Relithiation process for direct regeneration of cathode materials from spent lithium-ion batteries

Belharouak, Ilias·Bai, Yaocai·Essehli, Rachid·Li, Jianlin
View original source ↗Read source document ↗Export metadata ↓

Abstract

A method for the regeneration of cathode material from spent lithium-ion batteries is provided. The method includes dissolving a lithium precursor in a polyhydric alcohol to form a solution. Degraded cathode material containing lithium metal oxides are dispersed into the solution under mechanical stirring, forming a mixture. The mixture is heat treated within a reactor vessel or microwave oven. During this heat treatment, lithium is intercalated into the degraded cathode material. The relithiated electrode material is collected by filtration, washing with solvents, and drying. The relithiated electrode material is then ground with a lithium precursor and thermally treated at a relatively low temperature for a predetermined time period to obtain regenerated cathode material.

Keep this discovery

BibTeXRIS

Belharouak, Ilias, Bai, Yaocai, Essehli, Rachid, Li, Jianlin. 2024-08-20. Relithiation process for direct regeneration of cathode materials from spent lithium-ion batteries. https://www.osti.gov/biblio/2542520

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Lithium-ion batteries material

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2024

Efficient Leaching of Metal Ions from Spent Li-Ion Battery Combined Electrode Coatings Using Hydroxy Acid Mixtures and Regeneration of Lithium Nickel Manganese Cobalt Oxide

Extensive use of Li-ion batteries in electric vehicles, electronics, and other energy storage applications has resulted in a need to recycle valuable metals Li, Mn, Ni, and Co in these devices. In this work, an aqueous mixture of glycolic and lactic acid is shown as an excellent leaching agent to recover these critical metals from spent Li-ion laptop batteries combined with cathode and anode coatings without adding hydrogen peroxide or other reducing agents. An aqueous acid mixture of 0.15 M in glycolic and 0.35 M in lactic acid showed the highest leaching efficiencies of 100, 100, 100, and 89% for Li, Ni, Mn, and Co, respectively, in an experiment at 120 °C for 6 h. Subsequently, the chelate solution was evaporated to give a mixed metal-hydroxy acid chelate gel. Pyrolysis of the dried chelate gel at 800 °C for 15 h could be used to burn off hydroxy acids, regenerating lithium nickel manganese cobalt oxide, and the novel method presented to avoid the precipitation of metals as hydroxide or carbonates. The Li, Ni, Mn, and Co ratio of regenerated lithium nickel manganese cobalt oxide is comparable to this metal ratio in pyrolyzed electrode coating and showed similar powder X-ray diffractograms, suggesting the suitability of α-hydroxy carboxylic acid mixtures as leaching agents and ligands in regeneration of mixed metal oxide via pyrolysis of the dried chelate gel.

Electrochemistry↗
DOE OSTI2026

Direct regeneration of degraded LiFePO4 cathodes via a separator-enabled prelithiation strategy

A persistent challenge in lithium-ion batteries is the loss of active lithium due to the solid electrolyte interphase (SEI) formation and associated side reactions. While prelithiation employing lithium replenishment separator (LRS) has been proven effective in compensating for lithium loss, previous studies have largely been accompanied by gas evolution or solid residue formation during the prelithiation process. To surmount this challenge, we present a LRS based on 4-fluoro-1,2-dihydroxybenzene lithium salt (LiDF), capable of mitigating lithium loss while producing decomposition products that integrate directly into the electrolyte as functional additives which can assist with the stability of the SEI, free from gas or solid formation, thus establishing a sustainable and environmentally benign strategy for lithium compensation. Incorporation of the LRS enables the pristine LiFePO4||graphite (Gr) full cell to achieve 10.8% higher capacity than the cell with a polypropylene separator (PPS) after 200 cycles at 0.5C. Remarkably, the degraded LiFePO4 (D-LFP)||Gr full cell with the LRS exhibits a 135.8% capacity improvement over the PPS-based cell after 500 cycles. These findings establish the LRS as a powerful approach for both boosting high-performance lithium-ion batteries and recovering the capacity of degraded batteries.

Tao, Fujun↗