Wafer-Scale MgB 2 Superconducting Devices

Abstract

Progress in superconducting device and detector technologies over the past decade has realized practical applications in quantum computers, detectors for far-infrared telescopes, and optical communications. Superconducting thin-film materials, however, have remained largely unchanged, with aluminum still being the material of choice for superconducting qubits and niobium compounds for high-frequency/high kinetic inductance devices. Magnesium diboride (MgB 2 ), known for its highest transition temperature (T c = 39 K) among metallic superconductors, is a viable material for elevated temperature and higher frequency superconducting devices moving toward THz frequencies. However, difficulty in synthesizing wafer-scale thin films has prevented implementation of MgB 2 devices into the application base of superconducting electronics. Here, we report ultrasmooth (<0.5 nm root-mean-square roughness) and uniform MgB 2 thin (<100 nm) films over 100 mm in diameter and present prototype devices fabricated with these films demonstrating key superconducting properties including an internal quality factor over 10 4 at 4.5 K and high tunable kinetic inductance in the order of tens of pH/sq in a 40 nm thick film. This advancement will enable development of elevated temperature, high-frequency superconducting quantum circuits, and devices.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Kim, Changsub, Bell, Christina, Evans, Jake M., Greenfield, Jonathan, Batson, Emma, Berggren, Karl K., Lewis, Nathan S., Cunnane, Daniel P.. 2024-09-24. Wafer-Scale MgB 2 Superconducting Devices. https://doi.org/10.1021/acsnano.4c11001

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Simultaneous ELM suppression and divertor detachment via synergistic boron powder and neon injection in EAST

A novel approach for simultaneous power exhaust and edge-localized mode (ELM) control is presented in the Experimental Advanced Superconducting Tokamak discharges, which utilize an ITER-like tungsten divertor. Real-time injection of boron (B) powder and neon (Ne) gas overcomes their limitations encountered when used separately. Pure Ne seeding leads to a narrow operational window constrained by core impurity accumulation and H-mode to L-mode back transitions, while pure solid B injection (SBI) is insufficient for effective divertor cooling. In comparison, their combined use achieves a stable, stationary, ELM-suppressed H-mode with adequate power exhaust. This synergistic scenario features partial energy detachment at the outer divertor while maintaining good plasma confinement (H 98 ∼ 1) with minimal degradation. Two key features of this scenario are: (1) the SBI triggers a persistent Edge Harmonic Mode (EHM), which provides a crucial continuous particle transport channel, preventing Ne and tungsten/molybdenum accumulation without flushing out by ELM, and (2) the B + Ne mixture allows for active optimization of the radiated power profile. Core radiation can be reduced by substituting a portion of the Ne with B, leveraging their complementary non-coronal equilibrium radiation efficiencies. This combined B + Ne injection scheme presents a promising pathway toward integrated core-edge scenarios, offering the potential to minimize total impurity throughput while leveraging an actuator (powder injection) already being considered for ITER.

Boron↗

Molecular dynamics simulations of reflection and sputtering behavior of boron under deuterium ion irradiation

Boronization is a commonly used method of wall conditioning in fusion reactors. The application of boron films to the plasma-facing materials results in enhanced plasma performance due to the reduction of intrinsic impurities. This is primarily driven by a reduction in oxygen content that is chemically trapped in the boron film. The reactive nature of these boron films also raises questions concerning interactions with hydrogen isotopes. In this work, boron-deuterium interactions were studied using molecular dynamics (MD). Reactive force field potentials were used to model the chemical interactions between B and D. An amorphous boron substrate was irradiated by D atoms at varying incident energies, 10 eV < E i < 150 eV and angles, 0° < α < 85°. The reflection probability was calculated and compared to results from the commonly-used binary collision approximation (BCA) method. This comparison found that the BCA underestimated the reflection probability at E i < 35 eV and α > 45 ∘ . The source of this discrepancy was found to be the surface binding energy model. The BCA calculation with an isotropic surface binding energy model was more closely aligned to the MD result. This, in combination with a correction function based on the MD results allows for corrections to the reflection probability of deuterium impinging on boron surfaces. The sputtering of the substrate material was also studied. While this study did not contain sufficient events to quantitatively describe the sputtering behavior, some qualitative results emerged: namely, chemical sputtering of B and D-containing molecules (BD, BD 2 , BD 3 ) at low ( < 20 eV) incident deuterium energies. This result suggests that chemical sputtering could be a significant factor in limiting boron coating lifetime when exposed to lower ion energies, such as those in detached plasmas. The results show that chemical interactions should be taken into account when modeling the interactions between D ions and B surfaces.

Boron↗

Fabrication, oxidation, and combustion of nanoscale magnesium diboride and tetraboride

The difficult ignition and low combustion efficiency of boron particles decrease the performance of boron-loaded, fuel-rich propellants for solid fuel ramjets and ducted rockets. One approach to solving this problem involves the use of magnesium diboride (MgB 2 ), which ignites easier than boron. Magnesium tetraboride (MgB 4 ) offers greater energy density owing to its higher boron content. However, the effect of B/Mg ratio on the ignition and combustion is unknown. Additionally, while nanoscale MgB₂ particles and quasi-2D structures are promising energetic additives, the oxidation and combustion properties of nanoscale MgB₄ have not been explored. To address these knowledge gaps, the present work included synthesis and high-energy ball milling of MgB 2 and MgB 4 powders, thermogravimetric analysis (TGA) of their oxidation, and combustion experiments with thin layers of the obtained powders. Comparison of two synthesis routes (a solid-state reaction in a tube furnace and combustion synthesis) has shown that the former is the superior method for producing magnesium borides. TGA has revealed that oxidation of both MgB 2 and MgB 4 results in a high conversion into the oxides (88–91 %), far exceeding the low conversion of boron (62.5 %). MgB 4 begins to oxidize rapidly at a much lower temperature (∼900 °C) than MgB 2 (∼1200 °C). The burning rates of milled MgB 2 and MgB 4 are about eight and five times, respectively, faster than that of submicron boron. Magnesium borides exhibit a stable, sustained boron flame, needed for high combustion efficiency, whereas physical Mg/B mixtures undergo Mg-driven "flash" combustion.

Boron↗