Materials Data on Ba2La2Fe2Cu2O11 by Materials Project

Abstract

Ba2La2Fe2Cu2O11 crystallizes in the tetragonal P4mm space group. The structure is three-dimensional. there are two inequivalent Ba2+ sites. In the first Ba2+ site, Ba2+ is bonded in a distorted q6 geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.80–2.89 Å. In the second Ba2+ site, Ba2+ is bonded in a distorted q6 geometry to ten O2- atoms. There are a spread of Ba–O bond distances ranging from 2.78–2.99 Å. There are two inequivalent La3+ sites. In the first La3+ site, La3+ is bonded to twelve O2- atoms to form LaO12 cuboctahedra that share corners with eight LaO12 cuboctahedra, faces with five LaO12 cuboctahedra, faces with two equivalent CuO6 octahedra, faces with four FeO6 octahedra, and faces with two equivalent CuO5 square pyramids. There are a spread of La–O bond distances ranging from 2.65–2.87 Å. In the second La3+ site, La3+ is bonded to twelve O2- atoms to form LaO12 cuboctahedra that share corners with eight LaO12 cuboctahedra, faces with five LaO12 cuboctahedra, faces with two equivalent FeO6 octahedra, faces with four CuO6 octahedra, and faces with two equivalent FeO5 square pyramids. There are a spread of La–O bond distances ranging from 2.74–2.80 Å. There are four inequivalent Fe3+ sites. In the first Fe3+ site, Fe3+ is bonded to six O2- atoms to form FeO6 octahedra that share corners with five CuO6 octahedra, a cornercorner with one CuO5 square pyramid, and faces with eight LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–3°. There are a spread of Fe–O bond distances ranging from 1.86–1.96 Å. In the second Fe3+ site, Fe3+ is bonded to five O2- atoms to form FeO5 square pyramids that share corners with five CuO6 octahedra and faces with four equivalent LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–2°. There is one shorter (1.85 Å) and four longer (1.92 Å) Fe–O bond length. In the third Fe3+ site, Fe3+ is bonded to five O2- atoms to form FeO5 square pyramids that share a cornercorner with one CuO6 octahedra and corners with four equivalent CuO5 square pyramids. The corner-sharing octahedral tilt angles are 0°. There is one shorter (1.86 Å) and four longer (1.98 Å) Fe–O bond length. In the fourth Fe3+ site, Fe3+ is bonded to six O2- atoms to form FeO6 octahedra that share a cornercorner with one CuO6 octahedra, corners with five CuO5 square pyramids, and faces with four equivalent LaO12 cuboctahedra. The corner-sharing octahedral tilt angles are 0°. There are a spread of Fe–O bond distances ranging from 1.87–2.02 Å. There are four inequivalent Cu3+ sites. In the first Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share corners with five FeO6 octahedra, a cornercorner with one FeO5 square pyramid, and faces with eight LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–3°. There are a spread of Cu–O bond distances ranging from 1.90–2.00 Å. In the second Cu3+ site, Cu3+ is bonded to six O2- atoms to form CuO6 octahedra that share a cornercorner with one FeO6 octahedra, corners with five FeO5 square pyramids, and faces with four equivalent LaO12 cuboctahedra. The corner-sharing octahedral tilt angles are 0°. There are a spread of Cu–O bond distances ranging from 1.96–2.05 Å. In the third Cu3+ site, Cu3+ is bonded to five O2- atoms to form CuO5 square pyramids that share a cornercorner with one FeO6 octahedra and corners with four equivalent FeO5 square pyramids. The corner-sharing octahedral tilt angles are 0°. All Cu–O bond lengths are 2.01 Å. In the fourth Cu3+ site, Cu3+ is bonded to five O2- atoms to form CuO5 square pyramids that share corners with five FeO6 octahedra and faces with four equivalent LaO12 cuboctahedra. The corner-sharing octahedra tilt angles range from 0–6°. There is four shorter (1.94 Å) and one longer (2.00 Å) Cu–O bond length. There are ten inequivalent O2- sites. In the first O2- site, O2- is bonded in a distorted linear geometry to four equivalent La3+, one Fe3+, and one Cu3+ atom. In the second O2- site, O2- is bonded in a distorted linear geometry to four La3+, one Fe3+, and one Cu3+ atom. In the third O2- site, O2- is bonded in a distorted linear geometry to four equivalent La3+, one Fe3+, and one Cu3+ atom. In the fourth O2- site, O2- is bonded in a distorted linear geometry to four equivalent La3+, one Fe3+, and one Cu3+ atom. In the fifth O2- site, O2- is bonded in a distorted linear geometry to two equivalent Ba2+, two equivalent La3+, one Fe3+, and one Cu3+ atom. In the sixth O2- site, O2- is bonded in a distorted linear geometry to four equivalent La3+, one Fe3+, and one Cu3+ atom. In the seventh O2- site, O2- is bonded to four Ba2+, one Fe3+, and one Cu3+ atom to form a mixture of distorted edge, corner, and face-sharing OBa4FeCu octahedra. The corner-sharing octahedra tilt angles range from 9–17°. In the eighth O2- site, O2- is bonded in a distorted linear geometry to four equivalent Ba2+, one Fe3+, and one Cu3+ atom. In the ninth O2- site, O2- is bonded in a 2-coordinate geometry to two equivalent Ba2+, two equivalent La3+, one Fe3+, and one Cu3+ atom. In the tenth O2- site, O2- is bonded in a distorted linear geometry to four equivalent Ba2+, one Fe3+, and one Cu3+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-06-04. Materials Data on Ba2La2Fe2Cu2O11 by Materials Project. https://doi.org/10.17188/1286122

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗