A high-performance intermediate temperature reversible solid oxide cell with a new barrier layer free oxygen electrode

Abstract

The best solution to address the critical durability issue of solid oxide electrolytic cells (SOECs) for high-efficiency and high-rate H 2 production is to lower the operating temperature without sacrificing the performance. Developing high performance oxygen electrodes (OEs) is a key to capitalizing this solution. Here, in this paper, we report on a highly active OE for intermediate temperature ZrO 2 -based SOECs without a CeO 2 barrier layer. The new barrier-layer-free (BLF) OE is a composite of two materials, (Bi 0.75 Y 0.25 ) 0.93 Ce 0.07 O 1.5±δ (BYC) that exhibits high oxide-ion conductivity and La 0.8 Sr 0.2 MnO 3 (LSM) that possesses a high electronic conductivity to enable fast oxygen reduction/evolution reactions (ORR/OER). Featuring a microscale porous BYC scaffold decorated with high surface area LSM nanoparticles (NPs), the new BLF-OE exhibited a low area specific resistance (ASR) of 0.10 Ω cm 2 at 650 °C in air. With 50%H 2 -50%H 2 O as a feed to hydrogen electrode (HE) and air to OE, the single cell performance achieved 588 mA cm -2 at 0.80 V in the fuel cell mode and 688 mA cm -2 at 1.30 V in the electrolytic mode at 650 °C. Our in-house testing showed that this level of performance was ~3.5x higher than the cell with the benchmark La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ -Ce 0.9 Gd 0.1 O 2-δ OE. The long-term durability testing under alternating fuel cell and electrolytic modes showed a low degradation rate of 0.10 mA cm -2 h -1 over 550 hours. These encouraging results showed the great promise of the newly developed BYC-LSM to be an excellent OE candidate for intermediate temperature SOECs.