Materials Data on Sc2Si4Mo3 by Materials Project

Abstract

Sc2Mo3Si4 crystallizes in the orthorhombic Pnma space group. The structure is three-dimensional. Sc3+ is bonded to seven Si4- atoms to form distorted ScSi7 pentagonal bipyramids that share corners with four equivalent MoSi6 octahedra, corners with six equivalent ScSi7 pentagonal bipyramids, corners with five equivalent MoSi6 pentagonal pyramids, edges with two equivalent ScSi7 pentagonal bipyramids, edges with three equivalent MoSi6 pentagonal pyramids, faces with two equivalent MoSi6 octahedra, faces with three equivalent ScSi7 pentagonal bipyramids, and faces with three equivalent MoSi6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 47–51°. There are a spread of Sc–Si bond distances ranging from 2.70–2.92 Å. There are two inequivalent Mo+3.33+ sites. In the first Mo+3.33+ site, Mo+3.33+ is bonded to six Si4- atoms to form MoSi6 octahedra that share corners with four equivalent MoSi6 octahedra, corners with eight equivalent ScSi7 pentagonal bipyramids, corners with six equivalent MoSi6 pentagonal pyramids, faces with four equivalent ScSi7 pentagonal bipyramids, and faces with four equivalent MoSi6 pentagonal pyramids. The corner-sharing octahedra tilt angles range from 49–52°. There are a spread of Mo–Si bond distances ranging from 2.57–2.75 Å. In the second Mo+3.33+ site, Mo+3.33+ is bonded to six Si4- atoms to form distorted MoSi6 pentagonal pyramids that share corners with three equivalent MoSi6 octahedra, corners with five equivalent ScSi7 pentagonal bipyramids, corners with four equivalent MoSi6 pentagonal pyramids, edges with three equivalent ScSi7 pentagonal bipyramids, edges with three equivalent MoSi6 pentagonal pyramids, faces with two equivalent MoSi6 octahedra, faces with three equivalent ScSi7 pentagonal bipyramids, and a faceface with one MoSi6 pentagonal pyramid. The corner-sharing octahedra tilt angles range from 39–40°. There are a spread of Mo–Si bond distances ranging from 2.50–2.63 Å. There are three inequivalent Si4- sites. In the first Si4- site, Si4- is bonded in a 9-coordinate geometry to four equivalent Sc3+, four Mo+3.33+, and one Si4- atom. The Si–Si bond length is 2.51 Å. In the second Si4- site, Si4- is bonded in a 9-coordinate geometry to two equivalent Sc3+, six Mo+3.33+, and one Si4- atom. The Si–Si bond length is 2.51 Å. In the third Si4- site, Si4- is bonded in a 9-coordinate geometry to four equivalent Sc3+, four Mo+3.33+, and one Si4- atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-20. Materials Data on Sc2Si4Mo3 by Materials Project. https://doi.org/10.17188/1655048

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗