Materials Data on Sr(BiS2)2 by Materials Project

Abstract

Sr(BiS2)2 crystallizes in the hexagonal P6_3/m space group. The structure is three-dimensional. there are two inequivalent Sr2+ sites. In the first Sr2+ site, Sr2+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Sr–S bond distances ranging from 3.12–3.46 Å. In the second Sr2+ site, Sr2+ is bonded in a 8-coordinate geometry to eight S2- atoms. There are a spread of Sr–S bond distances ranging from 3.07–3.31 Å. There are four inequivalent Bi3+ sites. In the first Bi3+ site, Bi3+ is bonded to six S2- atoms to form BiS6 octahedra that share corners with two equivalent BiS5 square pyramids, edges with six BiS6 octahedra, and an edgeedge with one BiS5 square pyramid. There are a spread of Bi–S bond distances ranging from 2.63–3.04 Å. In the second Bi3+ site, Bi3+ is bonded to six S2- atoms to form distorted BiS6 octahedra that share corners with four equivalent BiS5 square pyramids, edges with four BiS6 octahedra, and an edgeedge with one BiS5 square pyramid. There are a spread of Bi–S bond distances ranging from 2.56–3.52 Å. In the third Bi3+ site, Bi3+ is bonded to five S2- atoms to form distorted BiS5 square pyramids that share corners with six BiS6 octahedra, edges with two BiS6 octahedra, and edges with two equivalent BiS5 square pyramids. The corner-sharing octahedra tilt angles range from 3–83°. There are a spread of Bi–S bond distances ranging from 2.59–2.89 Å. In the fourth Bi3+ site, Bi3+ is bonded to six S2- atoms to form a mixture of edge and corner-sharing BiS6 octahedra. The corner-sharing octahedral tilt angles are 60°. There are a spread of Bi–S bond distances ranging from 2.69–3.04 Å. There are eight inequivalent S2- sites. In the first S2- site, S2- is bonded to four equivalent Sr2+ and one Bi3+ atom to form distorted SSr4Bi square pyramids that share a cornercorner with one SSrBi5 octahedra, corners with ten SSr4Bi square pyramids, corners with two equivalent SSr2Bi3 trigonal bipyramids, edges with eight SSrBi4 square pyramids, and edges with two equivalent SSr2Bi3 trigonal bipyramids. The corner-sharing octahedral tilt angles are 3°. In the second S2- site, S2- is bonded to two Sr2+ and three Bi3+ atoms to form distorted SSr2Bi3 trigonal bipyramids that share a cornercorner with one SSrBi5 octahedra, corners with eight SSr4Bi square pyramids, corners with two equivalent SSr2Bi3 trigonal bipyramids, edges with two equivalent SSrBi5 octahedra, edges with five SSr4Bi square pyramids, and edges with two equivalent SSr2Bi3 trigonal bipyramids. The corner-sharing octahedral tilt angles are 46°. In the third S2- site, S2- is bonded to two equivalent Sr2+ and three Bi3+ atoms to form distorted SSr2Bi3 trigonal bipyramids that share corners with four equivalent SSrBi5 octahedra, corners with four SSr2Bi3 square pyramids, an edgeedge with one SSrBi5 octahedra, edges with four SSr4Bi square pyramids, and edges with four SSr2Bi3 trigonal bipyramids. The corner-sharing octahedra tilt angles range from 5–43°. In the fourth S2- site, S2- is bonded to four Sr2+ and one Bi3+ atom to form distorted SSr4Bi square pyramids that share corners with six SSr4Bi square pyramids, corners with two equivalent SSr2Bi3 trigonal bipyramids, edges with two equivalent SSrBi5 octahedra, edges with seven SSr4Bi square pyramids, and edges with three SSr2Bi3 trigonal bipyramids. In the fifth S2- site, S2- is bonded in a distorted trigonal planar geometry to three equivalent Bi3+ atoms. In the sixth S2- site, S2- is bonded to one Sr2+ and four Bi3+ atoms to form distorted SSrBi4 square pyramids that share corners with four equivalent SSrBi5 octahedra, corners with two equivalent SSr4Bi square pyramids, corners with three equivalent SSr2Bi3 trigonal bipyramids, an edgeedge with one SSrBi5 octahedra, edges with six SSr4Bi square pyramids, and an edgeedge with one SSr2Bi3 trigonal bipyramid. The corner-sharing octahedra tilt angles range from 5–95°. In the seventh S2- site, S2- is bonded to two equivalent Sr2+ and three Bi3+ atoms to form distorted SSr2Bi3 square pyramids that share corners with two equivalent SSr4Bi square pyramids, corners with five SSr2Bi3 trigonal bipyramids, edges with two equivalent SSrBi5 octahedra, edges with three SSr4Bi square pyramids, and edges with three equivalent SSr2Bi3 trigonal bipyramids. In the eighth S2- site, S2- is bonded to one Sr2+ and five Bi3+ atoms to form distorted SSrBi5 octahedra that share corners with five SSrBi4 square pyramids, corners with five SSr2Bi3 trigonal bipyramids, edges with two equivalent SSrBi5 octahedra, edges with five SSr4Bi square pyramids, and edges with three SSr2Bi3 trigonal bipyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-04-30. Materials Data on Sr(BiS2)2 by Materials Project. https://doi.org/10.17188/1679136

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗