The Electron Thermal Conductivity of Pu and Zr Substituted $\mathcal{γ}$-U

Abstract

Uranium alloys are attractive recycled nuclear fuels because of their high thermal conductivity (𝑘) and fissile density. Limited experimental studies of the 𝑘 of U-Pu-Zr alloys in the range of 15 to 20 wt% Pu and 6 to 15 wt% Zr indicate that increasing the content of either Zr or Pu tends to lower 𝑘. However, which element has the greater effect on 𝑘, and the associated mechanisms, remains unclear. Here, in this study, the electron thermal conductivity (𝑘 𝑒 ) of U-Pu-Zr compositions are calculated using density functional theory. The electronic structure is evaluated to understand the effects of plutonium (Pu) and zirconium (Zr) substitution on the 𝑘 𝑒 of 𝛾-U. Alloys of up to 37.5 at. % Pu and 37.5 at. % Zr are examined. Two methods are applied to calculate 𝑘 𝑒 ; we find that the accuracy of each method depends on the electronic and mass similarities between the solute and solvent atoms. Specifically, when the solute atom is similar in electronic structure and mass, the more accurate method is that which employs the electron relaxation time of 𝛾-U, while if the elements are dissimilar, a mixed method that mixes several parameters associated with JNW_S⁢3033426825100132 from each element in the alloy is best. The introduction of all alloying elements decreases 𝑘 𝑒 ; however, in binary compounds, Pu and Zr have different effects. Pu flattens the electronic bands but compensates for this deleterious effect by increasing electron density near the Fermi level. Zr flattens the electronic bands more severely without adding electron density near the Fermi level. Therefore, Zr decreases 𝑘 𝑒 more than Pu in binary compounds. In ternary compounds, the difference between Pu and Zr is minimal due to the phononic change from the large mass change of Zr substitution, even at 12.5 at. %. Thus, we predict that higher loadings of Pu, and potentially other actinides, can be added to U-Pu-Zr compositions for faster recycling of spent fuel without sacrificing 𝑘. We also note that these 𝑘 𝑒 calculation methods can be applied to non-fuel alloys that require 𝑘 𝑒 predictions, such as cladding, heat exchanger, and structural materials.