Doping Metallic Grain Boundaries to Control Atomic Structure and Damage Tolerance

Abstract

Grain boundaries often act as sites for crack and void nucleation during plastic deformation of metallic materials. While it is known that grain boundary character and structure can greatly influence this damage nucleation process, the current level of control over such details is limited. The objective of this project was to obtain a fundamental understanding of how metallic grain boundary structure can be controlled through intelligent doping, with the idea of inducing planned amorphous grain boundary phases or complexions. The effect of amorphous complexion structure on dislocation accommodation mechanisms was studied, to improve the field’s understanding of damage nucleation at a promising type of interface. Different microstructural descriptors were studied, as grain boundaries can have large variations and complexity of local structure, and influence the mechanical damage resistance of these features was tested. Nanocrystalline systems that contain amorphous grain boundary complexions were prioritized, as these have more extreme variations in interfacial structure and damage tolerance, with an emphasis on isolating the importance of complexion population (type, thickness, etc.), network topology, local structure, and local chemistry. This research used a combination of computational, experimental, and characterization techniques to isolate and understand the importance of nanoscale grain boundary structure and interfacial chemistry. Amorphous grain boundary complexions were found to clearly increase a material’s resistance to mechanical damage, with the local distribution of structural short-range order within the complexions found to be an important descriptor for damage and the proposed focus of future work in this area.