Screening and qualification methodology for SiC end plug processing methods

Abstract

Deployment of SiC-ceramic-based fuel cladding for light water reactors requires a hermetic end plug–to–cladding joint that can withstand neutron irradiation during normal operation and maintain integrity during design-basis accidents. Reactor experiments have shown that some SiC composite tubes with SiC end plugs can retain hermeticity after irradiation. However, achieving consistent joint performance under irradiation remains a key challenge. Resolving this issue is essential to enable integral irradiation testing and to demonstrate fuel integrity under commercial-reactor irradiation conditions. This report aims to: (1) provide guidance for designing radiation-tolerant end plug joints for SiC cladding; (2) demonstrate experimental methods to detect processing defects that are unstable under neutron irradiation at light-water-reactor-relevant temperatures and doses; and (3) outline a step-by-step approach for designing and conducting reactor experiments to screen joining methods. The resulting data will be used to improve joint processing and to define critical defect types and sizes that must be detected and eliminated through non-destructive evaluation for quality assurance. Based on prior irradiation experiments at the High Flux Isotope Reactor, differential swelling among the cladding, bonding layer, and end plug was identified as an underlying mechanism for irradiation-induced joint degradation. Accordingly, this effect must be considered in the design of radiation-tolerant joining techniques. In this work, miniature SiC end plug joint specimens irradiated during the previous project were analyzed using X-ray computed tomography to characterize the joint microstructure. Digital volume correlation of the tomography data quantified radiation-induced microstructural changes and enabled evaluation of defect-related risks. Finally, ongoing neutron irradiation efforts using larger specimen volumes are presented. These efforts aim to statistically assess joint performance and to build a microstructure–performance (e.g., leak-tightness) dataset to inform processing improvements and quality control.