Materials Data on LiB3O5 by Materials Project

Abstract

LiB3O5 crystallizes in the orthorhombic Pnma space group. The structure is three-dimensional. there are four inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded to six O2- atoms to form distorted LiO6 octahedra that share a cornercorner with one LiO6 octahedra, corners with eight BO4 tetrahedra, and edges with two equivalent BO4 tetrahedra. The corner-sharing octahedral tilt angles are 72°. There are a spread of Li–O bond distances ranging from 2.00–2.39 Å. In the second Li1+ site, Li1+ is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Li–O bond distances ranging from 1.90–2.12 Å. In the third Li1+ site, Li1+ is bonded in a 4-coordinate geometry to four O2- atoms. There are a spread of Li–O bond distances ranging from 1.93–2.17 Å. In the fourth Li1+ site, Li1+ is bonded to six O2- atoms to form distorted LiO6 octahedra that share a cornercorner with one LiO6 octahedra and corners with eight BO4 tetrahedra. The corner-sharing octahedral tilt angles are 72°. There are a spread of Li–O bond distances ranging from 2.06–2.56 Å. There are six inequivalent B3+ sites. In the first B3+ site, B3+ is bonded to four O2- atoms to form BO4 tetrahedra that share corners with three LiO6 octahedra and corners with four BO4 tetrahedra. The corner-sharing octahedra tilt angles range from 55–73°. There are a spread of B–O bond distances ranging from 1.44–1.62 Å. In the second B3+ site, B3+ is bonded to four O2- atoms to form BO4 tetrahedra that share corners with two LiO6 octahedra and corners with four BO4 tetrahedra. The corner-sharing octahedra tilt angles range from 59–71°. There are a spread of B–O bond distances ranging from 1.45–1.57 Å. In the third B3+ site, B3+ is bonded to four O2- atoms to form BO4 tetrahedra that share a cornercorner with one LiO6 octahedra and corners with seven BO4 tetrahedra. The corner-sharing octahedral tilt angles are 60°. There are a spread of B–O bond distances ranging from 1.42–1.51 Å. In the fourth B3+ site, B3+ is bonded in a trigonal planar geometry to three O2- atoms. There are a spread of B–O bond distances ranging from 1.36–1.41 Å. In the fifth B3+ site, B3+ is bonded to four O2- atoms to form BO4 tetrahedra that share corners with six BO4 tetrahedra and an edgeedge with one LiO6 octahedra. There are a spread of B–O bond distances ranging from 1.43–1.54 Å. In the sixth B3+ site, B3+ is bonded to four O2- atoms to form BO4 tetrahedra that share corners with two LiO6 octahedra and corners with six BO4 tetrahedra. The corner-sharing octahedra tilt angles range from 68–69°. There are a spread of B–O bond distances ranging from 1.42–1.57 Å. There are thirteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two equivalent B3+ atoms. In the second O2- site, O2- is bonded in a 4-coordinate geometry to two Li1+ and two equivalent B3+ atoms. In the third O2- site, O2- is bonded to two Li1+ and two equivalent B3+ atoms to form distorted corner-sharing OLi2B2 tetrahedra. In the fourth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two equivalent B3+ atoms. In the fifth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two B3+ atoms. In the sixth O2- site, O2- is bonded to two Li1+ and two B3+ atoms to form a mixture of distorted edge and corner-sharing OLi2B2 trigonal pyramids. In the seventh O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two B3+ atoms. In the eighth O2- site, O2- is bonded in a 4-coordinate geometry to one Li1+ and three B3+ atoms. In the ninth O2- site, O2- is bonded in a trigonal planar geometry to three B3+ atoms. In the tenth O2- site, O2- is bonded in a trigonal planar geometry to three B3+ atoms. In the eleventh O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two B3+ atoms. In the twelfth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+ and two equivalent B3+ atoms. In the thirteenth O2- site, O2- is bonded in a distorted trigonal non-coplanar geometry to one Li1+ and two equivalent B3+ atoms.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-02. Materials Data on LiB3O5 by Materials Project. https://doi.org/10.17188/1350858

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗