Materials Data on Li2BiO3 by Materials Project

Abstract

Li2BiO3 crystallizes in the monoclinic C2/c space group. The structure is three-dimensional. there are three inequivalent Li sites. In the first Li site, Li is bonded in a 6-coordinate geometry to six O atoms. There are a spread of Li–O bond distances ranging from 2.07–2.63 Å. In the second Li site, Li is bonded to six O atoms to form LiO6 octahedra that share corners with two equivalent LiO6 octahedra, corners with four BiO6 octahedra, edges with two equivalent LiO6 octahedra, and edges with four BiO6 octahedra. The corner-sharing octahedra tilt angles range from 3–7°. There are a spread of Li–O bond distances ranging from 2.14–2.49 Å. In the third Li site, Li is bonded to six O atoms to form LiO6 octahedra that share corners with two equivalent LiO6 octahedra, edges with two equivalent LiO6 octahedra, and edges with six BiO6 octahedra. The corner-sharing octahedral tilt angles are 7°. There are a spread of Li–O bond distances ranging from 2.24–2.37 Å. There are two inequivalent Bi sites. In the first Bi site, Bi is bonded to six O atoms to form BiO6 octahedra that share corners with two equivalent LiO6 octahedra, edges with three equivalent BiO6 octahedra, and edges with five LiO6 octahedra. The corner-sharing octahedral tilt angles are 3°. All Bi–O bond lengths are 2.16 Å. In the second Bi site, Bi is bonded to six O atoms to form BiO6 octahedra that share corners with two equivalent LiO6 octahedra, edges with three equivalent BiO6 octahedra, and edges with five LiO6 octahedra. The corner-sharing octahedral tilt angles are 7°. There are a spread of Bi–O bond distances ranging from 2.37–2.40 Å. There are three inequivalent O sites. In the first O site, O is bonded to four Li and two Bi atoms to form a mixture of corner and edge-sharing OLi4Bi2 octahedra. The corner-sharing octahedra tilt angles range from 0–10°. In the second O site, O is bonded to four Li and two Bi atoms to form a mixture of distorted corner and edge-sharing OLi4Bi2 octahedra. The corner-sharing octahedra tilt angles range from 0–13°. In the third O site, O is bonded to four Li and two Bi atoms to form a mixture of corner and edge-sharing OLi4Bi2 octahedra. The corner-sharing octahedra tilt angles range from 0–13°.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-05-03. Materials Data on Li2BiO3 by Materials Project. https://doi.org/10.17188/1289055

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗