Multilayer Architecture Barriers for High Temperature Nuclear Applications

Abstract

Innovative thin film multilayer metal/ceramic barrier coatings have been developed by Argonne National Laboratory to protect fuel cladding against different phenomena that can be encountered under the harsh operating conditions of advanced nuclear reactors. One phenomenon is Fuel-Cladding Chemical Interaction (FCCI), which can represent a challenge to the performance of steel-clad metallic fuels in sodium-cooled fast reactors (SFRs), especially when operating to high burnups at elevated cladding temperatures, and long fuel residence time. Another phenomenon is the corrosion of zirconium-based cladding under prototypic boiling water reactor (BWR) conditions and associated cladding during off normal conditions, including loss of coolant accidents (LOCA). This work provides details of the development and testing of a thin film (few microns) multilayer metal/ceramic (CrY/Y 2 O 3 ) coatings on steel cladding and its performance against FCCI. The coating architecture evolved through systematic mechanical testing, radiation tolerance assessments, and high-temperature diffusion studies from a preliminary multilayer concept to an optimized high-performance design. The optimized structure leverages stoichiometric Y 2 O 3 for its exceptional radiation stability, chemical inertness, and ultra-low fission product diffusivity (e.g., Ce diffusivity ~10 -20 m 2 /s in irradiated Y 2 O 3 at 650 °C). This is paired with ductile chromium-rich interlayers (Cr 95 Y 5 ), which significantly enhance fracture toughness and mechanical resilience. Design refinements, including increased ceramic layer thickness and optimized Cr–Y interlayer composition, eliminated fracture propagation and preserved coating integrity under extreme mechanical stress (>10× typical reactor conditions) and prolonged radiation exposure (~300 dpa). Those conditions are well beyond expected conditions during normal operations in SFR, and cover some of the transient conditions as well. In addition, the coating deposition was demonstrated to be applied uniformly to the inner surface of steel tubes representing prototypic SFR cladding. Another phenomenon under consideration in this work is the corrosion of zirconium-based cladding under prototypic boiling water reactor (BWR) conditions and associated off normal conditions including loss of coolant accident (LOCA). Another multilayer thin film coating is considered for mitigation of this phenomenon, where a coating of yttrium aluminum and yttrium aluminum ceramic/metal thin film coating. Preliminary results on the coating performance during high temperature thermal cycling (up to 1000 C) have shown promising performance of the coating. On-going optimization of the coating will continue in FY26.