Results for “metal casting”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

194 records · Page 11

XRD and SEM/EDS characterization of two quaternary fuel alloys (U-2.5Mo-2.5Ti-5.0Zr and U-1.5Mo-1.5Ti-7.0Zr in wt. %) for fast reactors

The current study focuses on characterization of two potential fuel alloys for sodium-cooled fast reactors: U-2.5Mo-2.5Ti-5.0Zr (U-MT5Z) and U-1.5Mo-1.5Ti-7.0Zr (U-MT7Z) in wt. %. As-cast alloys and annealed (600°C, 500h) alloys are studied by X-ray powder diffraction (XRD) for their bulk structures, and scanning electron microscopy / energy dispersive X-Ray spectroscopy (SEM/EDS) for their microstructures and phase constituents. For as-cast alloys, the XRD results show that U-MT5Z mainly contains γ, while U-MT7Z alloy contains a. In both alloys, there are three phases indicated by EDS, a U-rich phase, secondary phase, and Zr-rich phase. Further, the elemental compositions varied in different phases and in different alloys. After annealing, both alloys exhibit the structures of α-U and U 2 Ti according to XRD. The EDS results suggest there are five phases found in both alloys.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

High entropy alloys with hexagonal close-packed structure derived from thin film combinatorial approach

A thin film combinatorial synthesis approach was utilized to develop a compositional and structural library for the OsRuWCo alloy system. The survey of this alloy space produced 24 unique compositions and their corresponding crystal structures, which represent a phase map where amorphous and single-phase hexagonal close-packed alloys were identified. Based on the identification of a promising candidate film region, a new high entropy alloy based on OsRuWCo, but with non-equiatomic composition, was synthesized in bulk form. The alloy exhibited a single-phase hexagonal close-packed structure in the as-cast state. Three derivatives from this system were also developed by considering the heat of mixing, atomic size, and binary solubility. These new alloys are based on OsRuWCoIr and OsRuWCoFe, both of which exhibit single-phase hexagonal close-packed as-cast structures, as determined by X-ray diffraction and electron microscopy. Additionally, this large compositional space was utilized to evaluate conventional parameters that describe high entropy alloys (ΔS mix , ΔH mix , Ω, δ, and VEC), and these were found to elucidate the criteria for solid solution formation in this system. Additionally, trends illustrating the evolution from amorphous to crystalline phases are demonstrated and discussed. It is concluded that in this particular case, the dominant factors promoting crystallinity are thermodynamic or electronic, rather than geometric.

36 MATERIALS SCIENCE↗

Preparation of Macroscopic Low-Density Gold Foams with Good Machinability

Uniform, macroscopic monoliths (ranging from a few millimeters to a centimeter) of low-density gold foams with ~95% porosity and ~10-μm-diameter pores were prepared by the casting of gold-coated polystyrene core-shell particles followed by the thermal removal of the polymer core. The Au foams were composed of unique hollow gold spheres and showed superior mechanical integrity and resilience compared to the foams we previously reported. Highly efficient seeding and electroless gold-plating methods in this study caused a significant morphological transition in the gold coatings from coarse particles to fine particles, and finally, to a continuous layer. A modified, scalable casting approach to form large uniform monoliths (up to ~1-cm diameter) and a gentle baking condition to minimize undesirable densification of the final foams enabled us to develop a simple, efficient synthetic route to nanostructured macroscopic low-density gold foams. To demonstrate the improved mechanical stability and machinability, a representative monolithic Au foam (~0.9 g/cm 3 ) was carefully cut into the hollow cylinder of gold foams by a series of machining and processing steps. Finally, we tried to understand the unique mechanical behaviors and properties of this gold foam by nanoindentation measurement.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗

New directions and principles for solvent extraction for recovery of lithium from aqueous brines and mineral leachates: A brief review

Increasing demand for lithium for manufacturing of batteries is fueling the unprecedented search for improved recovery and alternative sources. Wider source distribution, lower energy consumption, and greater sustainability make extraction of lithium from brines, both natural and process-derived, an attractive alternative to mineral ores. Solvent extraction, used industrially for production of metals, salts, and pharmaceuticals, has been investigated as a methodology for lithium recovery for several decades. However, industrial application of solvent extraction for lithium recovery has so far been limited. In contrast, direct lithium extraction using adsorbents based on inorganic minerals has rapidly advanced from research to commercialization. A comparison of solvent extraction processes to adsorption highlights these issues and explains the preference for adsorbents. Although the application of solvent extraction has been criticized for use of large amounts of acid, alkali, and organic solvents, steady progress has been made to improve its potential for industrial lithium production, spurred on generally by the advantages of solvent extraction in selectivity and throughput. Previously developed beta-diketone, organophosphate, and crown ether ligands are being adapted and improved. Their novel use with ionic liquids, deep eutectic solvents, and membrane technologies promises to expand capabilities for extraction of lithium from dilute aqueous sources while improving sustainability. Possibilities for further discovery and innovation abound. In this review, we provide a unique perspective from the field of solvent extraction starting with fundamentals such as ion-transfer theory and apply them to understanding lithium selectivity and extraction behavior. In conclusion, the results are cast in the light of the practical realities of developing economical solvent extraction processes.

Brine↗

Co-introduction of precipitate hardening and TRIP in a TWIP high-entropy alloy using friction stir alloying

Tuning deformation mechanisms is imperative to overcome the well-known strength-ductility paradigm. Twinning-induced plasticity (TWIP), transformation-induced plasticity (TRIP) and precipitate hardening have been investigated separately and have been altered to achieve exceptional strength or ductility in several alloy systems. In this study, we use a novel solid-state alloying method—friction stir alloying (FSA)—to tune the microstructure, and a composition of a TWIP high-entropy alloy by adding Ti, and thus activating site-specific deformation mechanisms that occur concomitantly in a single alloy. During the FSA process, grains of the as-cast face-centered cubic matrix were refined by high-temperature severe plastic deformation and, subsequently, a new alloy composition was obtained by dissolving Ti into the matrix. After annealing the FSA specimen at 900 °C, hard Ni–Ti rich precipitates formed to strengthen the alloy. An additional result was a Ni-depleted region in the vicinity of newly-formed precipitates. The reduction in Ni locally reduced the stacking fault energy, thus inducing TRIP-based deformation while the remaining matrix still deformed as a result of TWIP. Our current approach presents a novel microstructural architecture to design alloys, an approach that combines and optimizes local compositions such that multiple deformation mechanisms can be activated to enhance engineering properties.

36 MATERIALS SCIENCE↗

Fabrication of ceramic to metal graded structure for high temperature CSP receiver application using solid state additive manufacturing

The overarching goal of this project is to come up with an innovative joining solution for integration of SiC ceramic to structural materials such as stainless steels (SS)/Ni-base alloys, where intimate metallurgical bonding between SiC ceramic and the structural metallic alloy is demonstrated at the interface. Implementation of a simple, yet robust joining method would help in increasing the application space of SiC in a high-temperature CSP (concentrated solar power) plant, especially in the receiver section. This research goal has been achieved by creating a functionally graded material (FGM) interface between SiC and the selected structural material with the help of powder metallurgy (PM) approach and demonstrate intimate metallurgical bonding between monolithic RB-SiC and 316L stainless steel alloy blanks.

36 MATERIALS SCIENCE↗

Controlling the Morphology of PEDOT:PSS Blend Films with Pre-Deposition Solution Composition and Deposition Technique

Understanding the relationships between morphology, fabrication processes, and thermoelectric performance in conducting polymers is essential to the development of high- efficiency organic thermoelectrics as an alternative to commonly used rare metals. Altering the film fabrication process of poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) with the addition of high boiling solvents to the precast solution improves the electrical conductivity and significantly increases its Seebeck value. Neutron scattering monitors the changes in the atomic, nanoscale, and mesoscale morphologies of PEDOT:PSS thin films with the addition of dimethyl sulfoxide (DMSO) to the aqueous solution prior to film formation and with varying fabrication procedures. The neutron scattering results show a decrease in the deuterated PSS domain size along with systematic variations in PEDOT fibril assemblies in the final blend film with the addition of DMSO to the pre-deposition solution. These structural modifications indicate that the increase in conductivity of PEDOT:PSS blends with addition of DMSO reported in the literature can be ascribed to the disruption of solvated PEDOT assemblies by the DMSO, forming smaller PSS domains in the pre-deposition solution and allowing smoother film formation. These improvements are observed significantly with the addition of just 1% DMSO but continue to modestly improve with the addition of up to 5% DMSO to the PEDOT:PSS blend pre-deposition solution. The fact that the variations in the measured morphology are independent of whether the films were deposited by spin or ultrasonic spray casting methods emphasizes the crucial importance of the structure of the blend in the pre-deposition solution in determining the final thin film blend morphology.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Microstructural evolution and intermetallic formation in Zn-3Mg (wt%) powder mixture processed by high-pressure torsion

Severe plastic deformation (SPD) techniques have been used extensively over the past 40 years for producing strong metals and alloys. High-pressure torsion (HPT) is one of the most promising SPD techniques for achieving high strength through nanoscale grain refinement and phase transformation. In this research, a mixture of pure zinc (Zn) and magnesium (Mg) powders, Zn-3Mg (wt%), was HPT-processed under a pressure of 6 GPa for 1, 5, 10, 20, and 30 turns at room temperature to achieve a high strength biodegradable material. In order to understand the effects of pre-consolidation on the resulting microstructure and hardness, HPT processing was performed on loose powders placed in the die and also on a pre-compacted powder mixture and the resulting HPT disks were characterized by X-ray diffraction, scanning electron microscopy, atom probe tomography, and Vickers microhardness. In both cases, the HPT disk microstructures contained nanoscale grains, and stable and metastable strain-induced intermetallics, but an unusual softening appeared at large shear strains. Grain size, grain morphology, and the formation of different intermetallics were analyzed to explain the unusual hardness distribution, and it was found that an inverse Hall-Petch relationship between hardness and grain size exists. It is suggested that thermally-activated phenomena such as grain boundary sliding contributed to the strain-induced softening of this nano-structured biomaterial due to its low melting point. Finally, the current results are compared with those for HPT-processed cast alloys and hybrids of the same composition.

36 MATERIALS SCIENCE↗

Polycarbonate‐Based Solid‐Polymer Electrolytes for Solid‐State Sodium Batteries

Solid-polymer electrolytes comprised of polypropylene carbonate (PPC) and varied sodium bis(fluorosulfonyl)imide (NaFSI) salt concentrations are investigated for implementation as a conductive solid polymer electrolyte into solid-state cathode composites utilizing a sodium-layered oxide active material. The ionic conductivity generally increases with NaFSI salt content, reaching ≈1 mS cm −1 at 80 °C at the highest salt concentration (PPC:NaFSI = 0.5:1). Through an all-in-one slurry casting method, Na 2/3 Ni 1/3 Mn 2/3 O 2 cathode composites are fabricated in which the dispersed PPC electrolyte acts as the primary binder. Enabled by a bilayer polymer electrolyte system, cycling performance with the PPC cathode electrolyte is optimized with respect to salt concentration and anode material. The best cyclability is achieved with a moderate salt concentration electrolyte (PPC:NaFSI = 5:1), showcasing an initial capacity of 83 mA h g −1 with a remarkable 80% capacity retention after 150 cycles at C/5 rate and 60 °C. The superior performance of the lower salt concentration electrolyte is attributed to better electrochemical stability, as confirmed by linear sweep voltammetry and online electrochemical mass spectrometry measurements. In conclusion, these results underscore the potential of carbonate-based polymer electrolytes and the importance of balancing electrolyte conductivity and stability in cell design.

25 ENERGY STORAGE↗

Trace Chemical Detection Using Intercalated MXenes as a Signal Enhancing Substrate in Optical Probes

MXenes are 2D materials composed of layered transition metal nitrides or carbides. These materials are synthesized by HF exfoliation from MAX phases (Ti{sub 3}AlC{sub 2}). The 2D nanomaterial was synthesized by the removal of the 'A' element, resulting in a Mxene product (Ti{sub 3}C{sub 2}). MXenes have the general formula M{sub n+1}X{sub n}T{sub x}, where M is an early transition metal, X is Carbon and/or Nitrogen, and T accounts for surface terminated functional groups such as Fluoride, hydroxyl, and oxygen. These materials have very unique properties, similar to graphene, that allows them to be applied in a variety of trace detection techniques including surface-enhanced Raman spectroscopy (SERS). MXenes have also been demonstrated to selectively uptake uranyl ion, UO{sub 2}{sup 2+}. If this property can be combined with SERS or fluorescence detection, it may be possible to use MXenes as the basis for an alternative method to kinetic phosphorescence analysis (KPA) for trace uranyl measurements. Objectives: To confirm that MXene Nano materials are suitable substrates for SERS and sensor development by enhancing Raman signaling. To determine if certain MXene preparation methods yield materials that are more suitable for trace sensing methods. To determine uranyl uptake properties of these MXene materials and test them for analytical signals. Sample Preparation: Preparation of Ti{sub 3}C{sub 2}MXene (at FSU). MXenes were prepared by etching Al from Ti{sub 3}AlC{sub 2} (MAX phase)material. Two etching techniques yield different MXene products: LiF/HCl: Milder reaction, larger MXene flakes. HF: Harsher reaction, smaller flakes, larger layer separation. Products washed to remove etchant, vacuum filtered, and dried. Dried MXene flakes are air-stable. Film preparation for sensor testing (at SRNL): Suspend powder in diH{sub 2}O, purge with Ar, sonicate for 30 min. Centrifuge and collect supernate with suspended particles. Observed LiF-etched Mxene yielded a higher density of particles and darker collected solution. Drop-cast (4 ml) supernate onto slides and dried with Ar. For Rhodamine B (RhB) testing, drop-cast 4 ml drops onto Mxene spots and dried with Ar. Scanning Electron Microscopy conditions: 10 kV Beam energy, high vacuum; Working distance of 8 mm; beam penetration depth appx. 4 microns, beam spot size appx. 2 nanometers. Results: Detection of aluminum correlates with bright spots on image. Presence of aluminum shows that LiF/HCl etching was less thorough than HF etching. Trace Cl detection in LiF images suggests incomplete rinsing. HF has smaller feature size, more layer structure, and increased homogeneity, consistent with expectations. Macroscopic Raman spectroscopy measurements: 532 nm excitation, ∼50 mW with a ∼100 micron spot size (InPhotonics RPB probe). Kaiser Optical Holospec f/1.8 spectrometer with cooled (-60 deg.C) Andor iDus OE420 CCD. LiF 1x supernate showed good signal for trace measurements of Rhodamine B. HF and 1/4x LiF supernates showed little Mxene or Rhodamine B signal. Low deposition densities led to excess background signal from glass slides. For LiF film, response is linear with Rhodamine B concentration over range tested. Will retest with Raman microscope (∼1 micron spot size) to characterize SERS of more dilute LiF and HF etched Mxenes. Conclusions: The LiF etched material was more suitable for macroscopic SERS measurements because it was more concentrated, resulting in a thicker film than the HF etched Mxene and diluted LiF sample. However, the other materials may give greater SERS enhancements, which we hope to determine from measurements with the Raman microscope. From characterization with SEM we concluded that the HF etched Mxene is more uniform/homogenous and has smaller particle size than the LiF etched Mxene. There is still aluminum present in both samples indicating that etching wasn't complete, but the removal of the aluminum was more efficient in the HF method. Path Forward: Observe SERS with Raman microscopy, to obtain better signals for the more diluted samples and be able to compare enhancement effects for the different MXenes. Characterize uranyl sorption into MXene films and test Raman and fluorescence signals. Revisit the etching conditions to improve removal of aluminum. FSU and SRNL will continue to collaborate to create and characterize different Mxene materials and test their usefulness for sensor applications.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Accelerated fission rate irradiation design, pre-irradiation characterization, and adaptation of conventional PIE methods for U-10Mo and U-17Mo

Metallic U alloys have high U density and thermal conductivity and thus have been explored since the beginning of nuclear power research. Alloys of U with modest amounts of Mo, such as U-10 wt % Mo (U-10Mo), are of particular interest because the γ-U crystal structure in this alloying addition shows prolonged stability in reactor service. Historically, radiation data on U-10Mo fuels were collected in Na fast reactors or lower temperature research reactor conditions, but little is known about irradiation behavior, particularly swelling and creep, at irradiation temperatures between 250 and 500°C. This work discusses the methodology and pre-irradiation characterization results from a U-Mo irradiation campaign performed in the High Flux Isotope Reactor at Oak Ridge National Laboratory. U-10Mo and U-17Mo samples irradiations are being completed at temperatures ranging from 250 to 500°C to three targeted fission densities between 2 × 10 20 and 1.5 × 10 21 fissions per cubic centimeter. Swelling measurement of the specimen sizes studied here required development and assessment of new methods for volume determination before and after irradiation. Laser profilometry and X-ray computation tomography (XCT) were used to provide preirradiation characterization of samples to determine the error and applicability of each to determine swelling following irradiation. These outcomes are contextualized through use of BISON simulations performed to assess the predicted expansion of U-Mo fuels subjected to the irradiation conditions of this work. Use of existing BISON fuel performance models predicted a maximum of 7% swelling under the irradiation conditions of this study. Pre-irradiation characterization revealed the as-cast U-Mo fuel samples were uniformly large-grained fully cubic U crystals with small U-C/N bearing precipitates and pores distributed throughout. Samples were found to contain a bulk porosity between .4 and 3% because of the casting process. Local porosity in areas far from large, interconnected pores was found by Slice-and-View to be under .2%. Nanometer-sized precipitates rich in C and N were identified in all samples, likely because of impurities during the fabrication process. Dendritic bands were also observed throughout the samples. These bands were characterized by variable Mo content that deviated from the overall Mo content by 2–3 wt %. No other microstructural features were correlated to these bands. Mechanical properties were found to be slightly strengthened compared to literature reports of bulk U-Mo fuels due to the nano-scale precipitates throughout the sample.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Development of High Bs Fe-Ni Based Metal Amorphous Nanocomposite by Optimization of Glass Forming Ability

A growing interest in electric vehicles challenges soft magnetic materials to improve efficiency and power density. Metal amorphous nanocomposites (MANCs) have lower coercivities and eddy current losses, allowing for greater efficiency and higher switching frequency. The later allows for high motor speeds and improved power density. However, commercially available and laboratory demonstrated MANCs have shortcomings. Fe-based MANCs, such as FINEMET have excellent magnetic properties, but mechanical properties limit their application in high speed electric motors (HSMs). Fe-Co based MANCs, such as HITPERM, have high saturation inductions and good mechanical properties, but elevated magnetostrictive losses. Co-based MANCs and more recent Fe-Ni based MANCs have low losses and good mechanical properties, but lower saturation inductions (1-1.2 T), that limit power density in HSMs. Recently, much work has explored improving saturation induction in MANCs by increasing the content of magnetic elements, which comes at the cost of glass-forming ability (GFA). These efforts where generally limited to trial and error testing. Additionally, all work to date has focused on Fe-based alloys. In this work, a method of using Thermocalc simulation to locate near-eutectic compositions has been applied to Fe-Ni based alloys. Minima in liquidus temperature and solidification range were found for a ternary composition range and used to identify compositions that retain good GFA as the percentage of magnetic elements is increased. The (Fe 70 Ni 30 ) x (B-Si-Nb) 100-x alloy system for x=82% and x=85% was explored by Thermocalc simulations. This is an increase in magnetic element content compared to previously developed x=80% alloys. 3 compositions in the x=82% system, and 1 alloy in the x=85% system where identified and successfully cast as amorphous ribbon. The amorphous nature of the ribbon was confirmed by a bend test and XRD. Magnetic testing was performed by PPMS to measure saturation induction and Curie temperature of the amorphous material. The Curie temperatures increased to 407-438 °C for the x=82% alloys, and 462 °C for the x=85% alloy. Saturation induction increased to 1.28-1.36 T for the x=82% alloy and 1.48 T for the x=85% alloy, which is a significant improvement over the ~370 °C Curie temperature and 1.2 T saturation of previous Fe-Ni alloy. Crystallization behavior was studied by XRD for the x=85% alloy, showing that crystallization process follows a 2-step process of Amorphous → BCC+FCC+Amorphous → BCC+FCC+Fe 3 B+Fe 23 B 6 . Post annealing magnetic properties were studied by strip testing, and saturation induction as high as 1.48 T was seen after optimal annealing. TEM was used to study structure of as cast and annealed material. 2 alloys with x=82% compositions were identified with an optimal crystalline size of 10-20 nm, while the x=85% alloy had this structure in the as cast state. This opens the possibility of using the alloy in the as cast state, without requiring annealing. In conclusion, alloys with good GFA and improved magnetic properties were identified by Thermocalc simulation.

Krimer, Yuval↗

Operando neutron diffraction reveals mechanisms for controlled strain evolution in 3D printing

Abstract Residual stresses affect the performance and reliability of most manufactured goods and are prevalent in casting, welding, and additive manufacturing (AM, 3D printing). Residual stresses are associated with plastic strain gradients accrued due to transient thermal stress. Complex thermal conditions in AM produce similarly complex residual stress patterns. However, measuring real-time effects of processing on stress evolution is not possible with conventional techniques. Here we use operando neutron diffraction to characterize transient phase transformations and lattice strain evolution during AM of a low-temperature transformation steel. Combining diffraction, infrared and simulation data reveals that elastic and plastic strain distributions are controlled by motion of the face-centered cubic and body-centered cubic phase boundary. Our results provide a new pathway to design residual stress states and property distributions within additively manufactured components. These findings will enable control of residual stress distributions for advantages such as improved fatigue life or resistance to stress-corrosion cracking.

36 MATERIALS SCIENCE↗

Microstructure and mechanical properties of ultrasonic spot welding of AA7075-T6 and A380 casting aluminum alloy

Ultrasonic spot welding (USW) was employed to join AA7075-T6 and casting Al alloy A380. Under a constant welding power, the influence of the welding time duration (from 1 s to 3 s) on peak temperature, microstructure, hardness, and mechanical strength of the joints were studied. It was found that the peak temperature increased with welding time. A sound solid-state metallurgical bonding was obtained at the joint interface. The cracks occurred at the edge of the joints were eventually eliminated as the welding time increased. A layer of refined grains formed in A380 adjacent to the bonding line. Further, hardness reduction occurred in AA7075 at the joint interface and the degree of hardness reduction and the volume increased with the peak temperature. By increasing welding time, lap shear tensile tests show that the peak load increased from 5.3 kN to 6.55 kN. The corresponding interfacial shear strength ranged from 96.29 MPa to 99.72 MPa, lower than the shear strength of both base materials (331 MPa for AA7075 and 185 MPa for A380). All joint samples exhibited interfacial fracture after lap shear tensile testing, with a thin layer of A380 remnant attached to AA7075 at the center of the fractured surface.

36 MATERIALS SCIENCE↗