Targeted synthesis and reaction mechanism discussion of Mo 2 C based insertion-type electrodes for advanced pseudocapacitors
Mo 2 C is one of the few compounds that possess good electronic conductivity. Meanwhile, it possesses a natural 1D zigzag tunnel structure that is ideally suited for fast ion diffusion. Here, an effective approach is demonstrated for fabrication of structurally stable N-doped Mo 2 C/C nanobelts. They demonstrate high and fast energy storage ability with initial capacitances of 1139 C g -1 at 1 mV s-1, 151 C g -1 at an extremely high scan rate of 2000 mV s -1 and 208 C g -1 at a discharge current density of 200 A g -1 . After electrochemical activation of cycling, the capacity is continuously enhanced and much higher capacitances of 2523 C g -1 at 1 mV s -1 and 1403 C g -1 at 50 A g -1 are achieved after 15,000 cycles at 50 mV s -1 . Using the power law, it is evaluated that a surface-controlled capacitive process makes the main contribution to the capacity, which is over 90% when the scan rates are higher than 10 mV s -1 and still high as 73% at 1 mV s -1 . From in situ synchrotron XRD, it is found that there is a negligible change in the crystal structure and volume during charging/discharging, reflecting an insertion-type charge storage mechanism.