NOx mediated formation of ε – UO 3 during thermal decomposition of uranyl nitrate hexahydrate under static air conditions

Abstract

The thermal decomposition of uranyl nitrate hexahydrate in air at temperatures of 650 – 800 °C is expected to yield α – U 3 O 8 through intermediate UO 3 phases. Here, n this study, Raman spectroscopy complimented by powder X-ray diffraction revealed the unexpected formation of ε – UO 3 as an accompanying phase during thermal decomposition of UNH at 700 °C under static air conditions. Experiments demonstrated that ε – UO 3 does not form during the initial ramp up stage nor during the high temperature heating period; but instead forms during the cooling stage between 250 – 400 °C. Additional experiments revealed that UNH initially decomposes through an amorphous UO 3 intermediate prior to α – U 3 O 8 formation. Attempts to bypass the U 3 O 8 precursor in the formation of ε – UO 3 were unsuccessful, supporting the necessity of U 3 O 8 (α – U 3 O 8 in this study) in the formation of ε – UO 3 . The observed phase evolution is proposed to result from the NOx species generated during UNH thermal decomposition, which create localized oxidizing conditions within the furnace under static air conditions. Furthermore, a predominantly phase pure ε – UO 3 was synthesized under static air conditions through the addition of an extra plateau at 250 °C during the cooling step. These findings demonstrate the importance of gas-phase chemistry and cooling conditions in uranium oxide phase evolution and provide additional insight into ε – UO 3 formation pathways.