Materials Data on V2Pb4(Se2O7)3 by Materials Project

Abstract

V2Pb4(Se2O7)3 crystallizes in the orthorhombic Fdd2 space group. The structure is three-dimensional. V5+ is bonded in a distorted trigonal bipyramidal geometry to five O2- atoms. There are a spread of V–O bond distances ranging from 1.67–2.01 Å. There are two inequivalent Pb3+ sites. In the first Pb3+ site, Pb3+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Pb–O bond distances ranging from 2.44–2.84 Å. In the second Pb3+ site, Pb3+ is bonded in a 7-coordinate geometry to seven O2- atoms. There are a spread of Pb–O bond distances ranging from 2.44–3.01 Å. There are three inequivalent Se+3.33+ sites. In the first Se+3.33+ site, Se+3.33+ is bonded in a distorted trigonal non-coplanar geometry to three O2- atoms. There are a spread of Se–O bond distances ranging from 1.68–1.77 Å. In the second Se+3.33+ site, Se+3.33+ is bonded in a trigonal non-coplanar geometry to three O2- atoms. There are a spread of Se–O bond distances ranging from 1.69–1.86 Å. In the third Se+3.33+ site, Se+3.33+ is bonded in a trigonal non-coplanar geometry to three O2- atoms. There are a spread of Se–O bond distances ranging from 1.72–1.76 Å. There are eleven inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted single-bond geometry to one V5+ and one Pb3+ atom. In the second O2- site, O2- is bonded in a bent 120 degrees geometry to two equivalent Se+3.33+ atoms. In the third O2- site, O2- is bonded in a distorted single-bond geometry to three Pb3+ and one Se+3.33+ atom. In the fourth O2- site, O2- is bonded in a distorted single-bond geometry to one V5+ and one Pb3+ atom. In the fifth O2- site, O2- is bonded in a 1-coordinate geometry to two Pb3+ and one Se+3.33+ atom. In the sixth O2- site, O2- is bonded in a bent 120 degrees geometry to one V5+ and one Se+3.33+ atom. In the seventh O2- site, O2- is bonded in a distorted bent 120 degrees geometry to one V5+, one Pb3+, and one Se+3.33+ atom. In the eighth O2- site, O2- is bonded in a 2-coordinate geometry to one V5+, one Pb3+, and one Se+3.33+ atom. In the ninth O2- site, O2- is bonded in a 2-coordinate geometry to one Pb3+ and one Se+3.33+ atom. In the tenth O2- site, O2- is bonded in a distorted single-bond geometry to one Pb3+ and one Se+3.33+ atom. In the eleventh O2- site, O2- is bonded in a distorted single-bond geometry to two Pb3+ and one Se+3.33+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on V2Pb4(Se2O7)3 by Materials Project. https://doi.org/10.17188/1701309

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗