as chemically inert protective coatings; machine tools and parts capable of resisting wear 10 times longer; ball bearings and metal cutting tools; a broad variety of optical instruments and systems; and consumer products. Among the American companies engaged in DLC commercialization is Diamonex, Inc., a diamond coating spinoff of Air Products and Chemicals, Inc. Along with its own proprietary technology for both polycrystalline diamond and DLC coatings, Diamonex is using, under an exclusive license, NASA technology for depositing DLC on a substrate. Diamonex is developing, and offering commercially, under the trade name Diamond Aegis, a line of polycrystalline diamond-coated products that can be custom tailored for optical, electronic and engineering applications. Diamonex's initial focus is on optical products and the first commercial product is expected in late 1990. Other target applications include electronic heat sink substrates, x-ray lithography masks, metal cutting tools and bearings.

Source record↗
NASA NTRS1983

Inboard seal mounting

A regenerator assembly for a gas turbine engine has a hot side seal assembly formed in part by a cast metal engine block having a seal recess formed therein that is configured to supportingly receive ceramic support blocks including an inboard face thereon having a regenerator seal face bonded thereto. A pressurized leaf seal is interposed between the ceramic support block and the cast metal engine block to bias the seal wear face into sealing engagement with a hot side surface of a rotary regenerator matrix.

Hayes, John R.↗
DOE OSTI2022

Carbon nanotube (CNT) reinforced 316L stainless steel composites made by laser powder bed fusion: Microstructure and wear response

Carbon nanotube (CNT) reinforced 316L stainless steel (SS) composites were fabricated by laser powder bed fusion (LPBF) additive manufacturing (AM). This study focuses on microstructure evolution, hardness, and wear behavior. The wear behavior for AM 316L SS and 1 wt% CNT/316L SS was studied by a dry sliding test under normal loads of 10, 15, and 25 N. The addition of CNT to 316L SS led to the change of solidification mode from cellular/columnar to dendritic growth, producing grain refinement. Nanoscale dendrites were observed. Although TEM characterization confirmed the existence of CNT in cell interior, most CNT were damaged, resulting in carbon material segregation along cellular/dendritic boundaries. The wear rate was found dramatically decreased due to the improved hardness. Compared to the adhesive and abrasive wear in AM 316L SS, the wear mechanism of CNT/316L composite was adhesion and oxidative wear. Furthermore, enhanced cellular/dendritic boundary strengthening by carbon segregation was the main strengthening mechanism of CNT/316L composite.

36 MATERIALS SCIENCE↗
NASA NTRS1980

Effect of Substrate Surface Finish on the Lubrication and Failure Mechanisms of Molybdenum Disulfide Films

An optical microscope was used to study the lubrication and failure mechanisms of rubbed (burnished) MoS2 films applied to three substrate surface finishes - polished, sanded, and sandblasted - as a function of sliding distance. The lubrication mechanism was the plastic flow of thin films of MoS2 between flat plateaus on the rider and on the metallic substrate. If the substrates were rough, flat plateaus were created during 'run in' and the MoS2 flowed across them. Wear life was extended by increasing surface roughness since valleys in the roughened substrate served as reservoirs for MoS2 and a deposit site for wear debris. In moist air, the failure mechanism was the transformation of metallic colored MoS2 films to a black, powdery material that was found by X ray diffraction to consist primarily of alpha iron and MoO3 powders. In dry argon, the failure mechanism was the gradual depletion of the MoS2 film from the contact region by transverse flow. Analysis of the wear debris on the wear track at failure showed it consisted mainly of alpha iron and some residual MoS2. No molybdenum oxides were found.

Fusaro, R. L.↗
NASA NTRS1978

Lubrication and failure mechanisms of molybdenum disulfide films. 2: Effect of substrate roughness

An optical microscope was used to study the lubrication and failure mechanisms of rubbed MoS2 films applied to three substrate surface finishes; polished, sanded, and sandblasted as a function of sliding distance. The lubrication mechanism was the plastic flow of thin films of MoS2 between flat plateaus on the rider and on the metallic substrate. If the substrate was rough, flat plateaus were created during run-in and the MoS2 flowed across them. Wear life was extended by increasing surface roughness since valleys in the roughened substrate served as reservoirs for MoS2 and as deposit sites for wear debris. In moist air the failure mechanism was the transformation of metallic colored MoS2 films to a black, powdery material that was found by X-ray diffraction to be alpha iron, MoO3, and possibly FeMoO3. In dry argon the failure mechanism was the gradual depletion of MoS2 from the contact region by transverse flow, and the wear debris on the track at failure was alpha iron, residual MoS2, and possibly FeS.

Fusaro, R. L.↗
NASA NTRS1989

Reaction of perfluoroalkylpolyethers (PFPE) with 440C steel in vacuum under sliding conditions at room temperature

Reactions of perfluoroalkylpolyethers (PFPE: Fomblin, Demnum and Krytox) were studied during the sliding contact of stainless steel specimens under ultrahigh vacuum conditions. All three fluids reacted with the steel specimens during sliding. Fomblin, which has acetal linkages, decomposed under the sliding conditions generating gaseous products, (COF2 and fluorinated carbons) which were detected by a quadrupole mass spectrometer. Gaseous products were not detected for the Demnum and Krytox fluids. The amount of gaseous products from Fomblin increased with increasing sliding speed. At the end of the sliding experiments, the wear scar and deposits on the specimens were examined by small spot size XPS. The oxide layer on the specimen surface was removed during sliding, and metal fluorides were formed on the worn surface. The surface of the wear scar and deposits were covered with adsorbed PFPE. Based on these results, it was concluded that the decomposition reaction on Fomblin was initiated by contacting the fluid with a fresh metal surface which was formed during sliding.

Mori, Shigeyuki↗
NASA NTRS1990

Decomposition of perfluoroalkylpolyethers (PFPE) in ultra-high vacuum under sliding conditions

Reactions of perfluoroalkylpolyethers (PFPE: Fomblin, Demnum and Krytox) were studied during the sliding contact of stainless steel specimens under ultrahigh vacuum conditions. All three fluids reacted with the steel specimens during sliding. Fomblin, which has acetal linkages, decomposed under the sliding conditions generating gaseous products, (COF2 and fluorinated carbons) which were detected by a quadrupole mass spectrometer. Gaseous products were not detected for the Demnum and Krytox fluids. The amount of gaseous products from Fomblin increased with increasing sliding speed. At the end of the sliding experiments, the wear scar and deposits on the specimens were examined by small spot size XPS. The oxide layer on the specimen surface was removed during sliding, and metal fluorides were formed on the worn surface. The surface of the wear scar and deposits were covered with adsorbed PFPE. Based on these results, it was concluded that the decomposition reaction on Fomblin was initiated by contacting the fluid with a fresh metal surface which was formed during sliding.

Mori, Shigeyuki↗
NASA NTRS1981

Effect of substrate surface finish on the lubrication and failure mechanisms of molybdenum disulfide films

An optical microscope was used to study the lubrication and failure mechanisms of rubbed (burnished) MoS2 films applied to three substrate surface finishes - polished, sanded, and sandblasted - as a function of sliding distance. The lubrication mechanism was the plastic flow of thin films of MoS2 between flat plateaus on the rider and on the metallic substrate. If the substrate was rough, flat plateaus were created during 'run-in' and the MoS2 flowed across them. Wear life was extended by increasing surface roughness since valleys in the roughened substrate served as reservoirs for MoS2 and a deposit site for wear debris. In moist air, the failure mechanism was the transformation of metallic-colored MoS2 films to a black, powdery material that was found by X-ray diffraction to consist primarily of alpha-iron and MoO3 powders. In dry argon, the failure mechanism was the gradual depletion of the MoS2 film from the contact region by transverse flow. Analysis of the wear debris on the wear track at failure showed it consisted mainly of alpha-iron and some residual MoS2. No molybdenum oxides were found.

Fusaro, R. L.↗
NASA NTRS1962

LUBRICATING PROPERTIES OF CERAMIC-BONDED CALCIUM FLUORIDE COATINGS ON NICKEL-BASE ALLOYS FROM 75 DEG TO 1900 DEG F

The endurance life and the friction coefficient of ceramic-bonded calcium fluoride (CaF2) coatings on nickel-base alloys were determined at temperatures from 75° to 1900° F. The specimen configuration consisted of a hemispherical rider (3/16-in. rad.) sliding against the flat surface of a rotating disk. Increasing the ambient temperature (up to 1500° F) or the sliding velocity generally reduced the friction coefficient and improved coating life. Base-metal selection was critical above 1500° F. For instance, cast Inconel sliding against coated Inconel X was lubricated effectively to 1500° F, but at 1600° F severe blistering of the coatings occurred. However, good lubrication and adherence were obtained for René 41 sliding against coated René 41 at temperatures up to 1900° F; no blisters developed, coating wear life was fairly good, and the rider wear rate was significantly lower than for the unlubricated metals . Friction coefficients were 0.12 at 1500° F, 0.15 at 1700° F, and 0.17 at 1800° and 1900° F. Because of its ready availability, Inconel X appears to be the preferred substrate alloy for applications in which the temperature does not exceed 1500° F. René 41 would have to be used in applications involving higher temperatures. Improved coating life was derived by either preoxidizing the substrate metals prior to the coating application or by applying a very thin (<0.0002 in.) burnished and sintered overlay to the surface of the coating. Preoxidation did not affect the friction coefficient. The overlay generally resulted i n a higher friction coefficient than that obtained without the overlay. The combination of both modifications resulted in longer coating life and in friction coefficients intermediate between those obtained with either modification alone.

Nickel alloy↗
NASA NTRS1962

Lubricating Properties of Ceramic-Bonded Calcium Fluoride Coatings on Nickel-Base Alloys from 75 to 1900 deg F

The endurance life and the friction coefficient of ceramic-bonded calcium fluoride (CaF2) coatings on nickel-base alloys were determined at temperatures from 75 F to 1900 F. The specimen configuration consisted of a hemispherical rider (3/16-in. rad.) sliding against the flat surface of a rotating disk. Increasing the ambient temperature (up to 1500 F) or the sliding velocity generally reduced the friction coefficient and improved coating life. Base-metal selection was critical above 1500 F. For instance, cast Inconel sliding against coated Inconel X was lubricated effectively to 1500 F, but at 1600 F severe blistering of the coatings occurred. However, good lubrication and adherence were obtained for Rene 41 sliding against coated Rene 41 at temperatures up to 1900 F; no blisters developed, coating wear life was fairly good, and the rider wear rate was significantly lower than for the unlubricated metals. Friction coefficients were 0.12 at 1500 F, 0.15 at 1700 F, and 0.17 at 1800 F and 1900 F. Because of its ready availability, Inconel X appears to be the preferred substrate alloy for applications in which the temperature does not exceed 1500 F. Rene 41 would have to be used in applications involving higher temperatures. Improved coating life was derived by either preoxidizing the substrate metals prior to the coating application or by applying a very thin (less than 0.0002 in.) burnished and sintered overlay to the surface of the coating. Preoxidation did not affect the friction coefficient. The overlay generally resulted in a higher friction coefficient than that obtained without the overlay. The combination of both modifications resulted in longer coating life and in friction coefficients intermediate between those obtained with either modification alone.

Sliney, Harold E.↗
NASA NTRS1986

A new chromium carbide-based tribological coating for use to 900 deg C with particular reference to the Stirling engine

A new chromium carbide-based coating (PS 200) is described. This coating is shown to have good friction and wear properties over a wide temperature range. A nickel alloy-bonded chromium carbide coating was used as a baseline material for comparison with experimental formulated coatings. Coatings were plasma sprayed onto metal disks, then diamond ground to a thickness of 0.025 cm. Friction and wear were determined using a pin on disk tribometer at temperatures from 25 to 900 C in hydrogen, helium, and air. Pin materials included several metallic alloys and silicon carbide. It was found that appropriate additions of metallic silver and of barium fluoride/calcium fluoride eutectic to the baseline carbide composition significantly reduced friction coefficients while preserving, and in some cases, even enhancing wear resistance. The results of this study demonstrate that PS 200 is a promising coating composition to consider for high temperature aerospace and advanced heat engine applications. The excellent results in hydrogen make this coating of particular interest for use in the Stirling engine.

Sliney, H. E.↗
NASA NTRS1986

A new chromium carbide-based tribological coating for use to 900 C with particular reference to the Stirling engine

A new chromium carbide-based coating (PS 200) is described. This coating is shown to have good friction and wear properties over a wide temperature range. A nickel alloy-bonded chromium carbide coating was used as a baseline material for comparison with experimentally formulated coatings. Coatings were plasma sprayed onto metal disks, then diamond ground to a thickness of 0.025 cm. Friction and wear were determined using a pin on disk tribometer at temperatures from 25 to 900 C in hydrogen, helium, and air. Pin materials included several metallic alloys and silicon carbide. It was found that appropriate additions of metallic silver and of barium fluoride/calcium fluoride eutectic to the baseline carbide composition significantly reduced friction coefficients while preserving, and in some cases, even enhancing wear resistance. The results of this study demonstrate that PS 200 is a promising coating composition to consider for high temperature aerospace and advanced heat engine applications. The excellent results in hydrogen make this coating of particular interest for use in the Stirling engine.

Sliney, Harold E.↗
NASA NTRS1980

Long-wearing TFE/metal bearings

Method for making metal/polytetrafluoroethylene (TFE) bearing surfaces embeds long-wearing layer of TFE in microscopic pits in metal. Technique has potential applications in automotive gears, ball joints, and roller chain components. Other applications are in use of unlubricated bearings in chemical, pharmaceutical, and food-processing equipment.

Brass, R. A.↗