Overcoming the Conductance versus Crossover Trade-off in State-of-the-Art Proton Exchange Fuel-Cell Membranes by Incorporating Atomically Thin Chemical Vapor Deposition Graphene

Abstract

Permeance–selectivity trade-offs are inherent to polymeric membranes. In fuel cells, thinner proton exchange membranes (PEMs) could enable higher proton conductance and increased power density with lower area-specific resistance (ASR), smaller ohmic losses, and lower ionomer cost. However, reducing thickness is accompanied by an increase in undesired species crossover harming performance and long-term efficiency. Here, we show that incorporating atomically thin monolayer graphene synthesized via scalable chemical vapor deposition (CVD) and tunable defect density into PEMs (Nafion, ~5–25 μm thick) can allow for reduced H 2 crossover (~34–78% of Nafion of a similar thickness) while maintaining adequate areal proton conductance for applications (>4 S cm –2 ). In contrast to most prior work using >50 μm symmetric Nafion sandwich structures, we elucidate the interplay of graphene defect density and Nafion proton transport resistance on the performance of Nafion|graphene composite membranes and find high-quality low-defect density CVD graphene (G) supported on Nafion 211 (~25 μm); i.e., N211|G has a high areal proton conductance (~6.1 S cm –2 ) and the lowest H 2 crossover (~0.7 mA cm –2 ). Fully functional centimeter-scale N211|G fuel-cell membranes demonstrate performance comparable to that of state-of-the-art Nafion N211 at room temperature as well as standard operating conditions (~80 °C, ~150–250 kPa-abs) with H 2 /air (power density ~0.57–0.63 W cm –2 ) and H 2 /O 2 feed (power density ~1.4–1.62 W cm –2 ) and markedly reduced H 2 crossover (~53–57%).