Density-functional theory- based calculations that complement our series of experimental efforts on optimizing Ag electrocatalyst performance for CO2 to CO conversion were presented. Three key findings are drawn out from the combined UHV surface science, STM and electrochemical measurements: (1) Using a series of Ag nanoparticles with 2-6 nm average diameters, CO2 reduction reaction (CO2RR) activity increases, with particle between 2 nm and ∼4 nm demonstrating the highest combination of activity and selectivity; (2) Electronic metal−support interactions (EMSIs) between Ag and C dramatically improve CO2RR performance as evidenced by a scaling relationship between particle size and the relative Ag−C EMSIs strength, which improves the CO2-to-CO Faradaic efficiency of sub-2 nm Ag particles from 2 to ∼100% and increases the CO turnover frequency ∼15-fold compared with similarly sized bare Ag particles; (3) The performance Ag electrocatalysts is improved when supported on S-doped C materials. Computational modeling of 1−10 nm Ag particles predicts a nearly identical size-dependent trend with maximum CO2RR activity predicted for 3.7nm particles. The calculations support the promotional effect of C materials, showing a large charge transfer of 1.02 e from Ag clusters to defective C and a 0.41 eV less endergonic step of forming COOH intermediate on Ag/defective-C compared to the Ag/C system. Calculations indicate a more favorable energetic pathway of CO2-to-CO at the C-S-Ag interface, consistent with experiments.