Brittle fracture is difficult to study in situ due to the speed of a growing crack and the often-catastrophic nature of failure in brittle materials. As a result, the influence of microstructural considerations, such as orientation, grain boundary locations, and strain field, on the crack path remains poorly understood. Presented in this study is a method addressing this knowledge gap, which utilizes the double-cleavage drilled compression geometry to achieve quasi-stable fracture in aluminum oxynitride (AlON). Synchrotron X-ray micro-computed tomography is used to characterize the crack shape and length, while high-energy diffraction microscopy provides information on the strains, orientations, and shapes of grains in the microstructure surrounding the crack tip. During testing, the crack grew in discrete and irregular jumps while the fracture toughness falls within reported ranges. The crack in AlON is found to have no greater tendency to crack intergranularly as compared to transgranularly, and grains which are cracked transgranularly do not display a trend in orientation or stress when compared to those around which the crack followed a grain boundary. The high resolution of the crack path and microstructural data provides a path forward for modeling and understanding 3D brittle fracture.