Physical thickness characterization of the FRIB production targets

Lee, D. J. [Michigan State University, East Lansing, MI (United States)]; Reaume, M. [Michigan State University, East Lansing, MI (United States)]; Franklin, W. [Michigan State University, East Lansing, MI (United States)]; Song, J. [Michigan State University, East Lansing, MI (United States)] (ORCID:0000000211630564)

doi:10.1088/1748-0221/21/07/t07005

DOE OSTI · 3580376

Physical thickness characterization of the FRIB production targets

Lee, D. J. [Michigan State University, East Lansing, MI (United States)]·Reaume, M. [Michigan State University, East Lansing, MI (United States)]·Franklin, W. [Michigan State University, East Lansing, MI (United States)]·Song, J. [Michigan State University, East Lansing, MI (United States)] (ORCID:0000000211630564)

View original source ↗Read source document ↗Export metadata ↓

Abstract

The FRIB heavy-ion accelerator, commissioned in 2022, is a leading facility for producing rare isotope beams (RIBs) and exploring nuclei beyond the limits of stability. These RIBs are produced via reactions between stable primary beams and a graphite target. Approximately 20–40% of the primary beam power is deposited in the target, requiring efficient thermal dissipation. Currently, FRIB operates with a primary beam power of up to 20 kW. To enhance thermal dissipation efficiency, a single-slice rotating graphite target with a diameter of approximately 30 cm is employed. The effective target region is a 1 cm-wide outer rim of the graphite disc. To achieve high RIB production rates, the areal thickness variation must be constrained within 2%. This paper presents physical thickness characterizations of FRIB production targets with various nominal thicknesses, measured using a custom-built non-contact thickness measurement apparatus.

Explore related subjects

Instrumentation for radioactive beams (fragmentation devices, fragment and isotope, separators incl. ISOL, isobar separators, ion and atom traps, weak-beam diagnostics, radioactive-beam ion sources)Targets (spallation source targets, radioisotope production, neutrino and muon sources)

Keep this discovery

BibTeX RIS

Lee, D. J. [Michigan State University, East Lansing, MI (United States)], Reaume, M. [Michigan State University, East Lansing, MI (United States)], Franklin, W. [Michigan State University, East Lansing, MI (United States)], Song, J. [Michigan State University, East Lansing, MI (United States)] (ORCID:0000000211630564). 2026-07-10. Physical thickness characterization of the FRIB production targets. https://doi.org/10.1088/1748-0221/21/07/t07005

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Targets (spallation source targets, radioisotope production, neutrino and muon sources) subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2026

Emissivity measurements of CuCrZr alloy

The Facility for Rare Isotope Beams (FRIB) heavy-ion accelerator, in user operation since 2022, produces rare isotope beams via interactions of high-intensity stable ion beams with a graphite production target. Approximately 20–40% of the primary beam power is deposited in the target, while the remaining 60–80% is absorbed by the beam dump. The minichannel beam dump (MCBD), currently operated at 20 kW and designed for operation up to 50 kW, uses CuCrZr alloy absorber plates. Thermal validation and thermal cycling tests of the MCBD were conducted at the Applied Research Laboratory (ARL) at Pennsylvania State University. Temperature measurements were obtained from an infrared (IR) camera. Since accurate temperature determination requires reliable emissivity values, the emissivity of CuCrZr was measured using the IR camera validated against thermocouple reference temperatures up to approximately 650 °C. The measurements were conducted under a vacuum level of approximately 10 -5 torr to minimize emissivity variations due to surface oxidation. The emissivity of CuCrZr was determined to be 0.057 ± 0.009 using a constant fit to the measured data over the surface temperature range from 100–650 °C.

Accelerator Subsystems and Technologies↗

DOE OSTI2026

Analysis of an irradiated uranium sample for source attribution without chemical separation using microplasma ionization and ultrahigh resolution mass spectrometry

The use of element isotope ratios has great potential in not only determining the reactor type used to produce plutonium (Pu) but also in determining the burnup and the time since irradiation. While a powerful nuclear forensic technique, determining element isotope ratios is complicated by severe isobaric interferences when performed on typical inductively coupled plasma mass spectrometers. Such analyses require extensive chemical separations prior to analysis to alleviate the inter-elemental isobars. Ultrahigh mass resolution spectrometry provides a potential alternative, greatly reducing the complexity of sample preparation and turnaround times for these critical measurements. To demonstrate the power of the approach, a sample of irradiated, depleted uranium was analyzed with the liquid sampling—atmospheric pressure glow discharge ion source coupled to an Orbitrap mass spectrometer. The Orbitrap is augmented with an external data acquisition system, Spectroswiss’s FTMS-Booster X2T, allowing collection of extended ion transients, providing higher mass resolution. In using this approach, the 150 Sm/ 149 Sm and 152 Sm/ 149 Sm isotope ratios were found to be within 20% of predicted values without any chemical separations and without mass bias corrections. In addition, the 240 Pu/ 239 Pu isotope ratio was determined, free from the 238 UH + interferences common to the ICP-MS platforms, while at the same time allowing for the determination of U isotopic signatures. While these demonstrative results are from a single sample, the advantages of the microplasma/ultrahigh mass resolution approach to intra-element isotope ratio determinations are clear.

Fuel burnup↗

DOE OSTI2023

Enhanced Optical Contrast and Switching in Near‐Infrared Electrochromic Devices by Optimizing Conjugated Polymer Oligo(Ethylene Glycol) Sidechain Content and Gel Electrolyte Composition

Abstract A detailed investigation addressing the effects of functionalizing conjugated polymers with oligo(ethylene glycol) (EG n ) sidechains on the performance and polymer‐electrolyte compatibility of electrochromic devices (ECDs) is reported. The electrochemistry for a series of donor‐acceptor copolymers having near‐infrared (NIR)‐optical absorption, where the donor fragment is 3,4‐ethylenedioxythiophene (EDOT) or an EG n functionalized bithiophene (g2T) and the acceptor fragment is diketopyrrolopyrrole (DPP) functionalized with branched alkyl or EG n sidechains, is extensively probed. ECDs are next fabricated and it is found that EG n sidechain incorporation must be finely balanced to promote polymer‐electrolyte compatibility and provide efficient ion exchange. Proper electrolyte‐cation pairing and polymer structural tuning affords a 2x increase in optical contrast (from 12% to 24%) and >60x reduction in switching time (from 20 to 0.3 s). Atomic force microscopy (AFM)/grazing incidence wide‐angle X‐ray scattering (GIWAXS) characterization of the polymer film morphology/microstructure reveals that an over‐abundance of EG n sidechains generates large polymer crystallites, which can suppress ion exchange. Lastly, time‐of‐flight secondary ion mass spectrometry (ToF‐SIMS) indicates sidechain/electrolyte identity does not influence the electrolyte penetration depth into the films, and EG n sidechain inclusion increases electrolyte cation uptake. The material structural design insight and guidelines regarding the polymer‐electrolyte ion insertion/expulsion dynamics reported here should be of significant utility for developing next‐generation mixed ionic‐electronic conducting materials.

Chemistry↗