Microstructure & Mechanical Properties of Scaled Thermally Aged LPBF 316H SS Builds

Abstract

As part of the US Department of Energy’s Advanced Materials and Manufacturing Technologies program’s mission to accelerate qualification of advanced manufacturing pathways for nuclear applications, laser powder bed fusion (LPBF) 316H stainless steel (SS) has been selected as a model system to develop a rapid code case framework. This effort directly addresses the grand challenges of (1)expanding the limited portfolio of materials currently codified for elevated-temperature nuclear structural service under Section III, Division 5of the American Society of Mechanical Engineers’ Boiler and Pressure Vessel Code; and (2) significantly reducing qualification timelines that traditionally exceed a decade. The strategic importance of LPBF 316H lies in its immediate industrial relevance, existing data foundation from wrought 316H, and alignment with ongoing code case development for LPBF 316L.Prior work revealed accelerated precipitation of deleterious secondary phases and reduced creep ductility in as-printed LPBF 316H. Building on that prior research, FY2025activities focused on establishing an understanding of the key failure mechanisms of crept 316H specimens to aid in code case development and on evaluating stress relief (SR) parameters on the high-temperature performance and thermal aging-induced degradation of tensile and fracture behavior in LPBF316H.