Diffusion and phase formation in the γ-uranium-technetium system

Abstract

Phase formation in the U-Tc binary system at 800 °C was investigated using a diffusion couple experiment. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) identified four novel potential intermetallic phases - U 7 Tc 3 , U 13 Tc 12 , U 3 Tc 5 , and UTc 4 . Diffusion coefficients were calculated for the intermetallic phases using the Boltzmann-Matano method and were respectively found to be – 120, 38.2, 15.6, and 1.51 × 10 −18 m 2 /s. Tc also exhibits a solid-solution phase with high penetration into the U with a diffusion coefficient of ∼ 10 −14 m 2 /s. Furthermore, these findings expand the number of known U-Tc phases and provide the first diffusion coefficients for the U-Tc system, and contribute valuable data to the broader field of actinide metallurgy.