Production-Ready CsPbBr3 Module Fabrication

Abstract

The purpose of this SBIR was to work on evaluation, development, and testing of CsPbBr3 semiconductors for use in commercial gamma-ray detection. The overarching goal was to demonstrate the capability to fabricate functional detectors through resources available to H3D, Inc in pursuit of an alternative to CdZnTe for room-temperature semiconductor detectors. Throughout the project, CdZnTe crystals from Redlen were used as a control group to demonstrate whether the fabrication processes could produce reasonable results. The CdZnTe crystals were diced into roughly 6 mm x 6 mm x 4.5 mm pieces and electrodes were evaporated onto planar faces. In one case, pixels were patterned through a laser ablation method; in the other, a rudimentary pixel shadow-mask was fabricated, and the pixels were generated in the evaporation process. A 16 mm x 16 mm x 14 mm CsPbBr3 crystal was diced into four smaller crystals. These CsPbBr3 had electrodes applied in a similar way to the CdZnTe samples with a rudimentary mask used for pixels on the cathode. Tested CdZnTe pieces were found to generally function with reasonable, low-energy performance. CsPbBr3 crystals were found to be non-functional under forward bias with a large dark-current. A separate attempt, using reverse bias in a non-H3D, Inc test system, observed a dark current similar to previous observations, and some active pixels but no waveforms were observed.