A Review of the Influence of Processing Parameters on ODS Steels Produced via Additive Manufacturing Techniques

Abstract

Abstract This paper reviews current observations regarding processing conditions for oxide dispersion-strengthened steels consolidated through additive manufacturing techniques. Variations in ODS steels observed across process parameters include changes in grain size, grain texture, oxide size, density of oxides, porosity, melt pool characteristics, and mechanical properties. These properties were then compared across techniques to understand which techniques and processing conditions lead to the highest strength, ductility, and oxide density. Current literature suggests that a mix of grain types, in the form of either morphology or phase, can significantly increase the strength of printed ODS steels. Meanwhile, the most ductile samples, regardless of consolidation technique or matrix material, were made from feedstock with oxide additions located on the powder surface. Reported grain and oxide sizes were plotted against the ratio of laser power to scan speed, volumetric energy density, and normalized enthalpy. No strong correlation between these values and microstructural features was observed. The plots that were made suggest that a larger data set, more in-depth representative equations, and more defined material properties as a function of specific feedstock used are necessary to determine a value that can be correlated to the printed ODS steel microstructure.

Keep this discovery

BibTeXRIS

deJong, Matthew, Horn, Timothy, Kaoumi, Djamel (ORCID:0000000170550444). 2025-10-20. A Review of the Influence of Processing Parameters on ODS Steels Produced via Additive Manufacturing Techniques. https://doi.org/10.1007/s11837-025-07777-2

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Influence of microstructure and temperature on impact toughness of H13 steel produced by binder jet additive manufacturing

Binder Jet Additive Manufacturing (BJAM) is a promising manufacturing pathway to produce H13 steel dies and tooling with complex geometries for applications in high pressure aluminum die casting, hot stamping, and injection molding. While fully dense H13 coupons produced using BJAM have been subjected to detailed microstructure characterization, properties which are critical and relevant to the aforementioned applications, such as impact toughness, have not been reported. Here, this work evaluated the influence of microstructural characteristics and test temperature on the impact toughness of H13 produced by BJAM. Coupons were produced from three different powder size distributions (PSDs), with nominal powder size ranges of −22 μm, 10-32 μm, and 15-53 μm. Coupons were printed, sintered, hot isostatically pressed (HIPed), and heat treated by quenching and tempering. After HIPing, the measured porosities of the different PSDs were all less than 0.015 vol%. The −22 μm PSD BJAM material exhibited the best impact toughness of all three PSDs across the entire test temperature range from 25 to 400 °C, and also exhibited an ambient temperature impact toughness of 10.9 J at a hardness of 46 HRC, equivalent to minimum threshold requirements for premium grade H13. However, all three BJAM PSDs exhibited moderately lower impact toughness than premium grade wrought H13 from RT to 400 °C. We attribute this in part due to the very large prior-austenite grain (PAG) sizes near 400 μm and segregation from former liquid channels leading to greater amounts of carbide precipitation on PAG boundaries. Technical pathways for optimizing processing and chemistry of BJAM H13 to further improve impact toughness are discussed.

Binder jet additive manufacturing

Microstructure-dependent particulate populations in ODS steels revealed by single-particle ICP-TOF-MS

In this work, we evaluated the ability of single-particle inductively coupled plasma time-of-flight mass spectrometry (SP-ICP-TOF-MS) to characterize particulates generated from 300 series stainless steels and oxide dispersion–strengthened (ODS) steels. Particulates were produced using two different rotary tools (cutting disk and grinding bit) to assess the influence of particle generation on effluent particulates. Across all materials and preparation techniques, SP-ICP-TOF-MS detected a substantial population of particles containing the expected constituent elements, with average compositions closely matching the nominal alloy values. A secondary population of Y-bearing particles was evident in ODS steels; their formation is strongly favored in particulates generated using the grinding bit. Specifically, in PM2000, Y-bearing particles were predominantly colocated with Al, whereas in 14YWT, Y-bearing particles were less frequently Fe-free but showed stronger colocation with Ti. These trends are consistent with the known microstructural differences between Y–Al–O oxide particles in PM2000 and finer Y–Ti–O nanoclusters in 14YWT. Together, these results demonstrate that SP-ICP-TOF-MS can resolve distinct particulate populations in complex, multicomponent steels at the femtogram mass scale, enabling particle-resolved insight into microstructure-driven phase separation and preparation-dependent particle generation.

Brubaker, Zach E. [Oak Ridge National Laboratory (

Influences of Introduced Yttrium Oxide Particles on Superalloy 718

Additive manufacturing has proven useful for introducing oxide particles into superalloys, to provide oxide dispersion strengthening (ODS) at high temperatures. This study screened how such an approach can influence microstructure and failure modes for superalloy 718. The objective of this study was to compare tensile and creep failure modes for additively manufactured superalloy 718 having introduced oxide particles. Fine yttrium-oxide (yttria) particles were introduced into 718 powder using two different powder mixing methods. Additive manufacturing by laser powder bed fusion was then used to prepare specimen blanks for each case, oriented parallel and transverse to the building direction. These were subsequently given consistent stress relief, hot isostatic pressurization, and final heat treatments, then subjected to tensile and creep tests at varied temperatures. Additively manufactured 718 without ODS (“no-ODS”) had nearly equiaxed grains at 50 μm in width. Roll-mixed ODS material had a bimodal grain size distribution, with fine grains at 9 μm and coarse grains at 66 μm in average width. The fine grains were elongated about 5x in the building direction. Acoustic-mixed ODS materials had grains at 10 μm in width that were elongated about 10x in the build direction. Compared to no-ODS, roll-mixed and acoustic mixed ODS materials did not show improved tensile strengths at room temperature, 760 °C, and 1093 °C. The tensile failure strains parallel to the building direction of roll-mixed ODS material were lowest in these tests. Flattened clumps of yttria had formed transverse to the building direction in roll-mixed material, which were easily cracked. Creep rupture response at 760 °C in the building direction was highest for acoustic-mixed material test. Creep tests at 1093 °C showed varied results, with low rupture lives associated with enhanced cavitation at grain boundaries and surface oxidation. Transverse to the building direction, all three materials had low failure strains in tests at 760 °C. The elongated grain boundaries failed readily in all transverse specimens tested at 760 °C and 1093 °C.

oxide dispersion strengthening