Fostering a Guiding Multiscale Model for the Development of Advanced MgB 2 Hydrogen Storage Materials (Final Technical Report)

Abstract

Project Goal and Objective. The demand for energy and for an upgraded energy infrastructure has steadily grown, as have the needs for energy independence and alternatives to our reliance on petroleum. Hydrogen is considered the most viable fuels for wide-scale implementation in the near future as it is less-polluting, non-toxic, and has more stored energy than petroleum. It is envisioned that hydrogen can eventually become the prime energy carrier, integrating the transportation, grid, and chemical sectors in a way that improves resiliency, diversifies feedstocks, and affords new economic opportunities. A key remaining challenge is the development materials with enhanced gravimetric and volumetric hydrogen storage capacities that offer a higher performance than compressed gas. These materials would eliminate the need for large-scale compression, thereby dramatically reducing the footprint and cost of gas storage. The high gravimetric and volumetric hydrogen capacities of complex hydrides has prompted an intensive investigation of the potential of this class of materials as hydrogen storage media over the past 25 years. Among the many complex hydrides that have been explored, magnesium borohydride, Mg(BH 4 ) 2 , has been found to possess the best combination of practical thermodynamic properties. These include a gravimetric H 2 density of 14.9 wt% H 2 and thermodynamics for the dehydrogenation of Mg(BH 4 ) 2 to MgB 2 (equation 1) (ΔH° = 39 kJ/mol H 2 , ΔS = 112 J/K mol H 2 ) which lie in the narrow window required Mg(BH 4 ) 2 $\Leftrightarrow$ MgB 2 + 4 H 2 (1) for reversibility under moderate pressure and temperature. However, overcoming the extremely slow kinetics of the reversible release of hydrogen by this material in the solid state is a daunting challenge. At temperatures greater than 400 °C, the borohydride releases up to 14 wt% hydrogen giving MgB 2 . We discovered that the direct re-hydrogenation of MgB 2 to Mg(BH 4 ) 2 can be accomplished under 950 bar H 2 at 400 °C. While this demonstrated that complete reversibility can be achieved, the conditions employed are far too extreme for commercial hydrogen storage applications. More recently, we found through US DOE funded research projects (EERE HyMARC and HySCOR), that hydrogen cycling, can be accomplish at much milder conditions upon modification of the borohydride or boride. Guided by these discoveries these discoveries, the objective of this research project was to obtain key information that will enable the development of a model of reversible hydrogenation of MgB 2 to Mg(BH 4 ) 2 . The ultimate goal of our efforts is to attain a model of this transformation that can be utilized to accelerate development further advanced materials. This project directly follows on discoveries that were made over the course of a US DOE, EERE HyMARC project that was focused on improvement of the hydrogen cycling kinetics of modified MgB 2 . We found that that mechanical milling with graphene results the desired, pronounced kinetic enhancement. The dramatic lowering of the conditions required for the hydrogenation of MgB 2 is a significant step towards overcoming its chemical inertness allowing its development as a practical onboard hydrogen storage material. However, the exact nature of the modification(s) of MgB 2 that is responsible for its activation towards hydrogenation is completely unknown. This situation is not unique, as efforts to develop hydrogen storage materials typically have a narrow focus rather than a comprehensive approach that takes atomic level bonding and structure; molecular dynamics; long range, nano- and mesoscale-structure and their interconnection all into account. The goal of this project was the development of a comprehensive, multi-scale computational model of reversible hydrogenation of MgB 2 to Mg(BH 4 ) 2 that can be utilized for development of higher performance versions of the modified material. Development of the model requires determination of: 1) the bulk, nano-scale, and meso-scale structural changes occurring at elevated pressure following mechano-chemical modification of MgB 2 ; 2) the reaction pathway of the reversible hydrogenation of MgB 2 to Mg(BH 4 ) 2 ; 3) the effect of elevated pressure and mechano-chemical modification on the chemical reaction pathways; 4) the interactions at solid-gas interfaces; and particle surfaces; and 5) the kinetics and thermodynamic parameters associated with each step of the hydrogenation reaction pathway. This investigation required advanced techniques as preliminary, standard XRD, 11 B NMR, and FTIR analysis showed no signs of material modification. In order to gain this level of understanding of modified MgB 2 , required the teaming of a diverse group of experts and state-of-the art experimental capabilities at the University of Hawaii at Manoa (UHM) and collaborating National Laboratories: Craig Jensen , Department of Chemistry (PI and Project Director), solid state, solution, and high pressure NMR spectroscopy; solid-state synthesis; and high pressure hydrogenation (collaboration with SNL); Godwin Severa , Hawaii Natural Energy Institute (co-PI) calorimetry; infrared and Raman spectroscopy (collaboration with NREL); Dera , high pressure X-ray diffraction including in situ experiments (collaboration with ANL); Hope Ishii , Hawaii Institute of Geophysics electron microscopy investigations (collaboration with LBNL); and Joe Brown , Mechanical Engineering , material electronic structure and electric field effects.