DOE OSTI2022

Micro- to nano-scale areal heterogeneity in pore structure and mineral compositions of a sub-decimeter-sized Eagle Ford Shale

Mineral and organic matter compositions & pore structures of fine-grained shale influence reservoir properties. To improve the understanding of spatial heterogeneity in core-sized samples, methods of microscale X-ray fluorescence (μXRF) mapping, (ultra-) small-angle x-ray scattering [(U)SAXS] and wide-angle X-ray scattering (WAXS) have been used to determine elemental, pore-structure variations at scales up to ~10 cm on two samples prepared at circular and rectangular orientations from a piece of Eagle Ford Shale outcrop in South Texas, USA. In addition, thin section petrography and field emission-scanning electron microscopy observations, X-ray diffraction (XRD), total organic carbon, and pyrolysis were utilized to investigate the potential spatial heterogeneity of pore types, mineral and organic matter compositions for cm-sized samples at both orientations. Overall, the siliceous-carbonate mineral contents in these two samples (8 cm×8 cm×0.08 cm and 5 cm × 8 cm × 0.08 cm, in terms of width×length×thickness) of carbonate-rich Eagle Ford Shale vary between laminations at mm scales. For the circular sample, porosity and specific surface area (SSA) variations range from 0.82 to 3.04% and 1.51 to 14.1 m 2 /g, respectively. For the rectangular sample, values for porosity and SSA vary from 0.93 to 2.50% and 3.95 to 10.8 m 2 /g. By analyzing six selected sub-samples on each of two samples with (U)SAXS and XRD techniques, nm-sized pores are mainly interparticle ones in the higher calcite regions, where the porosity is also relatively lower, while the lower calcite regions consist of both interparticle and intraparticle pore types with higher porosity. Lastly, the μXRF and (U)SAXS mappings are combined to generate porosity distribution maps to provide more insights about sample heterogeneity related to the laminations and fractures at our observational scales.

58 GEOSCIENCES↗
DOE OSTI2025

Resolving Lonsdaleite's decade-long controversy: Atomistic insights into a metastable diamond polymorph

Lonsdaleite, a theoretically proposed hexagonal diamond polymorph, has remained at the center of a five-decade scientific controversy since its 1967 identification. While some studies claim it exhibits superior hardness through compression-induced structural changes, others contend it is merely a stacking-faulted cubic diamond. Meteoritic samples and synthetic preparations have yielded conflicting evidence, with even advanced characterisation techniques like XRD and TEM failing to provide definitive proof. In this work, we employ first-principles density functional theory (DFT) and molecular dynamics (MD) simulations to generate unambiguous theoretical fingerprints through XRD, Raman, and SAED patterns that distinguish true Lonsdaleite from cubic diamond and its defective variants. Our atomistic approach quantifies the thermodynamic metastability of Lonsdaleite under realistic pressure-temperature conditions, reveals distinct spectral signatures through simulated Raman and resolves the structural ambiguity through generalised stacking fault energy analysis. By establishing clear criteria for definitive identification, this study provides long-awaited clarity to the Lonsdaleite debate while offering a robust computational framework for characterising metastable carbon phases in meteoritic, synthetic and industrial materials.

DFT↗
DOE OSTI2025

Electrodeposition of near-equiatomic CoCuFeNi multi-principal element alloys from an acidic glycine-citrate-triton X100 aqueous electrolyte

Understanding the composition and morphology control of electrodeposited CoCuFeNi is the first step to finding a general strategy for developing electrodeposition processes of unconventional alloys with large redox potential differences and complicated deposition mechanisms. Here, in this work, we have successfully synthesized the near-equiatomic (<5 at% error) CoCuFeNi films with ~200nm thickness by electrodeposition from glycine-citrate-Triton X-100 acidic electrolytes. This system generally follows the Principle II in Brenner’s paradigm on alloy composition control in electrodeposition. X-ray diffraction (XRD) profiles show that the films only consist of one crystalline phase, different from the deposit from ammonia-citrate-boric acid electrolytes and the equilibrium phases predicted by CALPHAD. The near-equiatomic deposits at Ru substrates were successfully annealed at 400 ° C without significant intermixing between the substrate and the deposit, in which no phase separation of the crystalline phase was observed in its XRD profile. Xray photoelectron spectroscopy (XPS) reveals that some depositing elements (mainly Fe) exist as metal oxides. Cu is dissolved in the crystalline phases, stabilized by small crystalline domain size and the amorphous metal oxides inside the CoCuFeNi deposits.

CoCuFeNi↗
DOE OSTI2022

Melting and phase relations of Fe-Ni-Si determined by a multi-technique approach

Many studies have suggested silicon as a candidate light element for the cores of Earth and Mercury. However, the effect of silicon on the melting temperatures of core materials and thermal profiles of cores is poorly understood, due to disagreements among melt detection techniques, uncertainties in sample pressure evolution during heating, and sparsity of studies investigating the combined effects of nickel and silicon on the phase diagram of iron. Here, in this study we develop a multi-technique approach for measuring the high-pressure melting and solid phase relations of iron alloys and apply it to Fe 0.8 Ni 0.1 Si 0.1 (Fe-11wt%Ni-5.3wt%Si), a composition compatible with recent estimates for the cores of Earth and Mercury. This approach combines results (20-83 GPa) from two atomic-level techniques: synchrotron Mossbauer spectroscopy (SMS) and synchrotron x-ray diffraction (XRD). Melting is independently detected by the loss of the Mossbauer signal, produced exclusively by solid-bound iron nuclei, and the onset of a liquid diffuse x-ray scattering signal. The use of a burst heating and background updating method for quantifying changes in the reference background during heating facilitates the determination of liquid diffuse signal onsets and leads to strong reproducibility and excellent agreement in melting temperatures determined separately by the two techniques. XRD measurements additionally constrain the hcp-fcc phase boundary and in-situ pressure evolution of the samples during heating. We apply our updated thermal pressure model to published SMS melting data on fcc-Fe and fcc-Fe 0.9 Ni 0.1 to precisely evaluate the effect of silicon on melting temperatures. We find that the addition of 10 mol% Si to Fe 0.9 Ni 0.1 reduces melting temperatures by ~250 K at low pressures (<60 GPa) and flattens the hcp-fcc phase boundary. Extrapolating our results, we constrain the location of the hcp-fcc-liquid quasi-triple point at 147±14 GPa and 3140±90 K, which implies a melting temperature reduction of 500 K compared with Fe 0.9 Ni 0.1 . The results demonstrate the advantages of combining complementary experimental techniques in investigations of melting under extreme conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2025

In situ deformation of antigorite-olivine two-phase mixtures: Implications for dynamics and seismic anisotropy in the mantle wedge

Water released from hydrous minerals in subducting slabs reacts with the overlying plate, resulting in widespread serpentinization in the mantle wedge. Deformation of serpentinized peridotites has been invoked to explain forearc seismic anisotropy, yet studies of the mechanical properties and deformation behaviors of serpentine-bearing multiphase aggregates remain limited. Here we deformed olivine-antigorite mixtures containing 70, 50, and 20 vol.% of antigorite at 2.5 – 7.6 GPa, 673 K and strain rates of ∼10 –5 –10 –4 s –1 . Elasto-viscoplastic self-consistent simulations, constrained by synchrotron X-ray diffraction (XRD) data, were used to estimate lattice strain, stress–strain partitioning, crystallographic preferred orientations (CPO) development, and aggregate strength. Selected run products were also analyzed by electron backscatter diffraction for comparison with the CPO results obtained from XRD experiments. We found olivine transitions from A- or B-type to C-type when antigorite fraction drops to 20 vol.%, coinciding with a microstructural change from interconnected weak layers to a load-bearing framework (LBF). An additional run on a sample Atg50/Ol50 with preexisting microstructures suggested the formation of LBF was promoted by these microstructures, although the preexisting antigorite CPO has been overprinted at 20.8 % strain and could be erased completely by subsequent deformation in nature. Estimated viscosity of the two-phase mixtures suggests that low-degree serpentinization (≤20 %) in the mantle wedge may increase the strength of olivine-rich peridotite and hinder slab-mantle decoupling, whereas high-degree serpentinization (≥50–70 %) weakens the peridotite and favors decoupling if sufficient viscosity contrast (>10) develops. Seismic anisotropy shows a nonlinear dependence on antigorite fraction: antigorite CPO governs the anisotropy of the mixtures with ≥50 vol.% antigorite, whereas olivine CPO dominates at low fractions (∼20 vol.%). The presence of pre-existing microstructures reduces seismic anisotropy of the deformed mixtures, however the persistence of pre-existing CPO in actively subducting slabs remains uncertain, making their significance over geological timescales questionable.

Crystallographic preferred orientation↗
DOE OSTI2026

Synchrotron resolved microscale mineralogy and elemental composition of individual plinthic and manganiferous nodules from agricultural soils

Iron and manganese oxides are strong sorbents and elemental scavengers in the environment that can form macroscopic nodules in soils. Despite their importance in the geochemical cycling of nutrients and contaminants, nodules are rarely characterized. When analyzed, they are often combined into bulk samples, obscuring individual characteristics. This study investigates the composition and mineralogy of individual plinthic and manganiferous nodules in soil from cropping systems in the Farming Systems Project in Beltsville, Maryland. Elemental composition indicates the accumulation of contaminants and nutrients, including copper in all nodules and high levels of phosphorus in select nodules. Sequential extractions determine that highly crystalline minerals comprise the nodules, locking away these nutrients and contaminants. Bulk X-ray diffraction (XRD) demonstrated distinct mineralogies in the plinthic and manganiferous nodules, with the former comprised of quartz, goethite, and kaolinite, and the latter consisting of quartz, Mn 2 O 3 , and hematite. Synchrotron and laboratory-based X-ray fluorescence (XRF) mapping gives critical insight into the elemental distribution within the nodules and elucidates spatial elemental associations, including the coupling of manganese and iron in the manganiferous nodules. XRF maps paired with µXRD provide microscale spatial resolution in mineralogy, which resolved several phases not apparent in bulk XRD, manganese’s association with goethite, and minerals indicative of redox transformations, including magnetite and maghemite. These novel results provide critical insight into the microscale mineralogy and individual elemental composition of plinthic and manganiferous nodules, as well as how they alter bulk soil geochemistry in ways largely unaccounted for in research on soil systems.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Effect of pore fluid chemistry on the mechanical behavior of a divalent compacted bentonite, an experimental and constitutive study

Ongoing research in isolating high-level nuclear waste and spent fuel has highlighted compacted bentonite as a suitable material for engineered barrier systems in deep geological repositories due to its extraordinary swelling and retention properties. This research focuses on the chemo-mechanical behavior of compacted bentonite exposed to different pore fluids with different concentrations and loading conditions. The study involves swelling pressure and compressibility experiments along with mineralogy analysis employing X-ray diffraction (XRD) and Cation exchange. The tests were conducted on BCV (a Mg/Ca- bentonite) compacted at a dry density of 1.48 ± .02 Mg/m 3 . An advanced chemical-mechanical constitutive model for unsaturated highly expansive clays was adopted to simulate the material response and better understand its behavior. The model is able to account for the main phenomena at both macro and microstructural levels and the interactions between them. The model successfully replicated experimental observations. The XRD analyses support the macroscopic observation, indicating that salinity impacts crystalline swelling as demonstrated by the reduction of basal spacing from 19.27 Å to 15.68 Å when the osmotic suction increases from 0 MPa to 33 MPa. The results suggested that the osmotic pressure generated by the concentration in the pore fluids promotes a reduction in swelling pressures, swelling strains, and crystalline swelling of clay minerals. Also, it affects the pre-consolidation stress and the compressibility of the compacted samples. In conclusion, it was also observed that both solution type and solution concentration impact the clay swelling pressure.

Chemo-mechanical constitutive model↗
DOE OSTI2023

Improved catalytic activity of Mo x Ni y Al z thin films as electrocatalyst for hydrogen evolution reaction in alkaline media

In this work, we report activities of Mo x Ni y X z (where X is Al, Co, Cr, Cu, Fe, W)-based electrocatalysts for hydrogen evolution reaction (HER) in a 1 M NaOH solution. Mo x Ni y X z thin film electrocatslysts were prepared by magentron sputtering at 25°C and 800°C and characterized by scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analyzer and X-ray diffraction (XRD) analysis. Here, the catalytic activity of electrocatalyst was studied by cyclic voltammetry and electrochemical impedance spectroscopy. The electrocatalyst based on Mo 80 Ni 5 Al 15 (800°C) shows the best value of the overpotential (-181 mV) for HER from all tested ternary systems. XRD analysis indicates that HER activity only Mo 80 Ni 5 Al 15 thin films prepared at 800°C contained fcc phase. Other less active composition contained only bcc phase. The results obtained from impedance spectroscopy are consistent with the results from cyclic voltammetry. The stability of the prepared catalyst was studied by chronoamperometric analysis. The results from chronoamperometry show that HER activity of Mo 80 Ni 5 Al 15 prepared at 800°C, after very slight initial activity decrease, stays constant, while activity of Ni catalyst decreased almost twice in measured time window. Since Ni is commonly used industrial catalyst, Mo 80 Ni 5 Al 15 based alloy could be more attractive catalyst material for alkaline electrolyzers.

08 HYDROGEN↗
DOE OSTI2023

Activated carbon supported Ni, Fe, and bimetallic NiFe catalysts for CO x -free H 2 production by microwave methane pyrolysis

The goal of this study was to test the effect of metal-impregnated carbon-based catalysts on the conversion of methane to hydrogen gas and solid carbon using microwave reactor technology. Monometallic and bimetallic catalysts on activated carbon supports (Ni/AC, Fe/AC, Ni-Fe/AC) are compared during methane pyrolysis testing. Catalytic methane pyrolysis was carried out in a microwave reactor at reaction temperatures of 600 °C and 800 °C. For comparison, one of the catalysts (Ni-Fe/AC) was tested in a conventionally heated reactor at 800 °C. The prepared catalysts were characterized by X-ray diffraction (XRD), while post-reaction catalysts were characterized by XRD and SEM. During reaction testing, the monometallic Ni/AC catalyst exhibited the best catalytic activity (CH 4 conversion: 46.0 and H 2 yield: 46.9%) when reacted in the microwave reactor, however, it suffered from rapid deactivation from carbon deposition (carbon yield: 0.39 gC/g catalyst). The bimetallic Ni-Fe/AC catalyst was slightly less active (CH 4 conversion: 36.9 and H 2 yield: 40.5%) but it was more resistant to carbon formation (carbon yield: 0.27 gC/g catalyst) suggesting it may have greater long-term stability. The Ni-Fe/AC catalyst was also the most energy efficient as it required the least microwave power to maintain the 800 °C reaction temperature compared to the other catalysts tested. Methane conversion of the bimetallic Ni-Fe/AC at 800 °C under microwave irradiation was three times the conversion under conventional heating at the same reaction temperature. Finally, this work demonstrates the use of microwave-specific catalysts for catalytic methane pyrolysis in a microwave reactor, and can be used as a foundation for further methane pyrolysis process and catalyst optimization for CO x -free H 2 production.

08 HYDROGEN↗
DOE OSTI2022

From ammonium Hexahalorhenates(IV) to nanocrystalline rhenium metal: A combined thermal, diffraction and microscopic analysis

Rhenium metal powder is a material of industrial importance. Several industrial and laboratory methods have been developed for the preparation of ultrafine Re metal powder and nanoparticles. The present study provides a better understanding of the characteristic and formation of Re metal powder from the decomposition of (NH4)2ReX6 salt (X = F, Cl, Br, I) at high temperature in inert atmosphere. Such analysis resulted in the formation of nanocrystalline Re metal as characterized by powder XRD. Williamson-Hall, Scherrer, and Williamson-Smallman methods were employed to study the effect of crystallize size, lattice strain, and dislocation density as analyzed from powder XRD peak broadening. Here, the morphology and composition of the metal were analyzed using scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Thin film combinatorial sputtering of Al-Ce alloys: Investigating the phase separation of as-deposited solid solutions and determining the coefficient of thermal expansion

Al x Ce 100–x thin films with a composition range of ~75.0 < x < 99.5 at% (36.5 < x < 97.5 wt%) were synthesized via combinatorial co-sputtering from an Al and an Al 50 Ce 50 target. The crystal structure, phase fraction, film morphology, electrical resistivity, and temperature-dependent coefficients of thermal expansion (CTE) are all correlated to the Al x Ce 100–x composition. The as-deposited films form a metastable solid-solution, and annealing leads to the formation of the thermodynamically stable two-phase system of Al and the α-Al 11 Ce 3 intermetallic. Temperature dependent x-ray diffraction (XRD) reveals that the two phases expand independently of one another, and the thin film Al temperature-dependent CTE is similar to bulk Al. The thin film Al 11 Ce 3 intermetallic phase has a nearly constant CTE of ~1.5 × 10 –5 /°C within the temperature range studied (25–550 °C). To confirm the thin film Al 11 Ce 3 results, bulk stoichiometric Al 11 Ce 3 and +/- 1 wt% Ce samples were prepared and the CTE of each was measured with the same conditions. A Rietveld analysis of the bulk data enabled an estimation of the CTE in each of the 3 orthorhombic lattice parameters, which displayed anisotropic behavior. The thin film and bulk CTE measurements were in very good agreement. Estimations of the temperature dependent CTE of the two-phase alloys are made via the Reuss and Voigt models. Finally, by demonstrating the efficacy of the approach, more complex multi-component rapid materials discovery of low CTE Al-alloys can be pursued via the combinatorial thin film synthesis and XRD measurement.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The Effect of Dopant Concentration and Annealing Treatments on N-Type Iodine Doped CdTe

We report properties of highly conducting n-type cadmium telluride single crystals doped with iodine (CdTe:I). These crystals were grown with dopant concentrations in the range of 10^17 cm-3 to 10^19 cm-3 by Modified Vertical Bridgman (MVB) melt growth. Post-growth dopant activation, including Cd annealing, Te annealing, and rapid thermal annealing (RTA), was applied to improve free carrier density. The structural, optical, and electrical properties were analyzed by Glow Discharge Mass Spectroscopy (GDMS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Photoluminescence Spectroscopy (PL), optical absorption, Hall measurements, Capacitance-Voltage (CV) measurements, and time-resolved photoluminescence (TRPL). The results indicate that Cd annealing is the most effective activation method to get 100% donor activation (n is approximately 2 x 10^18 cm-3), which is close to the room temperature solubility limit of iodine. This leads to the lowest resistivity and the highest mobility. Moreover, this data suggests a potential role of Cd vacancy-related defects on electrical self-compensation.

annealing↗
DOE OSTI2023

Epitaxial growth and characterization of magnesium gallate (MgGa 2 O 4 ) thin films by pulsed laser deposition

To advance high power device application of MgGa 2 O 4 , it is imperative to achieve crystalline epitaxial thin films and to observe its materials’ characteristics within a wide range of growth conditions. However, there is no published work on the growth of this promising ultrawide bandgap material till this day. In this study, we report the crystalline growth of MgGa 2 O 4 thin films on c-plane (006) sapphire substrates using the pulsed laser deposition (PLD) technique in a broad range of temperature and oxygen pressure. The temperature range for this crystalline growth was within the temperature range of 300°C to 700°C and a pressure range of 1x10 -1 to 1x10 -3 Torr. Within this parameter range, the structural, chemical, optical, and surface property of MgGa 2 O 4 thin films have been investigated. Specifically, the acquired XRD patterns confirmed the film growth along the [111] preferential crystal orientation in the lattice. Here, the rocking curve measurement of the prominent (222) plane showed an increasing trend of the crystallinity with growth temperature and pressure. Furthermore, the XRD phi (φ) scan demonstrated the six-fold rotational symmetry of the MgGa 2 O 4 films and the epitaxial relationship of 30° between the film and the sapphire substrate. The XPS spectra confirmed the presence of +2 and +3 oxidation state for Mg and Ga respectively, in the films. The direct bandgap of MgGa 2 O 4 films was obtained ~5.27±0.03 eV by analyzing the UV-Vis absorbance spectra using the Tauc equation. The SEM images exhibited a granular surface morphology of the MgGa 2 O 4 films with an increasing trend in the grain size from low to high temperature and pressure. The refractive index and thickness of these films were in the range of ~1.90±0.02 and ~70±2.0 nm, respectively determined by fitting the spectroscopic ellipsometry data.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Influence of Pt-Metal Alloy Catalysts with Various Ionomers on Oxygen Reduction Reaction in Fuel Cell Application

Pt-M/C (M = Co, Ni, Mn, etc.) alloy catalysts exhibit superior oxygen reduction reaction (ORR) activity compared to pure Pt/C, leading to a high energy efficiency in hydrogen fuel cells. However, many Pt-M/C alloy catalysts were synthesized and evaluated at the lab scale in model test-bed systems like rotating disc electrodes, which don't always correlate to performance within a fuel cell system; there is a clear need to evaluate catalysts in electrodes that can be prepared at industrially relevant scales to evaluate how factors like ink formulation can greatly affect device-level of fuel cell performance. Herein, three commercial Pt-M/C alloy catalysts (two Pt-Co/C and one Pt-Ni/C) were comprehensively characterized by various techniques. The results show that the average particle sizes of the three catalysts are close to 5 nm; the atomic ratio of Pt/M is around 4; and the M was successfully embedded into Pt lattice, resulting in the positive shift of Pt 4f in XPS spectra and XRD patterns. These catalytic materials were incorporated into 9 different cathode catalyst layers (CCLs) with three kinds of ionomers (Nafion D2020, high oxygen permeability ionomer (HOPI), and Aquivion D79-25BS), and their performance in proton exchange membrane fuel cells (PEMFCs) were investigated. The results demonstrate that the Pt-Co/C catalysts possess a higher mass activity (MA) than Pt-Ni/C; the cathodes with Nafion ionomer provide the highest MA while electrodes with Aquivion ionomer showed the lowest activity, attributed to poor H+ conductivity resulting from suboptimal ionomer incorporation. Finally, these alloys were shown to exceed DOE targets for MA and H2/Air performance reported in the recent publications at beginning of life and after 90k cycle catalyst AST protocol. This study provides valuable performance benchmarks for these materials guiding future Pt-M/C catalyst design and material integration for heavy duty PEMFC applications.

08 HYDROGEN↗
DOE OSTI2020

Direct processing of PbZr 0.53 Ti 0.47 O 3 films on glass and polymeric substrates

This work reports on direct crystallization of PbZr 0.53 Ti 0.47 O 3 (PZT) thin films on glass and polymeric substrates, using pulsed thermal processing (PTP). Specifically, xenon flash lamps deliver pulses of high intensity, short duration, broadband light to the surface of a chemical solution deposited thin film, resulting in the crystallization of the film. Structural analysis by X-ray diffraction (XRD) and transmission electron microscopy show the existence of perovskite structure in nano-sized grains (≤5 nm). Local functional analysis by band excitation piezoelectric spectroscopy and electrostatic force microscopy confirm the presence of a ferroelectric phase and retention of voltage-written polarization for multiple days. Based on structural and functional analyses, strategies are discussed for optimization of pulse voltage and duration for the realization of crystalline ferroelectric thin films. For ~200 nm-thick PZT films on glass substrates, 500 μs-long pulses were required for crystallization, starting with 100 pulses at 350 V, 10 or 25 pulses at 400 V and in general lower number of pulses at higher voltages (resulting in higher radiant energy). Overall power densities of >6.4 kW/cm 2 were needed for appearance of peaks corresponding to the perovskite phase in the XRD. Films on glass processed at 350–400 V had a higher degree of 111-oriented perovskite grains. Higher applied radiant energy (through increased pulse voltage or count) resulted in more random and/or partially 001-oriented films. For ~1 μm-thick PZT films on polymeric substrates, 10 to 25 250 μs-long pulses at voltages ranging between 200 to 250 V, corresponding to power densities of ~2.8 kW/cm 2 , were optimal for maximized perovskite phase crystallization, while avoiding substrate damage.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Structure and properties of NdCuGa 3 single crystals

Here this manuscript reports on the structural and magnetic properties of NdCuGa 3 using powder and single crystal X-ray diffraction (XRD), zero-field single crystal neutron diffraction, magnetization, and specific heat measurements. Our XRD on a single crystal specimen of NdCuGa3 confirmed that it crystallizes in the tetragonal BaNiSi 3 -type structure. A magnetic phase transition at T N = 3.3 K is assessed using specific heat and ac magnetic susceptibility measurements. No additional anomaly below T N down to 50 mK was detected by performing specific heat measurements. Neutron single crystal diffraction data collected at T = 300 mK confirm the antiferromagnetic phase below T N = 3.3 K with the propagation vector $\vec{\tau}$ = (0.2, 0, 0). Possible magnetic structure solutions of NdCuGa 3 are discussed

36 MATERIALS SCIENCE↗
DOE OSTI2025

What causes the variation in superconducting properties of UTe 2 ?

Reaching a consensus on the superconducting order parameter of unconventional superconductors remains a central challenge in the field of magnetically-mediated superconductivity. Though UTe 2 is largely accepted as a rare example of an odd-parity superconductor, its precise order parameter remains highly debated, even at ambient conditions. A key underlying issue is the large sample-to-sample variation in superconducting properties at zero applied pressure and magnetic field. Here, we investigate the origin of the observed variation by means of single crystal x-ray diffraction (SC-XRD) and scanning transmission electron microscopy (STEM) measurements. Our results reveal highly ordered crystalline lattices, in agreement with the expected Immm structure, and no signs of uranium vacancies. Tiny amounts of interstitial defects, however, are observed on the Te2 layers that host Te chains along the b axis. We argue that these defects give rise to slightly enhanced atomic displacement parameters observed in SC-XRD data and are enough to disrupt the unconventional superconducting state in UTe 2 . Our findings highlight the need to focus future order parameter determination efforts on single crystals of UTe 2 with minimal amounts of structural disorder.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2022

Multimodal analysis and characterization of the boehmite layer formed on AA6061 before and after alkaline etching

Low-enriched uranium (LEU) alloyed with 10% Mo (U-10Mo) is being considered as a promising alternative to oxide-based dispersion fuel with high-enriched uranium for use in research reactors. The configuration of this proposed LEU monolithic LEU fuel plate consists of a U-10Mo plate-type fuel foil with a 25 µm zirconium interlayer barrier clad with an aluminum alloy (AA6061). In certain research reactors, the clad AA6061 is coated with a boehmite layer to prevent corrosion. The boehmite layer has a high-pH passivation range, which makes it resistant to oxidation. Boehmite is usually formed on the AA6061 surface by autoclave processing. Before the boehmite layer is added, the surface of the AA6061 is cleaned using techniques such as polishing and wet etching. In this study, we use multimodal analysis to examine how pretreatment of AA6061 using polishing followed by alkaline etching affects the chemical composition of the boehmite layer. X-ray photoelectron microscopy (XPS), transmission electron microscopy (TEM), and x-ray diffraction (XRD) were used to study the chemical changes in the boehmite layer caused by alkaline etching pretreatment. XPS provides quantitative analysis for the Al:O ratio as well as oxidation states present on the surface, which suggests slight oxidation of the boehmite surface after alkaline etching of the AA6061 surface. We further explored this suggested oxidation of the boehmite surface using high-resolution transmission electron microscopy with selected area electron diffraction (SAED) and grazing incidence x-ray diffraction (GI-XRD), which suggested only a small amount of aluminum oxide at the surface. The multimodal analysis and imaging yielded new insights for optimizing boehmite growth on AA6061 for research reactors.

36 MATERIALS SCIENCE↗