Probing the fatigue enhancement in a thermally aged cast duplex stainless steel by in situ neutron diffraction

Yu, Dunji [ORNL] (ORCID:0000000189467851); Guo, Can [Tianjin University, China]; Fu, Sichao [ORNL] (ORCID:0009000846771640); Yu, Weiwei [Suzhou Nuclear Power Institute, China]; Chen, Yan [ORNL] (ORCID:0000000160951754); An, Ke [ORNL] (ORCID:000000026093429X); Chen, Xu [Tianjin University, China]

doi:10.1016/j.scriptamat.2024.116252

DOE OSTI · 3682580

Probing the fatigue enhancement in a thermally aged cast duplex stainless steel by in situ neutron diffraction

Yu, Dunji [ORNL] (ORCID:0000000189467851)·Guo, Can [Tianjin University, China]·Fu, Sichao [ORNL] (ORCID:0009000846771640)·Yu, Weiwei [Suzhou Nuclear Power Institute, China]·Chen, Yan [ORNL] (ORCID:0000000160951754)·An, Ke [ORNL] (ORCID:000000026093429X)·Chen, Xu [Tianjin University, China]

View original source ↗Read source document ↗Export metadata ↓

Abstract

After long-term thermal aging at 400 °C for 3000 h and 10,000 h, a cast duplex stainless steel exhibits promoted fatigue performance, including enhanced three-stage cyclic hardening and prolonged fatigue life. Utilizing in situ neutron diffraction, the phase-specific stresses are resolved, and their evolutions over entire fatigue cycling reveal the underlying mechanisms of the fatigue enhancement. It is found that the ferrite phase bears a much higher stress than the austenite matrix under both as-received and aged conditions. The enhanced cyclic hardening in Stage I is attributed to the strengthening of both phases due to thermal aging, while the enhancement in Stage III results from the martensitic transformation induced strengthening. The fatigue life is prolonged thanks to the cyclic hardening and the delay of martensitic transformation in the austenite phase after thermal aging.

Keep this discovery

BibTeX RIS

Yu, Dunji [ORNL] (ORCID:0000000189467851), Guo, Can [Tianjin University, China], Fu, Sichao [ORNL] (ORCID:0009000846771640), Yu, Weiwei [Suzhou Nuclear Power Institute, China], Chen, Yan [ORNL] (ORCID:0000000160951754), An, Ke [ORNL] (ORCID:000000026093429X), Chen, Xu [Tianjin University, China]. 2024-11-01. Probing the fatigue enhancement in a thermally aged cast duplex stainless steel by in situ neutron diffraction. https://doi.org/10.1016/j.scriptamat.2024.116252

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

A Compact Cryogenic Environment for In Situ Neutron Diffraction Under Mechanical Loading

Understanding the deformation mechanisms of materials at cryogenic temperatures is crucial for cryogenic engineering applications. In situ neutron diffraction is a powerful technique for probing such mechanisms under cryogenic conditions. In this study, we present the development of a compact cryogenic environment (CCE) designed to facil-itate in situ neutron diffraction experiments under mechanical loading at tempera-tures as low as 77 K. The CCE features a polystyrene foam cryogenic chamber, alumi-num blocks serving as neutron-transparent cold sinks, a liquid nitrogen dosing system for cryogen delivery, a nitrogen gas flow control system for thermal management, a process controller for temperature control, and a pair of thermally isolated grip adapt-ers for mechanical testing. The CCE achieves reliable temperature control with mini-mal neutron attenuation. Utilizing this setup, we conducted three in situ neutron dif-fraction tensile tests on a 316L stainless steel at 77 , 173 , and 298 K, respectively. The results highlight the pronounced effects of cryogenic temperatures on the material's deformation mechanisms, underscoring both the significance of cryogenic deformation studies and the effectiveness of the CCE.

Yu, Dunji [ORNL] (ORCID:0000000189467851)↗

DOE OSTI2018

Tracing Phase Transformation and Lattice Evolution in a TRIP Sheet Steel under High-Temperature Annealing by Real-Time In Situ Neutron Diffraction

Real-time in situ neutron diffraction was used to characterize the crystal structure evolution in a transformation-induced plasticity (TRIP) sheet steel during annealing up to 1000 °C and then cooling to 60 °C. Based on the results of full-pattern Rietveld refinement, critical temperature regions were determined in which the transformations of retained austenite to ferrite and ferrite to high-temperature austenite during heating and the transformation of austenite to ferrite during cooling occurred, respectively. The phase-specific lattice variation with temperature was further analyzed to comprehensively understand the role of carbon diffusion in accordance with phase transformation, which also shed light on the determination of internal stress in retained austenite. These results prove the technique of real-time in situ neutron diffraction as a powerful tool for heat treatment design of novel metallic materials.

Yu, Dunji [ORNL] (ORCID:0000000189467851)↗

DOE OSTI2026

Draft ASME Code Case to qualify L-PBF 316H material for Section III, Division 5 applications

This report documents the AMMT program’s development and submission of a draft ASME Code Case to qualify Laser Powder Bed Fusion (L PBF) Type 316H stainless steel for Section III, Divi-sion 5 Class A and SM high temperature nuclear applications. It summarizes the technical basis, the comprehensive high temperature mechanical test database assembled between 2023–2026, and the proposed code language and qualification framework submitted to ASME. The work was co-ordinated across multiple national laboratories and leverages prior ASME efforts to integrate additive manufacturing into the Boiler & Pressure Vessel Code. The body of the report describes the experimental database and analysis supporting the Code Case: tensile, creep, fatigue, creep fatigue, and thermal aging tests collected from multiple additive manufacturing sites, machine types, and powder lots, with material processed by a solution anneal heat treatment. The dataset — including both full size and subsized specimens and tests oriented parallel and perpendicular to build direction — shows limited tensile anisotropy, tensile properties comparable to wrought 316H, creep strength within the scatter of wrought material, but markedly reduced creep ductility above about 650 °C associated with rapid σ phase formation in L PBF microstructures. The draft Code Case itself prescribes a staged qualification model (manufacturing process qualification, component qualification, and per build witness testing), treats L PBF components as equivalent to Type 316 weld metal for design and inspection, and requires mechanical, chemical, and metallographic controls tied to ASTM/ISO 52946. Key acceptance criteria include tensile tests within a 90% prediction interval of the AMMT dataset, a creep fatigue screening test adapted from ASME Section III, Division 5, Subsection HB, HBB 2800 but with the cycle acceptance reduced to 100 for L PBF material, and double volumetric inspection of production components. The report concludes that the present data support treating L PBF 316H as analogous to conventional fusion weld metal for Division 5 design and inspection, while highlighting important caveats: the σ phase driven loss of creep ductility above ~650 °C, preliminary indications of enhanced creep fatigue sensitivity in some lots, and remaining gaps in long term aging and additional cyclic testing. Recommended next actions include completing outstanding cyclic and long duration creep/aging tests on the solution annealed condition, supporting inclusion of the 316H chemistry and heat treatment in ASTM/ISO 52946, and continuing engagement with ASME and NRC during balloting and review to enable industry adoption.