DOE OSTI · 3388191

Effect of Oxidizing Impurities on the Corrosion Behavior of Structural Alloys Exposed to MgCl 2 Molten Salt Vapor

Pennell, Samuel [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000315966206)·Pokharel, Kritee [National Laboratory of the Rockies (NLR), Golden, CO (United States)]·Foster, Kyle [National Laboratory of the Rockies (NLR), Golden, CO (United States)]·Vidal, Judith [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000205913250)·Rippy, Kerry [National Laboratory of the Rockies (NLR), Golden, CO (United States)]
View original source ↗Read source document ↗Export metadata ↓

Abstract

The corrosion behavior of structural alloys SS304 and IN617 when exposed to vapors of MgCl 2 molten salt at 764 °C for 100 h in an argon atmosphere was investigated as a function of the level of oxidizing impurities (e.g., NaOH) present in the salt. Increasing the concentration of oxidizing impurities in the salt caused an increase in corrosion in both structural alloys, as measured by Cr depletion layers. A poorly adhered oxide scale layer containing Mg, Al, and Cr was observed on the surface of the metals, and local attack was observed as well. The Ni-based IN617 showed lower Cr depletion and less scale formation than the Fe-based SS304. These results demonstrate that oxidizing impurities in the molten salt will impact the vapor phase corrosion for structural members exposed to the molten salt headspace. This finding is highly relevant for understanding the effects of the vapor phase in molten salt applications, including molten salt thermal energy storage, molten salt nuclear reactors, and molten salt electrochemistry.

Explore related subjects

25 ENERGY STORAGE36 MATERIALS SCIENCEcorrosionmetallurgymolten saltsthermal energy storage

Keep this discovery

BibTeXRIS

Pennell, Samuel [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000315966206), Pokharel, Kritee [National Laboratory of the Rockies (NLR), Golden, CO (United States)], Foster, Kyle [National Laboratory of the Rockies (NLR), Golden, CO (United States)], Vidal, Judith [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000205913250), Rippy, Kerry [National Laboratory of the Rockies (NLR), Golden, CO (United States)]. 2026-07-06. Effect of Oxidizing Impurities on the Corrosion Behavior of Structural Alloys Exposed to MgCl 2 Molten Salt Vapor. https://doi.org/10.1007/s11085-026-10433-y

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

25 ENERGY STORAGE subject36 MATERIALS SCIENCE subjectCORROSION subjectThermal energy storage subjectmetallurgy subjectmolten salts subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2026

Atomistic Mechanisms of Stress-Dependent Molten Salt Corrosion in NiCr Alloys

Ni-based structural alloys in molten salt environments often experience simultaneous mechanical loading and corrosive attack, yet the mechanisms governing stress-corrosion interactions remain unclear. Prior studies largely emphasize tensile stress, while the role of compressive stress has received limited attention. Here, reactive molecular dynamics simulations are used to investigate the coupled effects of applied strain and corrosion in Ni 0.75 Cr 0.25 exposed to molten FLiNaK at 800 °C. A Σ5(210) grain boundary model is subjected to tensile (+4%) to compressive (−4%) uniaxial strains, and corrosion behavior is evaluated through fluorine adsorption, charge redistribution, and grain boundary evolution. Tensile strain accelerates intergranular corrosion susceptibility by reducing local atomic packing through elastic dilation and increasing excess free volume at the grain boundary, which enhances atomic mobility and salt infiltration. In contrast, compressive strain can suppress corrosion by promoting the formation of a ridge-like surface layer along the grain boundary, limiting salt access to the underlying alloy. These results provide atomistic insight into how stress states influence grain boundary corrosion in molten salts.

36 - MATERIALS SCIENCE↗
DOE OSTI2026

Final Technical Report: Transport of Complex Mixtures in Ion-Containing Polymer Membranes

Permselective ion-containing membranes are an integral component for many applications from water treatment, fuel cells, and solar fuels devices where the selective transport of molecules and ions is desired. In solar fuels devices, ion-containing polymer membranes are responsible for permitting selective transport of ions between electrodes to maintain overall charge neutrality yet limit transport of reaction products produced at the electrodes. While the transport of single solutes through such membranes has been fairly well described, binary and multicomponent transport is poorly understood due to the myriad of interactions that occur in these systems (i.e. between co-permeants and between permeants and the membrane). Solar fuels devices are just one example of an application where understanding the transport of multiple simultaneous species is critically important to improving device performance as product crossover leads to reductions in overall device performance. The objectives of this research was to improve our understanding of the complex array of factors that influence transport behavior of multiple solutes within ion-containing polymer membranes. This experimental project addressed the lack of fundamental understanding of multicomponent transport behavior by synthesizing ion exchange membranes with varied incorporation of comonomers (ionic and neutral moieties) to investigate fundamental relationships between membrane structure, membrane physiochemical properties, and transport behavior of solutes and complex solute mixtures through dense, hydrated membranes.

25 ENERGY STORAGE↗
DOE OSTI2026

Mechanical and durability properties of ultra-high-performance concrete of spent nuclear fuel dry storage systems: a review

Dry storage systems are used for interim storage of spent nuclear fuel (SNF). However, with the growing need to extend the operational periods of these systems, there are concerns about the degradation of their concrete overpacks, which could compromise the system's structural integrity and safety during hazardous events. Traditional concrete mixtures used in SNF dry storage systems have remained largely unchanged since their inception and often use conventional ingredients. These materials are susceptible to degradation mechanisms such as chemical attacks, alkali-silica reactions (ASR), and freeze–thaw cycles, which can lead to a loss of strength and durability over time. To address these challenges, this paper reviews the application of ultra-high-performance concrete (UHPC) as a promising alternative for spent nuclear fuel dry storage system overpacks. UHPC offers superior mechanical properties, exceptional durability, and reduced susceptibility to degradation mechanisms compared to conventional concrete. This paper focuses on the role of supplementary cementitious materials (SCMs) such as silica fume, fly ash, and metakaolin in enhancing UHPC performance for SNF storage applications. These SCMs have been shown to significantly improve the material’s microstructure, strength, and resistance to environmental stressors typically encountered in SNF storage environments. Moreover, incorporating SCMs supports sustainable construction by reducing cement consumption and associated carbon emissions. The review brings together existing research and experimental data, providing insights for engineers and researchers on developing UHPC mixtures that meet the rigorous demands of spent nuclear fuel dry storage systems, extending their service life and minimizing inspection intervals.

36 - MATERIALS SCIENCE↗