Laser-heated diamond anvil cell synthesis and recovery of metastable MnSb 2 and YbZn 2 for post-synthesis transport studies

Abstract

The creation and exploration of new materials under extreme pressure–temperature conditions has become increasingly reliant on laser-heated diamond anvil cell (LHDAC) techniques, which provide direct access to previously unexplored regions of multinary phase diagrams. Whereas numerous high-pressure phases have been identified in situ, systematic recovery and post-synthesis physical property characterization of these materials remain significant challenges. In this work, we describe the setup and implementation of an LHDAC-based synthesis and recovery workflow and demonstrate its application to metastable MnSb 2 and YbZn 2 phases. Synchrotron x-ray diffraction and spatial mapping confirm dominant formation of the targeted phases, whereas laboratory-based refinement quantifies phase fractions despite intrinsic microstrain and minor secondary phases. High-pressure transport measurements on recovered samples reveal pressure-tunable electronic instabilities in both systems. In MnSb 2 , pressure suppresses two high-temperature magnetic ordering anomalies, observed in transport, by ∼5 GPa and, for higher pressures, induces a new low-temperature feature that increases with further pressure increase. In hexagonal high-pressure YbZn 2 , an electronic reconstruction emerges at ∼11 GPa, characterized by semiconducting-like behavior from ∼30 to 300 K and a broad low-temperature coherence crossover near 30 K. Our results establish LHDAC synthesis not only as a structural discovery tool but also as an experimental platform for investigating correlated quantum states stabilized far from equilibrium thermodynamic conditions.