Materials Data on Li2Mn3(P2O7)2 by Materials Project

Abstract

Li2Mn3(P2O7)2 crystallizes in the triclinic P-1 space group. The structure is three-dimensional. there are two inequivalent Li1+ sites. In the first Li1+ site, Li1+ is bonded in a distorted rectangular see-saw-like geometry to four O2- atoms. There are a spread of Li–O bond distances ranging from 1.96–2.27 Å. In the second Li1+ site, Li1+ is bonded in a distorted trigonal non-coplanar geometry to three O2- atoms. There are a spread of Li–O bond distances ranging from 1.98–2.03 Å. There are three inequivalent Mn2+ sites. In the first Mn2+ site, Mn2+ is bonded in a 6-coordinate geometry to six O2- atoms. There are a spread of Mn–O bond distances ranging from 2.15–2.52 Å. In the second Mn2+ site, Mn2+ is bonded to six O2- atoms to form MnO6 octahedra that share corners with six PO4 tetrahedra and an edgeedge with one MnO6 octahedra. There are a spread of Mn–O bond distances ranging from 2.09–2.31 Å. In the third Mn2+ site, Mn2+ is bonded to six O2- atoms to form distorted MnO6 octahedra that share corners with six PO4 tetrahedra and an edgeedge with one MnO6 octahedra. There are a spread of Mn–O bond distances ranging from 2.19–2.30 Å. There are four inequivalent P5+ sites. In the first P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with four MnO6 octahedra and a cornercorner with one PO4 tetrahedra. The corner-sharing octahedra tilt angles range from 48–59°. There are a spread of P–O bond distances ranging from 1.52–1.62 Å. In the second P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with four MnO6 octahedra and a cornercorner with one PO4 tetrahedra. The corner-sharing octahedra tilt angles range from 21–53°. There are a spread of P–O bond distances ranging from 1.50–1.62 Å. In the third P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with two equivalent MnO6 octahedra and a cornercorner with one PO4 tetrahedra. The corner-sharing octahedra tilt angles range from 55–60°. There are a spread of P–O bond distances ranging from 1.53–1.63 Å. In the fourth P5+ site, P5+ is bonded to four O2- atoms to form PO4 tetrahedra that share corners with two equivalent MnO6 octahedra and a cornercorner with one PO4 tetrahedra. The corner-sharing octahedra tilt angles range from 47–49°. There are a spread of P–O bond distances ranging from 1.53–1.62 Å. There are fourteen inequivalent O2- sites. In the first O2- site, O2- is bonded in a 1-coordinate geometry to two equivalent Mn2+ and one P5+ atom. In the second O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+, one Mn2+, and one P5+ atom. In the third O2- site, O2- is bonded in a distorted trigonal planar geometry to two Mn2+ and one P5+ atom. In the fourth O2- site, O2- is bonded to two Li1+, one Mn2+, and one P5+ atom to form a mixture of distorted corner and edge-sharing OLi2MnP tetrahedra. In the fifth O2- site, O2- is bonded in a distorted trigonal planar geometry to two Mn2+ and one P5+ atom. In the sixth O2- site, O2- is bonded in a 3-coordinate geometry to two Mn2+ and one P5+ atom. In the seventh O2- site, O2- is bonded to three Li1+ and one P5+ atom to form distorted OLi3P trigonal pyramids that share a cornercorner with one OLi2MnP tetrahedra, an edgeedge with one OLi2MnP tetrahedra, and an edgeedge with one OLi3P trigonal pyramid. In the eighth O2- site, O2- is bonded in a 1-coordinate geometry to two Mn2+ and one P5+ atom. In the ninth O2- site, O2- is bonded in a bent 150 degrees geometry to two P5+ atoms. In the tenth O2- site, O2- is bonded in a 3-coordinate geometry to two Mn2+ and one P5+ atom. In the eleventh O2- site, O2- is bonded in a distorted bent 150 degrees geometry to two P5+ atoms. In the twelfth O2- site, O2- is bonded in a distorted trigonal planar geometry to two Mn2+ and one P5+ atom. In the thirteenth O2- site, O2- is bonded in a distorted trigonal planar geometry to one Li1+, one Mn2+, and one P5+ atom. In the fourteenth O2- site, O2- is bonded in a distorted bent 150 degrees geometry to one Mn2+ and one P5+ atom.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

2020-08-03. Materials Data on Li2Mn3(P2O7)2 by Materials Project. https://doi.org/10.17188/1206056

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗