Using Artificial Microstructures to Understand Microstructure Property Relationship-Toughening Mechanisms in Metallic Glass (Final Report)

Abstract

Metallic glasses are a new class of structural materials which exhibit exciting mechanical properties including high strength and elasticity. In terms of fracture toughness, the material class of metallic glasses spans a wide range; Some metallic glasses are extremely brittle and exhibit near ideal brittle behavior whereas others can be exceptional tough with values comparable to the toughest metals out there. Such large range of observed fracture toughness within the material class of metallic glasses is surprising as they have seemingly a very similar atomic structure. Therefore, we developed “artificial microstructures” which allows to decouple the various contribution of sample geometry, imperfection and structure. Specifically, we decouple variations in the alloys’ chemical composition and the atomic structure and quantified the resulting fracture toughness. Atomic structure of a metallic glass can be modified by the fictive temperature. The fictive temperature of a glass is the temperature at which the liquid metallic glass falls out of equilibrium upon colling and forms a glass. Upon further cooling the structure is maintained only thermal oscillations decrease due to a lower absolute temperature. We found that the effect of fictive temperature (same chemistry, different structural stages of the glass) is comparable to the variations of fracture toughness when the chemistry is varied. Hence, it appears that the subtle differences in the glass structure are responsible for the large range of fracture toughness’s observed. Our results reveal that fracture toughness within the material class of metallic glasses varies significantly and we found some example alloys with exceptional high resistance to fracture and others that are almost ideally brittle. Significant influences on the fracture toughness have the structure of the glass, its chemistry, and some imperfections in the structure.