Understanding the corrosion behavior of steels in supercritical carbon dioxide (S-CO2) is essential for ensuring the safe application of S-CO2 as a heat-transfer fluid in high-temperature energy systems, including advanced nuclear reactors. In this work, molecular dynamics (MD) simulations using ReaxFF potential are performed to explore the atomic-scale corrosion mechanisms of body-centered cubic iron (BCC-Fe) in S-CO2. The results show that CO2 molecules in S-CO2 decompose at the Fe surface, generating free C and O atoms that form Fe-C and Fe-O bonds and subsequently produce oxides and carbides. Concurrently, Fe atoms dissolve from the surface and diffuse into the S-CO2 region, resulting in interdiffusion of Fe, C and O atoms at the interface. The corrosion-layer thickness calculations show that high pressure and temperature induced by S-CO2 have stronger effects than surface orientation on the corrosion process. In addition, surface Fe atoms undergo substantial displacement under S-CO2 exposure, further accelerating corrosion. When a radiation-induced void is introduced near the Fe surface, the corrosion is enhanced. The void-matrix interface expands the reaction surface area and simultaneously induces corrosion reactions inside the bulk, resulting in a deeper penetration of C and O and thicker corrosion layers. All these results indicate that high-temperature, high-pressure and radiation-induced voids can seriously affect the corrosion of Fe in S-CO2, and must be considered to better use S-CO2 in nuclear facilities.