Materials Data on Ga2FeNi9 by Materials Project

Abstract

FeNi9Ga2 is beta Cu3Ti-derived structured and crystallizes in the tetragonal P4/mmm space group. The structure is three-dimensional. Fe is bonded to twelve Ni atoms to form FeNi12 cuboctahedra that share corners with four equivalent FeNi12 cuboctahedra, corners with eight equivalent GaNi12 cuboctahedra, edges with twenty-four NiGa4Ni8 cuboctahedra, faces with two equivalent GaNi12 cuboctahedra, faces with four equivalent FeNi12 cuboctahedra, and faces with twelve NiFe4Ni8 cuboctahedra. There are eight shorter (2.45 Å) and four longer (2.51 Å) Fe–Ni bond lengths. There are four inequivalent Ni sites. In the first Ni site, Ni is bonded to four equivalent Fe and eight equivalent Ni atoms to form NiFe4Ni8 cuboctahedra that share corners with twelve NiFe4Ni8 cuboctahedra, edges with eight equivalent GaNi12 cuboctahedra, edges with sixteen equivalent NiGa2Fe2Ni8 cuboctahedra, faces with four equivalent FeNi12 cuboctahedra, and faces with fourteen NiFe4Ni8 cuboctahedra. All Ni–Ni bond lengths are 2.45 Å. In the second Ni site, Ni is bonded to eight Ni and four equivalent Ga atoms to form NiGa4Ni8 cuboctahedra that share corners with twelve NiFe4Ni8 cuboctahedra, edges with four equivalent FeNi12 cuboctahedra, edges with four equivalent GaNi12 cuboctahedra, edges with sixteen NiGa2Fe2Ni8 cuboctahedra, faces with four equivalent GaNi12 cuboctahedra, and faces with fourteen NiFe4Ni8 cuboctahedra. There are four shorter (2.53 Å) and four longer (2.54 Å) Ni–Ni bond lengths. All Ni–Ga bond lengths are 2.51 Å. In the third Ni site, Ni is bonded to two equivalent Fe, eight Ni, and two equivalent Ga atoms to form NiGa2Fe2Ni8 cuboctahedra that share corners with twelve NiGa2Fe2Ni8 cuboctahedra, edges with four equivalent FeNi12 cuboctahedra, edges with four equivalent GaNi12 cuboctahedra, edges with sixteen NiFe4Ni8 cuboctahedra, faces with two equivalent FeNi12 cuboctahedra, faces with two equivalent GaNi12 cuboctahedra, and faces with fourteen NiFe4Ni8 cuboctahedra. All Ni–Ni bond lengths are 2.51 Å. Both Ni–Ga bond lengths are 2.56 Å. In the fourth Ni site, Ni is bonded to eight Ni and four equivalent Ga atoms to form NiGa4Ni8 cuboctahedra that share corners with twelve NiGa2Fe2Ni8 cuboctahedra, edges with eight equivalent GaNi12 cuboctahedra, edges with sixteen NiGa4Ni8 cuboctahedra, faces with four equivalent GaNi12 cuboctahedra, and faces with fourteen NiGa4Ni8 cuboctahedra. All Ni–Ni bond lengths are 2.51 Å. All Ni–Ga bond lengths are 2.51 Å. Ga is bonded to twelve Ni atoms to form GaNi12 cuboctahedra that share corners with four equivalent FeNi12 cuboctahedra, corners with eight equivalent GaNi12 cuboctahedra, edges with twenty-four NiFe4Ni8 cuboctahedra, a faceface with one FeNi12 cuboctahedra, faces with five equivalent GaNi12 cuboctahedra, and faces with twelve NiGa4Ni8 cuboctahedra.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-09-03. Materials Data on Ga2FeNi9 by Materials Project. https://doi.org/10.17188/1758895

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗