Interface-engineered (AlMnCoNiZn) 3 O 4 @PPy nanocomposites for superior lithium storage: Mechanism and performance

Abstract

The practical application of graphite anodes in lithium-ion batteries (LIBs) is constrained by low specific capacity (372 mAh g -1 ) and sluggish kinetics. Here, to address these limitations, our present study focuses on high-entropy oxides (HEOs), which offer high theoretical capacity and structural stability. We synthesized spinel-structured (AlMnCoNiZn) 3 O 4 nanoparticles via a solution combustion method and fabricated an (AlMnCoNiZn) 3 O 4 @polypyrrole (PPy) nanocomposite through in-situ polymerization. Our electrochemical tests demonstrate that the PPy modification significantly enhances performance. While the pristine (AlMnCoNiZn) 3 O 4 delivered 445 mAh g −1 after 100 cycles at 100 mA g −1 and 350 mAh g −1 after 1000 cycles at 1000 mA g −1 , the (AlMnCoNiZn) 3 O 4 @PPy composite achieved 695 mAh g −1 after 100 cycles and maintained 675 mAh g −1 after 1000 cycles. Furthermore, the composite improved rate capacity at 1000 mA g −1 from 211 mAh g −1 to 403 mAh g −1 . This work highlights how conductive and flexible polymer modifications can dramatically improve the electrochemical properties of HEOs. The developed (AlMnCoNiZn) 3 O 4 @PPy composite provides a promising direction for designing advanced anodes to meet next-generation energy storage demands.