Low temperature tetragonal polymorph of CaZrF 6

Abstract

A new tetragonal polymorph of CaZrF 6 can be prepared by high energy ball milling of a CaF 2 /ZrF 4 mixture, followed by heat treatment at 325 °C. This polymorph is thermodynamically stable with respect to the well-known cubic form at low temperatures. However, it readily transforms to the cubic form on heating above ~400 °C. The tetragonal (β) CaZrF 6 is not isostructural with any previously known alkaline earth AZrF 6 phase. Unlike the cubic form, which shows strong negative thermal expansion over a wide temperature range, the tetragonal form displays positive thermal expansion in all directions (100–400 K: α l ~ +17 × 10 –6 K –1 and +13 × 10 –6 K –1 along the a- and c-axes, respectively).