94ND10 Intergranular Phase Analysis and Fabrication

Abstract

The composition and phase fraction of the intergranular phase of 94ND10 ceramic is determined and fabricated ex situ. The fraction of each phase is 85.96 vol% Al 2 O 3 bulk phase, 9.46 vol% Mg-rich intergranular phase, 4.36 vol% Ca/Si-rich intergranular phase, and 0.22 vol% voids. The Ca/Si-rich phase consists of 0.628 at% Mg, 12.59 at% Si, 10.24 at% Ca, 17.23 at% Al, and balance O. The Mgrich phase consists of 14.17 at% Mg, 0.066 at% Si, 0.047 at% Ca, 28.69 at% Al, and balance O. XRD of the ex situ intergranular material made by mixed oxides consisting of the above phase and element fractions yielded 92 vol% MgAl 2 O 4 phase and 8 vol% CaAl 2 Si 2 O 8 phase. The formation of MgAl 2 O 4 phase is consistent with prior XRD of 94ND10, while the CaAl 2 Si 2 O 8 phase may exist in 94ND10 but at a concentration not readily detected with XRD. The MgAl 2 O 4 and CaAl 2 Si 2 O 8 phases determined from XRD are expected to have the elemental compositions for the Mg-rich and Ca/Si-rich phases above by cation substitutions (e.g., some Mg substituted for by Ca in the Mg-rich phase) and impurity phases not detectable with XRD.