Structural uniformity and compositional homogeneity of solid-phase alloyed rod

Abstract

Solid-phase processes have emerged as an alternative to fusion-based alloying to avoid coarse microstructures, undesirable phase formation, and high energy consumption. However, achieving uniform distribution of alloying elements during friction-based processing remains challenging due to highly heterogeneous thermomechanical conditions. This work evaluates the structural uniformity and compositional homogeneity of Al–Cu–Zn alloyed rods produced by friction extrusion (FE) and establishes the role of the rotational speed to feed rate ratio (N/V) on alloying effectiveness. A systematic matrix of FE experiments was conducted at constant extrusion ratio with N/V values ranging from 3.7 to 300. Compositional uniformity was assessed along the rod length (ICP-OES), in three dimensions (X-ray computed tomography), and at the microscale (SEM–EDS), supported by a gray-level co-occurrence matrix (GLCM)–based homogeneity metric. Smoothed particle hydrodynamics (SPH) simulations were used to reveal material flow and thermomechanical fields. Results show that N/V = 100 produces a high-shear mixing zone that eliminates the unmixed core and enables near-full dissolution and dispersion of Cu and Zn. At lower N/V, a laminar flow region persists at the rod center, causing segregation and large composition gradients. The combined experimental–computational analysis provides mechanistic insight into the transition from fragmented particle dispersion to thermomechanically assisted metallurgical mixing. This study establishes processing–structure relationships for solid-phase alloying and provides guidance for achieving homogenized compositions comparable to wrought alloys via rapid, scalable FE processing.