Carbon in GaN as a nonradiative recombination center

Abstract

Trap-assisted nonradiative recombination has been shown to limit the efficiency of optoelectronic devices. While substitutional carbon (⁠C N ) has been suggested to be a nonradiative recombination center in GaN devices, a complete recombination cycle including the two charge-state transition levels has not been previously described. In this work, we investigate the trap-assisted recombination process due to C N in GaN, including multiphonon emission, radiative recombination, trap-assisted Auger–Meitner (TAAM) recombination as well as thermal emission of holes. Our study shows the key role of TAAM processes at the high carrier densities relevant for devices. We also reveal the carrier-density regimes where thermal emission and radiative recombination are expected to play an observable role. Our results highlight that carbon concentrations exceeding ~10 17 cm −3 can have a noticeable impact on device efficiency, not just in GaN active layers but also in InGaN and AlGaN. Furthermore, our comprehensive formalism not only offers detailed results for carbon but also provides a general framework for assessing the multiple processes that participate in trap-assisted recombination in semiconductors.

Explore related subjects

Keep this discovery

BibTeXRIS

Zhao, Fangzhou [University of California, Santa Barbara, CA (United States); Max Planck Institute for Structure and Dynamics of Matter and Center for Free-Electron Laser Science, Hamburg (Germany)] (ORCID:0000000173557406), Guan, Hongyi [University of California, Santa Barbara, CA (United States)] (ORCID:0000000213445258), Turiansky, Mark E. [University of California, Santa Barbara, CA (United States); US Naval Research Laboratory, Washington, DC (United States)] (ORCID:0000000291543582), Van de Walle, Chris G. [University of California, Santa Barbara, CA (United States)] (ORCID:0000000242125990). 2025-05-21. Carbon in GaN as a nonradiative recombination center. https://doi.org/10.1063/5.0267877

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

Integrated Approach to Post-Irradiation Examination of Nuclear Materials at Idaho National Laboratory

Idaho national Laboratory (INL) is the U.S. lead national laboratory for the Department of Energy’s Office of Nuclear Energy (DOE-NE), providing much of the nuclear research, development and demonstration capability needed to move nuclear innovation forward to deployment. INL’s Materials and Fuels Complex hosts a unique combination of personnel, facilities and infrastructure and offers the ability to perform post-irradiation examinations (PIE) of nuclear materials spanning multiple length scales. The ability to combine engineering-scale analysis and sub-microscopic characterization provides valuable insights into fuel and structural material behavior and degradation mechanisms. The holistic approach is used to accelerate these materials demonstration and deployment. Selected studies will be presented, highlighting the impact of these techniques on improving fuel reliability, safety, and efficiency, thereby advancing the development of sustainable and advanced nuclear energy technologies.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS

Kinetic control of phase evolution and defect-mediated recombination in AACVD-grown copper antimony sulphide thin films

Copper antimony sulphide (CAS) is a multinary chalcogenide semiconductor in which small deviations from stoichiometry can drive phase competition and strong defect-mediated modulation of optoelectronic properties. However, the systematic roles of copper precursor fraction and deposition time in governing phase evolution, off-stoichiometry, and recombination dynamics in aerosol-assisted chemical vapour deposition (AACVD)-grown undoped CAS thin films remain insufficiently understood. In this work, undoped CAS thin films were deposited by AACVD using Cu(dedtc)2 and Sb(dedtc)3 single-source precursors at 550 °C and a carrier gas flow rate of 150 sccm, while the Cu(dedtc)2 mole fraction (x = 0.15 – 0.55) and deposition time (1 – 2 hours) were systematically varied to probe how growth kinetics influence phase composition, microstructure, and defect-mediated optical properties without post-deposition annealing or extrinsic doping. Increasing copper precursor content drives phase evolution toward tetrahedrite-dominant CAS films at intermediate Cu(dedtc)2 mole fractions, with the film deposited at x = 0.35 exhibiting the strongest tetrahedrite character within the parameter space examined. The films are also copper-rich, antimony-poor, and sulphur-deficient, consistent with off-stoichiometric growth and intrinsic defect formation, plausibly including copper interstitials, Cu-on-Sb antisites, and sulphur vacancies. These growth-dependent compositional deviations are accompanied by tunable indirect optical bandgaps of approximately 1.60 – 2.18 eV and weak visible photoluminescence governed by defect-mediated recombination. Time-resolved photoluminescence reveals bi-exponential decay behaviour with lifetimes of approximately 0.1 – 3.6 ns, with emission dominated by slower donor–acceptor pair recombination and a smaller contribution from faster trap-assisted pathways. Collectively, these results establish an explicit kinetic process–structure–defect–property relationship for AACVD-grown CAS thin films and provide a growth–structure–property framework relevant to future optimization of CAS-based optoelectronic and energy materials.

36 MATERIALS SCIENCE

Thermal Disorder‐Induced Strain and Carrier Localization Activate Reverse Halide Segregation

The reversal of halide ions is studied under various conditions. However, the underlying mechanism of heat-induced reversal remains unclear. This work finds that dynamic disorder-induced localization of self-trapped polarons and thermal disorder-induced strain (TDIS) can be co-acting drivers of reverse segregation. Localization of polarons results in an order of magnitude decrease in excess carrier density (polaron population), causing a reduced impact of the light-induced strain (LIS – responsible for segregation) on the perovskite framework. Meanwhile, exposing the lattice to TDIS exceeding the LIS can eliminate the photoexcitation-induced strain gradient, as thermal fluctuations of the lattice can mask the LIS strain. Under continuous 0.1 W cm -2 illumination (upon segregation), the strain disorder is estimated to be 0.14%, while at 80 °C under dark conditions, the strain is 0.23%. However, in situ heating of the segregated film to 80 °C under continuous illumination (upon reversal) increases the total strain disorder to 0.25%, where TDIS is likely to have a dominant contribution. Therefore, the contribution of entropy to the system's free energy is likely to dominate, respectively. Various temperature-dependent in situ measurements and simulations further support the results. These findings highlight the importance of strain homogenization for designing stable perovskites under real-world operating conditions.

36 MATERIALS SCIENCE