NASA NTRS2002

Weibull-Based Design Methodology for Rotating Aircraft Engine Structures

The NASA Energy Efficient Engine (E(sup 3)-Engine) is used as the basis of a Weibull-based life and reliability analysis. Each component's life and thus the engine's life is defined by high-cycle fatigue (HCF) or low-cycle fatigue (LCF). Knowing the cumulative life distribution of each of the components making up the engine as represented by a Weibull slope is a prerequisite to predicting the life and reliability of the entire engine. As the engine Weibull slope increases, the predicted lives decrease. The predicted engine lives L(sub 5) (95 % probability of survival) of approximately 17,000 and 32,000 hr do correlate with current engine maintenance practices without and with refurbishment. respectively. The individual high pressure turbine (HPT) blade lives necessary to obtain a blade system life L(sub 0.1) (99.9 % probability of survival) of 9000 hr for Weibull slopes of 3, 6 and 9, are 47,391 and 20,652 and 15,658 hr, respectively. For a design life of the HPT disks having probable points of failure equal to or greater than 36,000 hr at a probability of survival of 99.9 %, the predicted disk system life L(sub 0.1) can vary from 9,408 to 24,911 hr.

Zaretsky, Erwin↗
NASA NTRS2016

Evaluation of 10V Chip Polymer Tantalum Capacitors for Space Applications

Due to low ESR and safe failure mode, new technology chip polymer tantalum capacitors (CPTC) have gained popularity in the electronics design community, first in commercial applications, and now in hi-rel and space systems. The major drawbacks of these parts are high leakage currents, degradation under environmental stresses, and a relatively narrow temperature range of operating and storage conditions. Several studies have shown that a certain amount of moisture in polymer cathodes is necessary for a normal operation of the parts. This might limit applications of CPTCs in space systems and requires analysis of long-term exposure to deep vacuum conditions on their performance and reliability. High leakage currents and limited maximum operational temperature complicate accelerated testing that is necessary to assess long-term reliability and require new screening and qualification procedures for quality assurance. A better understanding of behavior of CPTCs as compared to traditional, MnO2, capacitors is necessary to develop adequate approaches for QA system for space applications. A specific of CPTCs is that different materials and processes might be used for low-voltage (10 V and less) and high-voltage (above 10 V) capacitors, so performance and degradation processes in these groups require separate analysis. In this work, that is a part of the NASA Electronic Parts and Packaging (NEPP) program, degradation of AC and DC characteristics under environmental stresses at different temperatures and voltages have been studied in nine lots of commercial and automotive grade capacitors rated to 10 V. Results of analysis of leakage currents, high temperature storage (HTS) up to 5000 hrs in vacuum and air at different temperatures, and Highly Accelerated Life Testing (HALT) in the range from 85 C to 145 C are presented. Temperature and voltage acceleration factors were calculated based on approximation of distributions of degradation rates with a general log-linear Weibull model. Mechanisms of degradation and failures, and requirements for screening and qualification testing are discussed.

Tantalum Capacitors↗
NASA NTRS1986

A Monte Carlo study of Weibull reliability analysis for space shuttle main engine components

The incorporation of a number of additional capabilities into an existing Weibull analysis computer program and the results of Monte Carlo computer simulation study to evaluate the usefulness of the Weibull methods using samples with a very small number of failures and extensive censoring are discussed. Since the censoring mechanism inherent in the Space Shuttle Main Engine (SSME) data is hard to analyze, it was decided to use a random censoring model, generating censoring times from a uniform probability distribution. Some of the statistical techniques and computer programs that are used in the SSME Weibull analysis are described. The methods documented in were supplemented by adding computer calculations of approximate (using iteractive methods) confidence intervals for several parameters of interest. These calculations are based on a likelihood ratio statistic which is asymptotically a chisquared statistic with one degree of freedom. The assumptions built into the computer simulations are described. The simulation program and the techniques used in it are described there also. Simulation results are tabulated for various combinations of Weibull shape parameters and the numbers of failures in the samples.

Abernethy, K.↗
NASA NTRS1980

Effect of production processes on the fracture strength of silicon solar cells

Fracture of Czochralski silicon wafers during processing is an important factor in solar cell yield and cost. A fracture-mechanics test and analysis program was developed to evaluate fracture strength changes in the in-process wafer-to-cell processing at different stages on a manufacturer's production line. The strength data were described by Weibull statistical analysis and can be interpreted with the surface-flaw distribution of each of the process steps.

Chen, C. P.↗
NASA NTRS1985

Fracture strength of GaAs solar cells as a function of manufacturing process steps

Fracture of single crystal GaAs substrate during the solar cell processing is an important factor in solar cell yield and cost. Fracture mechanics technique was utilized to evaluate cell cracking characteristics and changes in fracture strength of GaAs solar cells in a present state-of-the-art of manufacturing process for GaAs solar cells from wafer to complete cell of a typical production line. Considerable change in the fracture strength of GaAs solar cells as a function of cell processing was found. The strength data were described by Weibull statistical analysis and can be interpreted with the change of flaw distribution of each of the manufacturing process steps.

Chen, C. P.↗
NASA NTRS1986

Some design considerations for ceramic components in heat engine applications

The design methodology for brittle material structures which is being developed and used at the Lewis Research Center for sizing ceramic components in heat engine applications is reviewed. Theoretical aspects of designing with structural ceramics are discussed, and a general purpose reliability program for predicting fast fracture response due to volume distributed flaws is described. Statistical treatment of brittle behavior, based on the Weibull model, is reviewed and its advantages, as well as drawbacks, are listed. A mechanistic statistical fracture theory, proposed by Batdorf to overcome the Weibull model limitations and based on Griffith fracture mechanics, is summarized. Failure probability predictions are made for rotating annular Si3N4 disks using various fracture models, and the results are compared to actual failure data. The application of these design methods to Government funded ceramics engine demonstration programs is surveyed. The uncertainty in observed component performance emphasizes the need for proof testing and improved nondestructive evaluation to guarantee adequate structural integrity.

Gyekenyesi, John P.↗
NASA NTRS2016

Degradation of Leakage Currents and Reliability Prediction for Tantalum Capacitors

Two types of failures in solid tantalum capacitors, catastrophic and parametric, and their mechanisms are described. Analysis of voltage and temperature reliability acceleration factors reported in literature shows a wide spread of results and requires more investigation. In this work, leakage currents in two types of chip tantalum capacitors were monitored during highly accelerated life testing (HALT) at different temperatures and voltages. Distributions of degradation rates were approximated using a general log-linear Weibull model and yielded voltage acceleration constants B = 9.8 +/- 0.5 and 5.5. The activation energies were Ea = 1.65 eV and 1.42 eV. The model allows for conservative estimations of times to failure and was validated by long-term life test data. Parametric degradation and failures are reversible and can be annealed at high temperatures. The process is attributed to migration of charged oxygen vacancies that reduce the barrier height at the MnO2/Ta2O5 interface and increase injection of electrons from the MnO2 cathode. Analysis showed that the activation energy of the vacancies' migration is ~ 1.1 eV.

acceleration factors↗
NASA NTRS1995

Reliability Analysis of Uniaxially Ground Brittle Materials

The fast fracture strength distribution of uniaxially ground, alpha silicon carbide was investigated as a function of grinding angle relative to the principal stress direction in flexure. Both as-ground and ground/annealed surfaces were investigated. The resulting flexural strength distributions were used to verify reliability models and predict the strength distribution of larger plate specimens tested in biaxial flexure. Complete fractography was done on the specimens. Failures occurred from agglomerates, machining cracks, or hybrid flaws that consisted of a machining crack located at a processing agglomerate. Annealing eliminated failures due to machining damage. Reliability analyses were performed using two and three parameter Weibull and Batdorf methodologies. The Weibull size effect was demonstrated for machining flaws. Mixed mode reliability models reasonably predicted the strength distributions of uniaxial flexure and biaxial plate specimens.

Salem, Jonathan A.↗
NASA NTRS2017

Reliability Issues with PME and BME Ceramic Capacitors

This work is a review of reliability issues specific for low-voltage precious metal electrode (PME) and base metal electrode (BME) multilayer ceramic capacitors (MLCC). A special attention is given to degradation and failures in capacitors with defects, in particular with cracks. Temperature and voltage reliability acceleration factors have been calculated based on approximation of distributions of degradation rates of leakage currents using a general log-linear Weibull model. Results show a substantial difference in behavior of BME and PME capacitors with defects. Mechanisms of degradation and failures in humid and dry environments and risks of overstressing capacitors during highly accelerated life testing (HALT) are discussed.

Teverovsky, Alexander↗
NASA NTRS2019

Degradation of ESR in Polymer Tantalum Capacitors During High Temperature Storage

Replacement of MnO2 cathodes with conductive polymers in chip tantalum capacitors allows for a substantial reduction of the equivalent series resistance (ESR), improvement of frequency characteristics, and elimination of the possibility of ignition during failures. One of the drawbacks of chip polymer tantalum capacitors (CPTCs) is a relatively poor long-term stability at high temperatures. Due to degradation processes in conductive polymer materials, the existing quality assurance testing that has been developed for MnO2 capacitors is not sufficient to guarantee long-term stability of CPTCs. Insertion of CPTCs in hi-rel systems requires development of models that can predict degradation of the parts at operating conditions. In this work, variations of AC characteristics (capacitance, DF and ESR) in different types of capacitors from three manufacturers have been monitored during storage at temperatures from 100ºC to 175ºC for periods of up to 15,000 hours. Results show that the most sensitive to degradation parameter is ESR. Distributions of times to parametric failure during storage have been simulated using a Weibull-Arrhenius model that allowed for assessments of activation energies of degradation and prediction of times to failure at use temperatures. Mechanisms of degradation and the effect of packaging are discussed.

equivalent series resistance (ESR)↗
NASA NTRS2013

Unit-Sphere Anisotropic Multiaxial Stochastic-Strength Model Probability Density Distribution for the Orientation of Critical Flaws

Models that predict the failure probability of monolithic glass and ceramic components under multiaxial loading have been developed by authors such as Batdorf, Evans, and Matsuo. These "unit-sphere" failure models assume that the strength-controlling flaws are randomly oriented, noninteracting planar microcracks of specified geometry but of variable size. This report develops a formulation to describe the probability density distribution of the orientation of critical strength-controlling flaws that results from an applied load. This distribution is a function of the multiaxial stress state, the shear sensitivity of the flaws, the Weibull modulus, and the strength anisotropy. Examples are provided showing the predicted response on the unit sphere for various stress states for isotropic and transversely isotropic (anisotropic) materials--including the most probable orientation of critical flaws for offset uniaxial loads with strength anisotropy. The author anticipates that this information could be used to determine anisotropic stiffness degradation or anisotropic damage evolution for individual brittle (or quasi-brittle) composite material constituents within finite element or micromechanics-based software

Nemeth, Noel↗
NASA NTRS2000

Rolling Bearing Life Prediction-Past, Present, and Future

Comparisons were made between the life prediction formulas of Lundberg and Palmgren, Ioannides and Harris, and Zaretsky and full-scale ball and roller bearing life data. The effect of Weibull slope on bearing life prediction was determined. Life factors are proposed to adjust the respective life formulas to the normalized statistical life distribution of each bearing type. The Lundberg-Palmgren method resulted in the most conservative life predictions compared to Ioannides and Harris, and Zaretsky methods which produced statistically similar results. Roller profile can have significant effects on bearing life prediction results. Roller edge loading can reduce life by as much as 98 percent. The resultant predicted life not only depends on the life equation used but on the Weibull slope assumed, the least variation occurring with the Zaretsky equation. The load-life exponent p of 10/3 used in the American National Standards Institute (ANSI)/American Bearing Manufacturers Association (ABMA)/International Organization for Standardization (ISO) standards is inconsistent with the majority roller bearings designed and used today.

Zaretsky, E V↗
NASA NTRS1989

Improved silicon carbide for advanced heat engines

The development of high strength, high reliability silicon carbide parts with complex shapes suitable for use in advanced heat engines is studied. Injection molding was the forming method selected for the program because it is capable of forming complex parts adaptable for mass production on an economically sound basis. The goals were to reach a Weibull characteristic strength of 550 MPa (80 ksi) and a Weibull modulus of 16 for bars tested in four-point loading. Statistically designed experiments were performed throughout the program and a fluid mixing process employing an attritor mixer was developed. Compositional improvements in the amounts and sources of boron and carbon used and a pressureless sintering cycle were developed which provided samples of about 99 percent of theoretical density. Strengths were found to improve significantly by annealing in air. Strengths in excess of 550 MPa (80 ksi) with Weibull modulus of about 9 were obtained. Further improvements in Weibull modulus to about 16 were realized by proof testing. This is an increase of 86 percent in strength and 100 percent in Weibull modulus over the baseline data generated at the beginning of the program. Molding yields were improved and flaw distributions were observed to follow a Poisson process. Magic angle spinning nuclear magnetic resonance spectra were found to be useful in characterizing the SiC powder and the sintered samples. Turbocharger rotors were molded and examined as an indication of the moldability of the mixes which were developed in this program.

Whalen, Thomas J.↗
NASA NTRS1995

Design Protocols and Analytical Strategies that Incorporate Structural Reliability Models

The general goal of this project is to establish design protocols that enable the engineer to analyze and predict certain types of behavior in ceramic composites. Sections of the final report addresses the following: Description of the Problem that Motivated the Technology Development, Description of the New Technology that was Developed, Unique and Novel Features of the Technology and Results/Benefits of Application (year by year accomplishments), and Utilization of New Technology in Non-Aerospace Applications. Activities for this reporting period included the development of a design analysis as part of a cooperative agreement with general Electric Aircraft Engines. The effort focused on modifying the Toughened Ceramics Analysis and Reliability Evaluation of Structures (TCARES) algorithm for use in the design of engine components fabricated from NiAl. Other activities related to the development of an ASTM standard practice for estimating Weibull parameters. The standard focuses on the evaluation and reporting of uniaxial strength data, and the estimation of probability distribution parameters for ceramics which fail in a brittle fashion.

Duffy, Stephen F.↗
NASA NTRS1988

Strength distribution in commercial silicon carbide materials

Four-point flexural strength testing has been conducted in order to establish the baseline strength and reliability of four different commercial SiC types, in conjunction with reliable Weibull modulus values. Average strength of the samples ranged from 380 to 482 MPa at room temperature and 307 to 470 MPa at 1370 C. The strength scatter reflects the effect of flaw variability, which must be minimized to improve reliability in sintered SiC.

Dutta, Sunil↗
NASA NTRS1992

Extreme value statistics analysis of fracture strengths of a sintered silicon nitride failing from pores

Statistical analysis and correlation between pore-size distribution and fracture strength distribution using the theory of extreme-value statistics is presented for a sintered silicon nitride. The pore-size distribution on a polished surface of this material was characterized, using an automatic optical image analyzer. The distribution measured on the two-dimensional plane surface was transformed to a population (volume) distribution, using the Schwartz-Saltykov diameter method. The population pore-size distribution and the distribution of the pore size at the fracture origin were correllated by extreme-value statistics. Fracture strength distribution was then predicted from the extreme-value pore-size distribution, usin a linear elastic fracture mechanics model of annular crack around pore and the fracture toughness of the ceramic. The predicted strength distribution was in good agreement with strength measurements in bending. In particular, the extreme-value statistics analysis explained the nonlinear trend in the linearized Weibull plot of measured strengths without postulating a lower-bound strength.

Chao, Luen-Yuan↗
NASA NTRS1992

Long-life assessment of graphite epoxy materials for Space Station Freedom pressure vessels

Graphite/epoxy composite overwrapped pressure vessels are being considered for use on Space Station Freedom because of their light weight and high efficiency. These composite pressure vessels weigh roughly one-third of comparable all-metal aluminum pressure vessels, and could result in a 15,000-lb weight saving for the propulsion and fluid management and distribution systems. These vessels must resist failures under sustained pressure loads for crew safety considerations and adequate protection of the space structure during their 30-yr life. Weibull statistical analysis techniques have been applied, and a model developed, for predicting long-term stress-rupture behavior based on published short-term test data on composite strands and pressure vessels. Graphite/epoxy materials are calculated to have a 99.99-percent probability of surviving stress rupture for 30 yr under a sustained load of 50 percent ultimate failure strength. Stress-rupture lifetimes are predicted to increase as the size of the pressure vessels increases in support of the viscoelastic load-transfer mechanism proposed for stress rupture of fiber/epoxy composite materials.

Thomas, Donald A.↗
NASA NTRS1985

Improved silicon nitride for advanced heat engines

The AiResearch Casting Company baseline silicon nitride (92 percent GTE SN-502 Si sub 3 N sub 4 plus 6 percent Y sub 2 O sub 3 plus 2 percent Al sub 2 O sub 3) was characterized with methods that included chemical analysis, oxygen content determination, electrophoresis, particle size distribution analysis, surface area determination, and analysis of the degree of agglomeration and maximum particle size of elutriated powder. Test bars were injection molded and processed through sintering at 0.68 MPa (100 psi) of nitrogen. The as-sintered test bars were evaluated by X-ray phase analysis, room and elevated temperature modulus of rupture strength, Weibull modulus, stress rupture, strength after oxidation, fracture origins, microstructure, and density from quantities of samples sufficiently large to generate statistically valid results. A series of small test matrices were conducted to study the effects and interactions of processing parameters which included raw materials, binder systems, binder removal cycles, injection molding temperatures, particle size distribution, sintering additives, and sintering cycle parameters.

Yeh, H. C.↗