Studying Perovskite Solar Cells in Reverse Bias to Accelerate and Investigate Degradation Due to Electrochemistry and Halogen Migration

McGehee, Michael D [University of Colorado] (ORCID:0000000196099030)
View original source ↗Read source document ↗Export metadata ↓

Abstract

This project improved the understanding of how electrochemical reactions cause degradation when perovskite solar cells are operated in reversed bias. Atomic layer deposition of

Explore related subjects

14 SOLAR ENERGYPerovskite Solar Cell

Keep this discovery

BibTeXRIS

McGehee, Michael D [University of Colorado] (ORCID:0000000196099030). 2026-05-11. Studying Perovskite Solar Cells in Reverse Bias to Accelerate and Investigate Degradation Due to Electrochemistry and Halogen Migration. https://doi.org/10.2172/3408470

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

14 SOLAR ENERGY subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2026

Semi-Transparent Perovskite Solar Cells in a Stacked Tandem Module: Cooperative Research and Development Final Report, CRADA Number CRD-19-00810

This project seeks to develop device design, materials composition, and processing tools and parameters to fabricate semi-transparent perovskite solar cells and modules for application in stand-alone products or added to other solar cells in a mechanically stacked tandem configuration. This technology presents significant advanced manufacturing challenges and opportunities in getting to scale, including development of perovskite inks, scalable perovskite and heterojunction deposition and annealing processes, heterojunction composition, transparent electrode composition and deposition process, anti-reflection layer composition and deposition process, and cell to module integration processes. Modification 5: The proposed project seeks to develop device design, materials composition, and processing tools and parameters to fabricate semi-transparent perovskite solar cells and modules for application in stand-alone products or added to other solar cells in a mechanically-stacked tandem configuration. This technology presents significant advanced manufacturing challenges and opportunities in getting to scale, including development of perovskite inks, scalable perovskite and heterojunction deposition and annealing processes, heterojunction composition, transparent electrode composition and deposition process, passivation layers including in module scribes, anti-reflection layer composition and deposition process, and cell to module integration processes. Advanced metrology and characterization will be performed on perovskite films, cells and module. Furthermore, we will examine module or materials recycling for circular economy considerations. Modifcation 6: Gigahertz frequency microwave pump-probe spectroscopies are highly sensitive to thin film semiconductor photoconductivity of individual and stacks of layers that comprise perovskite solar cells. As such, these techniques will be used to qualify reproducibility and quality correlations during the manufacturing process. Modification 7: Mechanical adhesion of top contacts within perovskite modules significantly impacts the durability of the module when exposed to accelerated degradation testing. The adhesion between the perovskite/transport layer interface and the transport layer/top contact interface are both very sensitive small changes in processing. ALD processing conditions of the transport layer will be tuned to optimize the mechanical adhesion within the perovskite module stack.

14 SOLAR ENERGY↗
DOE OSTI2026

Self-Leveling Inks for Printing Ultra-uniform Perovskite Solar Modules by Flexography

The report describes the development of scalable manufacturing methods for high-performance, stable perovskite solar modules using flexographic printing. The project developed self-leveling perovskite inks that exploit Marangoni flows to reduce coating defects and improve large-area film uniformity. Bayesian optimization was integrated with high-throughput photoluminescence mapping and photovoltaic measurements to efficiently optimize ink formulations and printing conditions. The resulting printed perovskite solar cells achieved champion power conversion efficiencies above 21.6%, with median efficiencies exceeding 20% across large device batches. At the module scale, printed devices achieved active-area efficiencies up to approximately 17.3% on 25 cm² substrates. The project also demonstrated improved performance and stability using additively patterned interconnections compared with laser-scribed controls. Overall, the work establishes a data-driven, roll-compatible pathway toward high-throughput, low-capital-cost manufacturing of uniform and stable perovskite photovoltaics.

14 SOLAR ENERGY↗
DOE OSTI2024

Additive‐Free Oxidized Spiro‐MeOTAD Hole Transport Layer Significantly Improves Thermal Solar Cell Stability

Perovskite solar cells are among the most promising new solar technologies, already surpassing polycrystalline silicon solar cell efficiencies. The stability of the highest efficiency devices at elevated temperature is, however, poor. These cells typically use Spiro-MeOTAD as the hole transporting layer. It is generally believed that additives, required for enhancing electrical conductivity and optimizing energy level alignment, are responsible for the reduced stability—inferring that Spiro-MeOTAD based hole transporting layers are intrinsically unstable. Here, a reliable noble metal free synthesis of Spiro-MeOTAD (bis(trifluoromethane)sulfonimide) 4 is presented which is used as the oxidizing agent. No additives are added to the partially oxidized Spiro-MeOTAD hole-transporting layer. Device efficiencies up to 24.2% are achieved. Electrical conductivity is largely developed by the first 1% oxidation. Further oxidation shifts the energy levels away from the vacuum level, which allows tuning of the energy level alignment without the use of additives—contradicting the current understanding of this system. Without additives, devices demonstrate significant improvement in stability at elevated temperatures up to 85 °C under one sun over 1400 h continuous illumination. The remaining degradation is pinpointed to ion migration and reactions in the perovskite layer which may be further suppressed with compositional engineering and adequate ion barrier layers.

14 SOLAR ENERGY↗