Optimization of catholyte for halide-based all-solid-state batteries

Abstract

Halide solid electrolytes gain significant attention due to their high ionic conductivity, low processing temperature, dry air compatibility, and high-voltage stability. However, low cathode active material (CAM) loading in the composite cathode constrains the realization of high energy density for halide-based all-solid-state batteries. In this study, three halide materials, raw Li 3 YBrCl 5 (LYBC-R, <30μm), milled LYBC (LYBC-M, <5 μm) and freeze-dried Li 3 InCl 6 (LIC, <500 nm), were used as catholytes, combined with LYBC-M as the electrolyte and LiIn alloy as the anode. The CAM:catholyte ratio was investigated as well as stack pressure and operating temperature. Our study demonstrates that particle size of the catholyte plays an important role only for high CAM loading or high C-rate cycling. At moderate CAM loading (65 and 70wt% LiNi 0.83 Mn 0.06 Co 0.11 O 2 ) and 0.1 C-rate, all the three catholytes perform well, providing initial discharge capacities >177 mAh/g. At high CAM loading (85wt%) and 0.1 C-rate, a cathode with the nano-scale LIC catholyte provides discharge capacity of 175 mAh/g, while the larger particle size catholytes suffer significantly reduced capacity. Both LYBC and LIC catholytes provided capacity retention >80% after 200 cycles at 0.5C. These results imply that cathode particle size is critically important for performance at high CAM loading. Furthermore, both electrolyte and cathode were tape cast to scale up size and prepare realistic layer thicknesses. A small amount of binder was used in both layers, to balance the electrochemical performance and mechanical properties. Further, the discharge capacity of a tape cell was 152mA h/g at 0.1C with a capacity retention of 81.8% after 20 cycles at 0.5C. The results demonstrate the excellent performance of LYBC as an electrolyte, and provide guidance for halide-based cathode design.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Shen, Fengyu [Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)], McGahan, Michael [Saint-Gobain Research North America, Northborough, MA (United States)], Pietras, John D. [Saint-Gobain Research North America, Northborough, MA (United States)], Doeff, Marca M. [Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)], Battaglia, Vincent S. [Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)], Tucker, Michael C. [Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)] (ORCID:000000028508499X). 2025-03-09. Optimization of catholyte for halide-based all-solid-state batteries. https://doi.org/10.1016/j.jpowsour.2025.236709

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

An immersed interface method for microstructure-scale electrochemical battery models: numerical formulation and performance portable implementation

We present the numerical formulation, verification, and performance portable implementation of an immersed interface method for microstructure scale electrochemical modeling of batteries. The innovation in this approach is the resolution of chemical species and electrostatic potential discontinuities at active interfaces without the use of interface conforming unstructured grids. A unified formulation on Cartesian grids for all domains (electrodes and electrolyte) is used with interfacial flux conditions applied using volume fraction or “color” function gradients. We have developed one dimensional and two dimensional test cases with analytic solutions for electrochemical modeling using which we verified the consistency and accuracy of our scheme. Our solver is also validated against solutions from a macroscale model and an unstructured multi-subdomain solver for a full lithium ion cell. We then demonstrated the utility of our solver on an image-based complex battery electrode microstructure at high charging rate. Our technique also exhibits good scalability on distributed memory architectures using central processing units (CPU), with problem sizes up to 1.8 billion degrees of freedom and with 5400 ranks. Initial performance studies of our open-source performance portable solver showed about 70 times speed up using a graphics processing unit (GPU) compared to single compute core for a problem with 4 million cells.

25 ENERGY STORAGE

Solvation-guided inhibition of manganese dissolution of lithium- and manganese- rich cathode via cyclic carbonate molecular engineering

Lithium and manganese-rich (LMR) layered oxides represent a leading class of high-energy cathode materials, but their practical realization is fundamentally limited by severe manganese (Mn) dissolution, a process that triggers structural degradation and rapid capacity fade. While mitigation efforts have predominantly focused on interfacial engineering, the intrinsic contribution of bulk electrolyte solvation to this degradation pathway remains largely unexplored, primarily due to the difficulty of deconvolving its effects from concurrent cathode-electrolyte interphase (CEI) formation. Here, we report an experimental design to isolate the role of solvation. We systematically varied the electrolyte solvent solvation power by substituting the strongly coordinating ethylene carbonate (EC) with its weaker coordinating fluorinated derivatives, fluoroethylene carbonate (FEC) and trans-4,5-Difluoro-1,3-dioxolan-2-one (DFEC), while maintaining a consistent interfacial chemistry. Remarkably, the electrolyte formulated with the weakest solvent, DFEC, exhibits superior cycling stability, suppressing Mn dissolution by up to 63% relative to the conventional EC-based system. Post-mortem analysis unequivocally attributes this performance enhancement to the preservation of the LMR cathode's structural integrity, a direct consequence of mitigated Mn dissolution. This work provides conclusive evidence that modulating bulk electrolyte solvation is a potent and direct strategy for stabilizing LMR cathodes, establishing a vital design principle for next-generation battery systems.

25 ENERGY STORAGE

Geothermal district energy systems coupled with seasonal underground thermal energy storage: a U.S. techno-economic screening by climate and geology

In the United States, cooling-dominated commercial building loads can cause geothermal heat pump-based district energy systems to accumulate a long-term subsurface thermal imbalance, motivating the incorporation of seasonal underground thermal energy storage. We developed a transferable workflow to evaluate geothermal district systems that pair ground heat exchangers with seasonal underground thermal energy storage. Using standardized hourly loads for seven commercial buildings and a uniform cost framework, we simulated ten U.S. cities with a physics-based ground heat exchanger model, subsurface storage simulations, and economic assessment to isolate the roles of climate and hydrogeology. In cooling-dominated cities, underground thermal energy storage supplied the majority of annual cooling, cutting electricity use and summer peaks substantially while achieving levelized costs comparable to or below conventional chiller-boiler plants. In cooler climates, the storage share shrunk, required borefield size and costs rose, and levelized cost of energy increased nearly linearly with declining underground thermal energy storage fraction, indicating storage fraction as the primary economic lever. Sensitivity analysis showed capital risk dominated by borefield drilling and surface heating, ventilation, and air-conditioning and piping, with underground thermal energy storage costs secondary. This workflow provides a transparent foundation for site-specific design and screening of next-generation geothermal district energy systems.

25 ENERGY STORAGE