Hydrogen diffusion induced dislocation transformations in a nickel superalloy

Abstract

The diffusion of hydrogen in metals and alloys induces embrittlement that can adversely affect the structural properties. We examine the adsorption and diffusion of hydrogen in Inconel-718 (IN-718), and scrutinize the ensuing effects on the dislocation behavior in the alloy to elucidate the fundamental mechanisms of hydrogen-microstructure interactions from classical molecular simulations. Hydrogen adsorption increases with time until the surface saturates, while hydrogen diffusion exhibits strong temperature dependence, with diffusion coefficients converging above 1300 K regardless of the initial hydrogen concentration in the alloy. The diffusion in IN-718 is significantly sluggish than in pure Ni, Fe, or Cr, and is strongly impacted by hydrogen concentrations, resulting in an order of magnitude higher diffusion coefficient for hydrogen (10-14 m2/s relative to 10-15 m2/s) at high concentrations, especially below 600 K. Hydrogen diffusion coefficient varies from 10-12 to 10-15 m2/s in IN-718 depending on temperature (500–1400 K). More critically, our results reveal that increasing hydrogen concentration induces microstructural changes in the alloy, transforming perfect dislocations into stair-rods and Shockley partials, with higher temperatures favoring the latter. The results are significant for hydrogen fuel applications to gain insights into the materials chemistry for designing safer and more efficient propulsion systems, particularly in high-performance environments related to controlled hydrogen combustion applications.

Keep this discovery

BibTeXRIS

Banerjee, Tanumoy, Balasubramanian, Ganesh. 2025-03-01. Hydrogen diffusion induced dislocation transformations in a nickel superalloy. https://doi.org/10.1016/j.fuel.2024.134064

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Microstructural Evolution and Mechanical Properties of LP-DED NASA HR-1 – A Hydrogen Resistant AM Superalloy for Space Propulsion Applications

The National Aeronautics and Space Administration (NASA) has actively pursued metal additive manufacturing (AM) technologies for spaceflight applications since the late 2000s. AM offers transformative advantages in cost, schedule, part consolidation, and design flexibility. Among the various AM techniques, laser powder directed energy deposition (LP-DED) is particularly well suited for fabricating complex geometries with fine feature resolution. In propulsion systems that utilize high-pressure gaseous hydrogen—such as liquid hydrogen rocket engines—hydrogen environment embrittlement (HEE) presents a serious threat to material performance 1,2 . Mechanical property degradation under these conditions can compromise component reliability, especially under cyclic loading. To address this challenge, NASA developed NASA HR-1 (Hydrogen Resistant-1) as a solution for liquid rocket engine components operating in hydrogen-rich environments, using the LP-DED technique 3-9 . A key component in a liquid rocket engine is the exhaust nozzle, which is typically regeneratively cooled (regen) due to the high heat flux. NASA HR-1 was specifically developed for regen nozzle applications using hydrogen as a propellant, providing resistance to HEE, a critical issue for many materials. The AM version of NASA HR-1 was also formulated to achieve high ultimate tensile strength, along with high yield strength and ductility in this environment 5,6 . Low-cycle fatigue (LCF) is another important consideration in nozzle design, as components are expected to endure multiple starts and missions. Additionally, the LP-DED version of the alloy exhibits improved thermal conductivity compared to its wrought counterpart, which benefits nozzle cooling. Overall, NASA HR-1 offers an excellent balance of high strength, HEE resistance, LCF performance, thermal conductivity, and ductility to meet the demanding requirements of channel-cooled nozzles and other components used with hydrogen and other propellants. The LP-DED–processed NASA HR-1 requires several post-processing heat treatment steps to achieve the material properties desirable for its intended application 6 . These steps include stress relief, homogenization, solution annealing, and aging for precipitation hardening. The stress relief treatment mitigates residual stresses accumulated during the LP-DED process and minimizes the potential for distortion. Homogenization, a common step for AM materials, reduces elemental segregation and promotes recrystallization to develop a more equiaxed grain structure. The subsequent solution annealing treatment heats the part to a solid solution temperature to dissolve the undesirable η-phase that forms during cooling from homogenization, followed by rapid cooling to retain an η-phase–free microstructure. Finally, aging promotes precipitation of the strengthening γ′ phase in the alloy. The integration of compositional design and optimized thermal processing enables high-quality LP-DED NASA HR-1 components with excellent microstructural and mechanical stability. Improved chemical and microstructure homogeneity enhances ductility and fatigue resistance—both critical for safe and reliable operation in high-pressure hydrogen environments. NASA has successfully fabricated and hot-fire tested multiple subscale and full-scale channel wall nozzles using LP-DED NASA HR-1 5,6, 9-14 . These efforts included process refinements to support thin-wall construction and various channel geometries. Throughout development, several key observations emerged. After homogenization, the as-built columnar grain structure transforms into a fully equiaxed microstructure. However, subsequent treatments—such as solution annealing and aging—result in changes that are more difficult to track. The grain structure remains largely unchanged, and the γ′ precipitates, typically 5–10 nm in diameter, are beyond the resolution of scanning electron microscopy (SEM). While transmission electron microscopy (TEM) can resolve these fine precipitates, TEM sample preparation is time-consuming and difficult for LP-DED material. As an alternative, differential scanning calorimetry (DSC) offers a useful, qualitative approach to monitor precipitate evolution throughout different stages of heat treatment. The overall goal is to improve the understanding of how heat treatment affects the microstructure and mechanical performance of LP-DED NASA HR-1. This paper presents heat treatment design considerations, microstructural characterization, mechanical testing – including tensile and LCF testing in both air and hydrogen environments.

Superalloy

Unlocking superplasticity in medium and high-entropy alloys

Superplasticity, the capacity of materials to sustain extraordinary tensile elongations at elevated temperatures, underpins a range of advanced metal-forming technologies. Conventionally, it is achieved in fine-grained alloys where deformation is dominated by grain-boundary sliding, accommodated by diffusion and dislocation activity. The advent of medium- and high-entropy alloys (M/HEAs), with their high chemical complexity and unconventional phase stability, offers new pathways to superplastic behavior beyond traditional alloy systems. Although investigated only recently, several M/HEAs already exhibit elongations that rival or exceed those of classical superplastic materials, particularly when ultrafine or metastable microstructures are engineered. Here, we review progress in understanding superplastic deformation in M/HEAs, emphasizing the interplay among composition, initial microstructure, thermomechanical processing, and microstructural evolution during high-temperature deformation. We discuss approaches to generating the fine-grained structures necessary for grain-boundary sliding, including severe plastic deformation and tailored heat treatments. We further highlight dynamic phenomena such as phase transformations, evolving grain-boundary chemistry, and deformation-induced grain refinement that can enhance plasticity in these systems. These mechanisms often shift the balance of deformation processes, enabling large elongations even outside classical criteria. Finally, we outline key challenges for application, including cost, scalability, recyclability, and microstructural stability.

klenam, Desmond [University of the Witwatersrand,

A transport-based framework for solidification cracking in Ni-based superalloys processed by laser powder bed fusion

Solidification cracking remains a persistent barrier to laser powder bed fusion (LPBF) processing of solid-solution-strengthened (SSS) Ni-based superalloys and is commonly attributed to carbide formation, liquation-type failure, or elemental segregation. In this work, the cracking behavior of three SSS Ni-based superalloys—Inconel 625 (625), Inconel 617 (617), and Haynes 230 (230)—is examined under comparable LPBF conditions to evaluate the origins of their cracking susceptibility. Carbides were present in both 625 and 230, yet cracking behavior differed significantly. MC-type carbides in 625 remain discrete and preserve liquid connectivity, whereas Cr-rich M23C6 carbides in 230 form at cellular triple junctions that bottleneck the interdendritic liquid network, influencing cracking through liquid connectivity rather than as an independent cause. Alloy 617 exhibited anomalous segregation without resolvable secondary phases yet cracked mildly, indicating that extensive carbide formation is not a prerequisite for cracking. To rationalize these observations, a transport-limited framework is proposed in which cracking occurs when terminal-liquid feeding cannot accommodate solidification-induced strain; among the mechanisms evaluated, this framework is most consistent with the physical constraints imposed by LPBF solidification. Transport-based crack-susceptibility indexes incorporating permeability, viscosity, and solidification kinetics distinguish the alloy hierarchy; permeability ratios Krat increased from approximately 7 (625) to 11.5 (617) and 14.5 (230), with corresponding increases in the μ-weighted mushy zone risk index (CSIMZRM). These results are consistent with transport-limited liquid feeding as a rate-limiting contributor to solidification cracking in LPBF-processed SSS Ni-based superalloys, providing a physically grounded basis for alloy and process design.

Hyer, Holden [ORNL] (ORCID:0000000343915561)