Radiation damage in tungsten under high-energy He-ion irradiation

Abstract

Tungsten (W) is a primary candidate for plasma-facing components (PFCs) in fusion reactors and hybrid fission-fusion reactors. However, W suffers from severe microstructural damage under Helium (He) ion irradiation in operation conditions. Key irradiation parameters, including incident ion energy, fluence, and irradiation temperature, are known to determine the formation of He bubbles and dislocation loops, which ultimately lead to the degradation of mechanical properties, such as radiation hardening and ductile-to-brittle transition temperature (DBTT) shifts. Various strategies, for instance, interface engineering and alloying, have been developed to enhance He irradiation tolerance in W to address these challenges. Studies in the recent two decades have enhanced the understanding of the underlying mechanisms that drive defect evolution and mechanical performance degradation, thereby offering more insights into the design of more resilient W-based materials for extreme environments.