Molten fluoride salts, such as FLiBe (LiF-BeF2), are promising candidates for tritium breeding and heat transfer in fusion reactors, but corrosion of structural materials remains a major challenge. This study investigates the corrosion behavior of austenitic stainless steel 304H in purified and NiF2-containing FLiBe at 500°C and 600°C, focusing on the effects of impurities and redox control. Exposure to purified FLiBe resulted in the concurrent depletion of Cr, Mn, and Fe, with corrosion at 500 °C dominated by the combined oxide formation and elemental dissolution, while at 600°C elemental depletion was predominant. The addition of a controlled NiF2 impurity significantly accelerated corrosion at both temperatures, demonstrating the sensitivity of 304H to the salt redox state. Beryllium additions were effective in mitigating corrosion for both baseline and NiF2-containing FLiBe; minimal depletion of Cr, Mn, and Fe occurred with Be additions as low as 2.5 mg (147 wppm), and no NiBe intermetallics formed at 5 mg (294 wppm), indicating that small Be inventories can provide substantial protection without deleterious phase formation. Thermodynamic equilibrium and coupled thermodynamic-kinetic analyses at the salt-alloy interface suggested low corrosion rates in systems with limited hydrogen fluoride (HF) generation, highlighting the importance of salt redox control. Estimates for a Be addition rate were calculated for the HYLIFE-II fusion reactor that can mitigate corrosion-induced degradation, assuming complete conversion of tritium to tritium fluoride (TF). Overall, 304H shows reasonable compatibility with FLiBe under optimized redox conditions. These results provide quantitative guidance for material selection and salt management in fusion blanket and heat exchanger systems and motivate validation under flowing, nonisothermal, and irradiated conditions.
Pillai, Rishi [ORNL] (ORCID:0000000243688197)↗