Negative linear compressibility and complex phase behaviour in 7Li2CO3

Hinton, Jasmine [Oak Ridge National Laboratory] (ORCID:000000034417462X); Ridley, Chris (ORCID:0000000230609656)

doi:10.14461/oncat.data/2536722

Home/Archive/DOE OSTI

DOE OSTI · 2536722

Negative linear compressibility and complex phase behaviour in 7Li2CO3

Hinton, Jasmine [Oak Ridge National Laboratory] (ORCID:000000034417462X)·Ridley, Chris (ORCID:0000000230609656)

View original source ↗Read source document ↗Export metadata ↓

Abstract

High pressure data collected from polycrystalline isotopically enriched 7Li2CO3 using the Paris-Edinburgh press on the SNAP diffractometer. Single toroidal cBN anvils were used with a TiZr gasket. The sample was measured with and without a pressure medium.

Explore related subjects

high pressure lithium MATERIALS SCIENCE neutron diffraction paris-edinburgh press

Keep this discovery

Explore connections, maps & timelines

BibTeX RIS

Hinton, Jasmine [Oak Ridge National Laboratory] (ORCID:000000034417462X), Ridley, Chris (ORCID:0000000230609656). 2025-03-24. Negative linear compressibility and complex phase behaviour in 7Li2CO3. https://doi.org/10.14461/oncat.data%2F2536722

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Polymorphism of Magnesium Chloride Decahydrate under High Pressures and Low Temperatures Found in Icy Moons

Magnesium chloride hydrates show a rich diversity of structural forms, with different hydration numbers ranging from 1 to 12. Here, we show that this structural versatility is also present within the same hydration numbers, with the formation of a new phase of magnesium chloride decahydrate (MgCl 2 ·10H 2 O-II) stable at the conditions of 0.03–0.40(14) GPa at 234(11) K and up to 2.11(3) GPa at 220(2) K, as determined by in situ single-crystal X-ray diffraction. The hydrogen bonding interactions of MgCl 2 ·10H 2 O-II are identified and the bulk modulus determined at B 0 = 18.9(12) GPa at 220(2) K. We discuss the implication of this high-pressure MgCl 2 hydrate for icy moon compositional investigations and showcase the structural and density changes between the various hydrates in MgCl 2 ·nH 2 O.

high pressure↗

DOE OSTI2025

Pressure-induced cation and vacancy disorder-order transition and near-zero τ f in deficient hexagonal perovskite Ba 8 ZnTa 6 O 24 dielectrics

Pressure applications can enable the tuning of atomic/defect ordering and provide access to new functional materials. Here, in this study, we report that pressure-induced structural transformation featuring disorder-order transition of both cations and vacancies in the 8-layer deficient hexagonal perovskite tantalate dielectrics Ba 8 ZnTa 6 O 24 , which transformed the structure from twin to shift and remarkably lowered the temperature coefficient of resonant frequency τ f down to near zero (∼0.56 ppm/°C) from 38 ppm/°C for the twinned precursor. The atomic scale STEM-HAADF and EDS results confirm the ordering of Zn in the Ta host at the nanometer scale in the shifted material featuring well-ordered Ba 8 ZnTa 6 O 24 slabs intergrown with Ba 3 ZnTa 2 O 9 and Ba 5 Ta 4 O 15 monolayers and anti-phase grain boundaries as planar defects. The pressure-induced twin-shift structural transformation of Ba 8 ZnTa 6 O 24 features the rare constant concentration of the hexagonal stacked layers, which is allowed by the vacancy ordering at the central layers of face-shared octahedral (FSO) trimers avoiding the FSO B-B repulsion, and remarkably the faster cationic ordering kinetics compared with the 2:1 ordered complex perovskites. Although the inclusion of numerous planar defects and the oxidizable atomic defects led to significant p-type conduction and inhomogeneous electrical microstructures, resulting in an extraordinarily high extrinsic dielectric loss for the high-pressure shifted Ba 8 ZnTa 6 O 24 pellet, the intrinsically near-zero τ f could make the shifted Ba 8 ZnTa 6 O 24 perovskite an ideal microwave dielectric resonator candidate if the defects could be eliminated.

high pressure↗

DOE OSTI2025

Coexistence of ordered and disordered vacancies in tungsten diboride with a broken hexagonal symmetry

As an important member of transition-metal borides, tungsten diboride (i.e., WB 2+𝑥 ) contains complex atomic vacancies with the originally assigned hexagonal symmetries, exhibiting many fascinating properties such as superconductivity and superior hardness. However, due to the difficulties in exploring atomic vacancies of transition-metal borides, the actual structure and composition of WB 2+𝑥 have been long-standing unsettled issues, which have impeded in-depth understanding of its structural stability and origins of such extraordinary properties. Here, we report a systematic investigation of the crystal structure of high-pressure synthesized WB 2+𝑥 samples by combination of state-of-the-art diffraction techniques and microstructural observations, leading to the discovery of an unusual coexistence of both the ordered and disordered atomic vacancies in WB 2+𝑥 with a broken hexagonal symmetry that can be well described by a dual-phase model involving hP12-W 0.70 ⁢B 1.73 and P1-W 0.75⁢ B 1.64 . Superposition of thin sample layers with disordered vacancies along the [001] or [110] direction is revealed to produce ordered vacancies, rationalizing the observed size-dependent symmetry breaking. In conclusion, these findings not only provide solid foundations for studying the phase stability and properties of this boride but also give powerful insights into how the intricate atomic vacancies can influence crystal structures of transition-metal borides.

high pressure↗