Creep Property of Intermetallic Dispersive Steels for Nuclear Applications

Abstract

To meet the materials performance demands of next-generation nuclear and high-temperature energy systems, a new class of intermetallic-dispersive steels (IDS) has been designed through integrated computational thermodynamics and alloy design strategies. The IDS alloys incorporate coherent L1₂ (γ′-Ni₃Al) nanoprecipitates within an Fe–Ni–Cr austenitic matrix, engineered to achieve both high temperature strength and thermodynamic stability while suppressing the formation of detrimental δ-Ni₃Nb and η-Ni₃Ti phases. Initial creep testing of Ti-IDS and TiTa-IDS alloys demonstrates rupture lives comparable to or exceeding those of Inconel 718 and ODS steels, despite being fabricated through conventional ingot metallurgy. Step-load creep tests identified a stress threshold near 300–350 MPa for the onset of tertiary creep, and in-situ neutron diffraction experiments on Ti-IDS revealed clear load partitioning between the matrix and γ′ precipitates: elastic strain is shared by both phases, while plastic strain localizes in the matrix. These results confirm that stable γ′–matrix interfaces play a dominant role in retarding dislocation motion and enhancing creep resistance. In FY26, the program will conduct repeat creep rupture testing of TiTa-IDS at 650 °C/400 MPa, initiate long-term rupture testing of TiNb-IDS, and perform TEM-based microstructural characterization to elucidate dislocation–precipitate interactions and microstructural stability. Collectively, these efforts will establish the mechanistic foundation for next-generation high-temperature structural materials based on the IDS concept.