Thick graded interfaces increase wear resistance in Ti/TiN nanolayered thin films

Cheng, Justin Y. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223391142); Hamilton, Ashlie [Univ. of Minnesota, Minneapolis, MN (United States)]; Odlyzko, Michael [Univ. of Minnesota, Minneapolis, MN (United States)]; De Leo, Mauricio [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223239757); Baldwin, J. Kevin [Los Alamos National Laboratory (LANL), Los Alamos, NM (United States). Center for Integrated Nanotechnologies (CINT)]; Mara, Nathan A. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000291354693)

doi:10.1016/j.tsf.2025.140653

DOE OSTI · 2911682

Thick graded interfaces increase wear resistance in Ti/TiN nanolayered thin films

Cheng, Justin Y. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223391142)·Hamilton, Ashlie [Univ. of Minnesota, Minneapolis, MN (United States)]·Odlyzko, Michael [Univ. of Minnesota, Minneapolis, MN (United States)]·De Leo, Mauricio [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223239757)·Baldwin, J. Kevin [Los Alamos National Laboratory (LANL), Los Alamos, NM (United States). Center for Integrated Nanotechnologies (CINT)]·Mara, Nathan A. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000291354693)

View original source ↗Read source document ↗Export metadata ↓

Abstract

Multilayered composites with nanoscale layer thickness incorporating titanium and titanium nitride (Ti/TiN) are used as a model system to study the effects of heterophase interface structure on elastic and plastic deformation, as well as wear behavior. Here, in this work, hardness, modulus, and wear rate under dry reciprocating sliding contact are quantified as a function of Ti-TiN heterophase interfacial nitrogen gradient thickness for Ti/TiN multilayers with 10–80 nm layer thickness. Hardness and modulus are found to be inversely proportional to layer thickness and independent of interface gradient for most specimens. Wear rate is found to be inversely proportional to interface gradient thickness at constant layer thickness, demonstrating that control of nanoscale interface structure is a valid approach to enhancing wear behavior. The materials studied in this work wear comparably or slower than other Ti- and TiN-based composites in the literature, providing a promising avenue for engineering wear-resistant materials for use in industrially relevant applications.

Explore related subjects

Graded interfaces Multilayers Nanoindentation Nanowear Physical vapor deposition

Keep this discovery

BibTeX RIS

Cheng, Justin Y. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223391142), Hamilton, Ashlie [Univ. of Minnesota, Minneapolis, MN (United States)], Odlyzko, Michael [Univ. of Minnesota, Minneapolis, MN (United States)], De Leo, Mauricio [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000223239757), Baldwin, J. Kevin [Los Alamos National Laboratory (LANL), Los Alamos, NM (United States). Center for Integrated Nanotechnologies (CINT)], Mara, Nathan A. [Univ. of Minnesota, Minneapolis, MN (United States)] (ORCID:0000000291354693). 2025-03-08. Thick graded interfaces increase wear resistance in Ti/TiN nanolayered thin films. https://doi.org/10.1016/j.tsf.2025.140653

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Mapping the Microhardness of Al Matrix in U-7Mo/Al Dispersion Fuels at Medium and High Burn-up by in situ Nanoindentation

The mechanical degradation of the Al matrix in U-7Mo dispersion fuels was detected after irradiation in previous studies, but more details of the degradation mechanism are not clear yet to clarify the root cause. In this study, microhardness mapping in fresh and irradiated U-7Mo dispersion fuels coated with ZrN, with burn-up of 3.35 × 10 21 and 6.28 × 10 21 f/cm 3 , are measured to reveal the hardening of the Al matrix as a function of distance to fuel particles. Micro cubes were pulled by plasma focused ion beam scanning electron microscopy and tested by in situ nanoindenter with Berkovitch tip. Size effects are measured in medium and high burn-up samples. The higher burn-up specimen exhibits a more pronounced size effect when indent load is lower than 20 mN. Size effect correction models are also calculated by plots fitting, which predicts the true microhardness without size effect. Results shows that the hardness of the Al matrix near the ZrN coating has the highest value, then decreases moving away from the coating and become stable when the distance reaches ∼10 µm. The hardness starts increasing again getting closer to the next fuel particle, which makes the hardness distribution between two fuel particles to be “U” shape.

36 - MATERIALS SCIENCE↗

DOE OSTI2024

Thermal stability of 3D interface Cu/Nb nanolaminates

Nanocrystalline alloys are promising structural materials yet lack thermal stability in many cases. Recent work shows that interface structure has an outsize effect on the thermal behavior of nanostructured alloys. Here, this work focuses on the role of controlled heterophase interface structure in the thermal evolution of model Cu/Nb nanolaminates. We introduce 3D interfaces containing nanoscale heterogeneities in all spatial dimensions between Cu and Nb, forming 3D Cu/Nb. TEM, nanoindentation, and DSC are used in tandem to establish thermal stability and to identify shifts in microstructure as a function of static annealing temperature. 3D interfaces are shown to survive annealing to 300 °C for 1 hr., while 3D Cu/Nb microstructure evolves to form low-density and voided regions correlating to the onset of layer pinch-off between 500 and 600 °C annealing temperatures. A diffusivity- and vacancy energetics-based mechanism is developed to explain void formation driven by 3D interface degradation at elevated temperature.

3D interfaces↗

DOE OSTI2026

All-Polyester Multilayer Plastics (‘All-Polyester MLPs’): A Redesign for Inherently Recyclable Plastics

Multilayer plastics (MLPs) are widely used in modern packaging because they combine multiple functions such as oxygen and moisture barriers, mechanical strength, puncture resistance, and heat sealability into lightweight and cost-effective packaging solutions. These attributes are essential for food, beverage, pharmaceutical, and consumer goods packaging. However, conventional commercial MLPs typically consist of five to twelve layers made from chemically incompatible materials, including polyolefins, polyethylene terephthalate, nylon, ethylene-vinyl alcohol (EVOH), adhesives, and tie layers. This complexity makes MLPs extremely difficult to recycle. As a result, the vast majority of multilayer plastics (MLPs) are disposed of through landfilling or incineration. This disposal pathway perpetuates demand for virgin material production, thereby driving high industrial energy consumption, increasing greenhouse gas (GHG) emissions, and contributing to the long-term accumulation of plastic waste. The scope of work included: (1) Design and fabrication of all-polyester multilayer structures using commercially relevant processing methods; (2) Experimental validation of barrier, mechanical, and sealing performance; (3) Demonstration of both mechanical and chemical recycling pathways; and (4) Comprehensive techno-economic analysis (TEA) and life-cycle assessment (LCA) to quantify cost, energy, and environmental impacts.

36 MATERIALS SCIENCE↗