Light, High Performance and Scalable Coal-Derived Composites for Construction: Precast and Cast-in-Place Applications

Abstract

The overall objective of this project was to produce a coal-based construction material that has up to ~95 weight percent (wt. %) coal with physical, chemical, and thermal properties exceeding those of ordinary Portland cement (OPC)-based construction materials. Additionally, the project aimed to minimize external binders by implementing novel mixing techniques, while exceeding the performance/cost ratio of OPC. Finally, the project was to demonstrate production of precast products via the design and fabrication of products via a bench scale process. Consistent with some of these objectives, the project successfully fabricated samples of coal-based composite materials with >80 wt% coal with physical, chemical and thermal properties on par with cement-based concrete. Select samples demonstrated compressive strengths with >7,000 psi and flexural strength of >420 psi. The composite materials minimized external binders and also demonstrated durability, as evidenced by resistance to acidic and basic solutions. Finally, larger slab and beam type samples were produced using a process developed by the Recipient, although, the process was not semicontinuous in nature. Taken together, the results of this project suggest that domestic coal has potential to serve as a replacement for cementitious materials utilized in incumbent construction technologies, which could significantly reduce the energy and emissions of the construction industry