Materials Data on Na3GdBr6 by Materials Project

Abstract

Na3GdBr6 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are four inequivalent Na1+ sites. In the first Na1+ site, Na1+ is bonded in a 7-coordinate geometry to seven Br1- atoms. There are a spread of Na–Br bond distances ranging from 2.98–3.69 Å. In the second Na1+ site, Na1+ is bonded in a 7-coordinate geometry to seven Br1- atoms. There are a spread of Na–Br bond distances ranging from 2.96–3.70 Å. In the third Na1+ site, Na1+ is bonded to six Br1- atoms to form NaBr6 octahedra that share corners with six GdBr6 octahedra. The corner-sharing octahedra tilt angles range from 43–47°. There are a spread of Na–Br bond distances ranging from 2.91–3.10 Å. In the fourth Na1+ site, Na1+ is bonded to six Br1- atoms to form NaBr6 octahedra that share corners with six GdBr6 octahedra. The corner-sharing octahedra tilt angles range from 43–47°. There are a spread of Na–Br bond distances ranging from 2.90–3.09 Å. There are two inequivalent Gd3+ sites. In the first Gd3+ site, Gd3+ is bonded to six Br1- atoms to form GdBr6 octahedra that share corners with six NaBr6 octahedra. The corner-sharing octahedra tilt angles range from 43–47°. There are a spread of Gd–Br bond distances ranging from 2.82–2.85 Å. In the second Gd3+ site, Gd3+ is bonded to six Br1- atoms to form GdBr6 octahedra that share corners with six NaBr6 octahedra. The corner-sharing octahedra tilt angles range from 43–47°. There are a spread of Gd–Br bond distances ranging from 2.82–2.85 Å. There are six inequivalent Br1- sites. In the first Br1- site, Br1- is bonded in a 3-coordinate geometry to four Na1+ and one Gd3+ atom. In the second Br1- site, Br1- is bonded in a 3-coordinate geometry to four Na1+ and one Gd3+ atom. In the third Br1- site, Br1- is bonded to three Na1+ and one Gd3+ atom to form a mixture of distorted corner and edge-sharing BrNa3Gd trigonal pyramids. In the fourth Br1- site, Br1- is bonded to three Na1+ and one Gd3+ atom to form a mixture of distorted corner and edge-sharing BrNa3Gd trigonal pyramids. In the fifth Br1- site, Br1- is bonded to three Na1+ and one Gd3+ atom to form a mixture of distorted corner and edge-sharing BrNa3Gd trigonal pyramids. In the sixth Br1- site, Br1- is bonded to three Na1+ and one Gd3+ atom to form a mixture of distorted corner and edge-sharing BrNa3Gd trigonal pyramids.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-07-24. Materials Data on Na3GdBr6 by Materials Project. https://doi.org/10.17188/1277994

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗